Layer-by-layer engineering of biocompatible, decomposable core-shell structures.

Dinesh B Shenoy·Alexei A Antipov·Gleb B Sukhorukov·Helmuth Möhwald
View original source ↗Export metadata ↓

Abstract

The objective of the present investigation was to fabricate composite colloidal particles consisting of a sacrificial, decomposable template of biodegradable nature covered with biocompatible polyelectrolyte multilayers using the layer-by-layer sequential adsorption technique. Poly-dl-lactic acid and poly(dl-lactic-co-glycolic acid) were chosen to design the microparticulate template, and a preliminary feasibility study was carried out with poly(styrene sulfonate sodium)-poly(allylamine hydrochloride) as shell components. The properties of both core-shell and hollow structures obtained by core dissolution were characterized by confocal laser scanning microscopy, microelectrophoresis, scanning force microscopy, and scanning electron microscopy. The concept was then extended to biocompatible polyelectrolytes as shell wall building blocks to deduce stable hollow capsules with tailored properties. Uniform, complete coating with oppositely charged polyelectrolyte pairs was achieved for all the combinations investigated. The results demonstrate that polyester microparticles could serve as viable alternative components to conventionally employed templates to derive hollow capsules with defined size, shape, and shell thickness. With all the components used for fabrication being biocompatible, these polyelectrolyte capsules may find interesting applications in the fields of biology, biochemistry, biotechnology, and drug delivery.

Explore related subjects

Biocompatible MaterialsMicroscopy, Electron, ScanningMicrospheresMolecular StructureJournal ArticleResearch Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Dinesh B Shenoy, Alexei A Antipov, Gleb B Sukhorukov, Helmuth Möhwald. Layer-by-layer engineering of biocompatible, decomposable core-shell structures.. https://doi.org/10.1021/bm025661y

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2003

Synthesis of gold functionalized poly-bisvinylethyleneurea/silica hybrid materials.

Novel gold/poly-(1,3-divinyl-imidazolid-2-one)/silica [poly-bisvinylethyleneurea (poly-BVU)/silica)] hybrid particles have been produced by adsorption and spontaneously occurring in situ reduction of Au(3+) cations on the surface of poly-BVU/silica hybrid particles. The successful functionalization of the poly-BVU/silica particles with gold nanoclusters has been evidenced by UV/vis and XPS spectroscopy as well as scanning electron microscopy. The size of the resulting gold clusters, estimated by means of the Mie-Drude theory on the full peak width at half-maximum of the surface plasmon UV/vis absorbance, correlates with the polymer content of the poly-BVU/silica hybrid particles used for the modification. Therefore, it is possible to control the size of the gold clusters simply by adjusting the monomer/silica ratio in the polymerization process, which corresponds with the polymer content of the hybrids.

Biocompatible Materials↗
PubMed2003

Evaluation of thermal- and photo-crosslinked biodegradable poly(propylene fumarate)-based networks.

Biodegradable networks of poly(propylene fumarate) (PPF) and the crosslinking reagent poly(propylene fumarate)-diacrylate (PPF-DA) were prepared with thermal- and photo-initiator systems. Thermal-crosslinking was performed with benzoyl peroxide (BP), which is accelerated by N,N-dimethyl-p-toluidine (DMT) and enables injection and in situ polymerization. Photo-crosslinking was accomplished with bis(2,4,6-trimethylbenzoyl) phenylphosphine oxide (BAPO), which is activated by long-wavelength UV light and facilitates material processing with rapid manufacturing techniques, such as stereolithography. Networks were evaluated to assess the effects of the initiators and the PPF/PPF-DA double bond ratio on the mechanical properties. Regardless of the initiator system, the compressive properties of the PPF/PPF-DA networks increased as the double bond ratio decreased from 2 to 0.5. BAPO/UV-initiated networks were significantly stronger than those formed with BP/DMT. The compressive modulus of the photo- and thermal-crosslinked PPF/PPF-DA networks ranged from 310 +/- 25 to 1270 +/- 286 MPa and 75 +/- 8 to 332 +/- 89 MPa, respectively. The corresponding fracture strengths varied from 58 +/- 7 to 129 +/- 17 MPa and 31 +/- 13 to 105 +/- 12 MPa. The mechanical properties were not affected by the initiator concentration. Characterization of the network structures indicated that BAPO was a more efficient initiator for the crosslinking of PPF/PPF-DA, achieving a higher double bond conversion and crosslinking density than its BP counterpart. Estimated average molecular weights between crosslinks (Mc) confirmed the effects of the initiators and PPF/PPF-DA double bond ratio on the mechanical properties. This work demonstrates the capability to control the properties of PPF/PPF-DA networks as well as their versatility to be used as an injectable material or a prefabricated implant.

Biocompatible Materials↗
PubMed2003

A biodegradable electrical bioconductor made of polypyrrole nanoparticle/poly(D,L-lactide) composite: A preliminary in vitro biostability study.

The electrical stability of a novel polypyrrole (PPy)/poly(D,L-lactide) (PDLLA) composite was studied in vitro and compared with that of PPy-coated polyester fabrics. Specimens were incubated in Ringer's solution at 37 degrees C for up to 8 weeks with or without the circulation of DC current under a constant 100 mV voltage. In situ current variation with incubation time was recorded. The AC volume electrical conductivity of the specimens before and after incubation in phosphate-buffered saline was recorded using a frequency analyzer. Water absorption and weight loss were monitored metrologically. Changes in the oxidation state of incubated PPy were analyzed with X-ray photoelectron spectroscopy. The morphological changes were observed with scanning electron microscopy, and the glass transition temperature of the PDLLA was investigated using differential scanning calorimetry. The PPy/PDLLA composite in Ringer's solution sustained a relatively stable conductivity up to 8 weeks after an initial period of "conditioning." The PPy-coated fabrics experienced a rapid loss of conductivity when subjected to electrical circulation and regained part of it when disconnected. The volume conductivity of the nonincubated PPy/PDLLA membrane behaved as a typical conductor in the low-frequency range. The mechanisms involved in the various electrical behaviours of the PPy/PDLLA composite and PPy-coated fabrics are discussed. In conclusion, the PPy/PDLLA composite was able to deliver a biologically significant electrical current in a simulated biological solution for up to 8 weeks and therefore may be considered as a first-generation synthetic biodegradable bioconductor.

Biocompatible Materials↗