Microstructure in gold-containing Ag3Sn-amalgam.

Abstract

The present study was conducted in order to understand the microstructural characteristics in dental amalgam which consists of both spherical and irregular Ag3Sn alloy particles with gold substituted in varying amounts for silver (0, 9, and 15%). Spherical alloy particles were used as obtained from Western Gold and Platinum and irregular alloy particles were prepared in the laboratory and then employed in the present study. The amalgam was prepared from the alloy particles by the trituration and condensation method. The polished and etched samples were studied using the techniques of X-ray diffraction, optical metallography, scanning electron microscopy, and X-ray energy dispersive spectroscopy. The microstructure in both types amalgam studied after two weeks of preparation contains gamma (unreacted Ag3Sn particles), gamma1 (Ag2Hg3), and gamma2 (Sn7-8Hg) phases in pure Ag3Sn-amalgam and gamma, gamma1, and (Au-Sn) phases in gold-containing amalgam. The The (Au-Sn) phase existed in the form of rings surrounding the gamma grains and acted as a barrier for mercury diffusion in Ag3Sn particles.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

M L Malhotra. 1976. Microstructure in gold-containing Ag3Sn-amalgam.. https://doi.org/10.1002/jbm.820100103

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

Failure mode of dental restorative materials under Hertzian indentation.

OBJECTIVE: To explore the application of Hertzian indentation testing to amalgam and GIC; study the failure behavior of the bi-layer structure of each material on a relatively soft substrate; and investigate the effect of thickness. METHODS: Amalgam (Lojic+, SDI, Bayswater, Australia) and ceramic-reinforced GIC (Advanced Healthcare, Tonbridge, UK) discs, 10 mm diameter, thicknesses ranging from 0.4 to 8.0 mm, were tested resting freely on a substrate (30% glass fibre-reinforced polyamide; E=10GPa, 10 mm diameter and 5 mm thick). Increasing load was applied to the center of the disc by a 20 mm-diameter hard steel ball until fracture occurred. Acoustic emission sensing was used as a supplemental method for crack detection. The load at the first crack was recorded. Fracture surfaces were observed under SEM to identify the crack initiation site and the failure mode. RESULTS: The main failure mode of both materials shifted from bottom-initiated radial cracking to near-contact cone cracking or subsurface plastic deformation as the thickness was increased. There was a wide thickness range for the transition of the failure mode for amalgam. Failure load was proportional to the square of thickness for amalgam, except for deviations at small and very large thickness; for the GIC, it was proportional to the thickness to the power approximately 1.6, except for thin layers. SIGNIFICANCE: The Hertzian indentation test can be applied to investigate the failure behavior of amalgam and GIC in addition to ceramics, for which purpose it may have value as a routine test. Failure mode changed with specimen thickness. The importance of considering both failure mode and failure load or strength is emphasized.

Dental Amalgam↗