Dimensional behavior of curing bone cement masses.

Abstract

The curing of bone cements is accompanied by release of polymerization heat and, hence, by a temperature rise of the curing cement mass. This temperature rise causes expansion of enclosed air bubbles and evaporation of the volatile monomer. An overall expansion of 3 to 5 vol % has been mentioned in the literature. It has often been stated that this expansion favours the fixation of metal endoprostheses in the marrow cavity of bone. To check for the influence of this expansion on linear dimensions of the cured cement mass we filled stainless steel cylinders with a precision bore of 22,000 +/- 0,005 mm and a length of 120 mm with bone cement. After curing of the cement in a environment of 37 degrees C the resulting cement rod was released from the cylinder and the diameter of the rod was measured at 37 degrees C. The influence of the "foaming effect" on the transverse dimensions of the rods was studied by curing the cement at 37 degrees C and 2 atm air pressure in a high-pressure-vessel. This method of curing eliminates porosity in the cement almost completely, so that curing shrinkage is to be expected rather than expansion of the cement mass. The results indicate that a volumetric expansion of the cement during curing of cylindrical rods in laboratory experiments, can be accompanied by a linear diametrical shrinkage of the cement mass. The explanation of this phenomenon is to be sought in the fact that the volumetric expansion takes place at a time when the cement is still plastic; by the formation of gas bubbles, the cement is forced in longitudinal direction into the cylinder and when the temperature of the mass has passed through a maximum, the cooling of the cement mass results in a thermal shrinkage of approximately 0.4% linearly. Extrapolating this laboratory result to clinical situation one might doubt whether the overall expansion of bone cements during curing will result in a permanent positive pressure on the walls of marrow cavity and whether it will contribute to a better fixation of endoprostheses than in the case of a, still hypothetical, nonporous cement.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

J R De Wijn, F C Driessens, T J Slooff. 1975. Dimensional behavior of curing bone cement masses.. https://doi.org/10.1002/jbm.820090414

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

Gamma-radiation-induced changes in structure and properties of tetracalcium phosphate and its derived calcium phosphate cement.

The purpose of the present study was to investigate the gamma-radiation effect on the structure and properties of the single-phase tetracalcium phosphate (TTCP) powder and its derived calcium phosphate cement (CPC). Experimental results show that low-dosed (0-30 kGy) CPC has a setting time of 10-12 min, while high-dosed (40-120 kGy) CPC has a setting time of 8-10 min. The low dose gamma-radiation does not significantly change porosity volume fraction or compressive strength of the CPC. The pH values of all CPC samples fell in a relatively narrow band, with a band width of 8.5-9.1 (in terms of pH value). With a dose of 10 or 20 kGy gamma-radiation, the TTCP-apatite conversion ratio does not change much. With 30 kGy the conversion ratio significantly increases and reaches a maximum value. With further increases in dose, the conversion ratio quickly declines. With increasing gamma-ray dose, the CPC morphology becomes more porous/loose and apatite particles become larger in size. When exposed to a high dose (120 kGy) of gamma-radiation, TTCP structure is radiation-damaged, and gamma-ray-induced formation of apatite is confirmed by transmission electron microscopic/selected-area diffraction/lattice imaging analyses.

Bone Cements↗

Influence of initial component temperature on the apparent viscosity and handling characteristics of acrylic (PMMA) bone cement.

The flow and polymerization characteristics of poly(methylmethacrylate) (PMMA) bone cement can be changed by manipulating the temperature of the bone cement components or the environment that they are prepared in. To quantify the effects of the initial component temperature (T(ic)) of acrylic bone cement on the rheological and handling characteristics, ASTM F451-99a compliant methods and clinically relevant testing methods were utilized. A rheometer was designed and fabricated using the dimensions of a clinical, commercially available, cement gun and nozzle. The influence on the apparent viscosity and handling characteristics (setting time, working time, and peak exotherm temperature) for a high viscosity (HV) commercially-available acrylic bone cement, Palacos R, were determined. The values of T(ic) used were 23 degrees C (room), 6 degrees C (refrigerator), and -14 degrees C (freezer). Using the apparent viscosity of a medium viscosity (MV) bone cement as a benchmark (Simplex P at room temperature), it was found that by adjusting the T(ic) the HV cement was able to mimic the flow characteristics of the MV cement. Lowering the T(ic) lowered the apparent viscosity of the bone cement. The effects of T(ic) on the polymerization of bone cement were studied in dynamic and static conditions. The dynamic test recorded temperature and torque from stirring resistance. Setting times were also determined using the ASTM exotherm mold method. The setting times determined by the dynamic testing conditions were consistently shorter than those determined by the ASTM method. Lowering the T(ic) increased the working and setting times; however, it did not have a significant effect on the peak exotherm temperature.

Bone Cements↗