Abstract

Limited space for extracoronal attachments is a serious complication in the design and fabrication of a precision attachment removable partial denture. A custom metal-ceramic housing joined to the partial framework with laser welding offers strength and improved esthetics while requiring minimal space. This article presents the technical aspects of custom housing construction.

Explore related subjects

Dental Soldering Denture Design Denture Precision Attachment Denture Retention Denture, Partial, Removable Esthetics, Dental Humans Lasers Metal Ceramic Alloys Surface Properties Journal Article

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Yoshihiro Goto, James S Brudvik. 2002. Custom precision attachment housings for removable partial dentures.. https://pubmed.ncbi.nlm.nih.gov/12239485/

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2006

Microstructures of beta-titanium orthodontic wires joined by infrared brazing.

The microstructures and interdiffusion in brazed beta-titanium orthodontic wires were investigated by scanning electron microscopy and electron probe microanalysis, respectively. Beta-titanium wire (Ti-11Mo-6Zr-4Sn) with cross-section dimensions of 0.032 in. x 0.032 in., titanium-based braze alloy (Ti-30Ni-20Cu), and silver-based braze alloy (Ag-22Cu-17Zn-5Sn) were selected for the study. Brazing was performed using infrared radiation (RS-1) under an argon atmosphere. Specimens were etched with two solutions (2.5% HF + 2.5% HNO(3) + 95% H(2)O; 25% HN(4)OH + 30% H(2)O(2) + 45%H(2)O). It was found that the silver-based braze alloy has a eutectic structure. In the diffusion layer between the beta-titanium wire and this silver-based braze alloy, Cu and Ti were enriched on the wire side, and Sn and Ti were enriched on the braze alloy side. The titanium-based braze alloy has a dendritic structure. Beta-titanium wire specimens brazed with the titanium-based braze alloy had a thicker intermediate area compared to the silver alloy; Ti in the diffusion layer had an irregular concentration gradient, and the braze alloy side had higher Ti concentration. The original microstructure of the beta-titanium wire was not altered with the use of either braze alloy. Infrared brazing of beta-titanium orthodontic wire is acceptable for clinical use, since the wire microstructure did not deteriorate with either the titanium-based or silver-based braze alloy. The differing microstructures of the joint regions for the two braze alloys suggest that the joint strengths may also differ.

Dental Soldering↗

PubMed2006

[Application of the laser welding to preventing the break of the base plate caused by the increase of magnetic attachments].

OBJECTIVE: This study was intended to design a kind of resisting part dint of device in order to preventing the base plate break while being subjected to the dint when partial base plate dint concentrates because of the increase of the magnetic attachment to the original movable artificial teeth. METHODS: Ten patients who should increase magnetic attachment was adopted in the study, and we increased a kind of new designed partial cast base plate on the original base plate using laser welding technique, then designed magnetic attachment and artificial teeth. RESULTS: None of ten sufferers appeared the phenomenon of the break of the base plate. CONCLUSION: The application of the laser welding technique can prevent the break of the base plate when partial dint increase because of the increase of the magnetic attachments.

Dental Soldering↗

PubMed2004

Optimizing mechanical properties of laser-welded gold alloy through heat treatment.

OBJECTIVE: The goal of this work was to improve the mechanical strength of laser-welded gold alloy with age-hardenability at intraoral temperature. METHODS: The gold alloy was cast conventionally in plate patterns (0.5 mm x 3.0 mm x 20 mm). After bench-cooling the mold to room temperature (as-cast state), transverse sections of the plate were made at mid-span. They were butted against one another and welded using Nd:YAG laser (current: 320 A; time: 10 ms; spot diameter: 1 mm). Three laser pulses were applied from both sides to cover the joint width (3.0 mm) of the specimens before or after solution heat treatment at 700 degrees C/5 min. Uncut control specimens (non-welded) were also prepared. After solution treatment, two different heat treatments were given the laser-welded specimens: high-temperature aging at 250 degrees C/15 min, or intraoral aging at 37 degrees C/3 days. Control specimens underwent all of the heat treatments after solution treatment. Tensile testing was conducted at a crosshead speed of 2 mm/min and a gauge length of 10 mm. RESULTS: Solution treatment of the gold alloy before laser-welding did not improve the mechanical strength of laser-welded gold alloy after high-temperature aging or intraoral aging. The joint strengths of laser-welded gold alloy were improved only by solution heat treatments after laser-welding and subsequent aging treatment at high or intraoral temperatures. SIGNIFICANCE: The results of this study indicated that laser-welded cast gold alloy prostheses aged at high or intraoral temperatures produce high strength when they are solution-treated after laser-welding.

Dental Soldering↗