Compression, compaction, and disintegration properties of low crystallinity celluloses produced using different agitation rates during their regeneration from phosphoric acid solutions.

V Kumar; S H Kothari; G S Banker

doi:10.1208/pt020207

Home/Archive/PubMed

PubMed · 14727882

Compression, compaction, and disintegration properties of low crystallinity celluloses produced using different agitation rates during their regeneration from phosphoric acid solutions.

V Kumar·S H Kothari·G S Banker

View original source ↗Export metadata ↓

Abstract

The tabletting characteristics of low crystallinity celluloses (LCPC)-LCPC-700, LCPC-2000, and LCPC-4000-prepared using agitation rates of 700, 2000, and 4000 rpm, respectively, during their regeneration from phosphoric acid, were evaluated and compared with those of Avicel PH-102 and Avicel PH-302. The mean deformation pressure values calculated from the linear region of the Athy-Heckel curves indicated LCPC-4000 to be the most ductile material. The area under the Athy-Heckel curve for LCPC-4000 was 330 MPa, whereas LCPC-700 and LCPC-2000 showed a corresponding value similar to that of Avicel PH-102 and Avicel PH-302 (192-232 MPa). The tensile strength of LCPC and Avicel compacts increased linearly with increasing applied pressures. A comparison of the area under the tensile strength-compression pressure curves indicated that LCPC-4000 formed the strongest tablets. The strengths of LCPC-700 and LCPC-2000 compacts, in contrast, were slightly lower than that of Avicel PH-302 and Avicel PH-102, respectively. The compacts of both LCPC-4000 and Avicel PH-102 were intact in water for 6 hours, whereas LCPC-2000 and Avicel PH-302 compacts disintegrated in 4 minutes and 2 minutes, respectively. In conclusion, LCPC-4000 was the most ductile material and exhibited the highest compression and compaction characteristics. The corresponding properties of LCPC-700 and LCPC-2000, in contrast, were comparable to that of Avicel PH-102 or Avicel PH-302.

Explore related subjects

Cellulose Chemistry, Pharmaceutical Crystallization Drug Compounding Excipients Phosphoric Acids Solutions Tablets Journal Article

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

V Kumar, S H Kothari, G S Banker. 2001-05-11. Compression, compaction, and disintegration properties of low crystallinity celluloses produced using different agitation rates during their regeneration from phosphoric acid solutions.. https://doi.org/10.1208/pt020207

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2026

Compost microbiomes as reservoirs of cellulolytic microorganisms for cellulosic textile degradation.

Cellulosic textiles, constituting over 30% of global fibre production, are biodegradable but remain challenging to recycle at scale owing to their high crystallinity, chemical finishes, and heterogeneous waste streams. Although microorganisms drive cellulose turnover in natural ecosystems, their potential for transforming anthropogenic cellulosic waste remains largely unexplored. In this study, composting was evaluated both as a sustainable approach to textile biodegradation and a reservoir of cellulolytic microorganisms with biotechnological potential. Biodegradation assays of cotton and lyocell were integrated with shotgun metagenomics and targeted cultivation to identify microbial taxa and enzymes involved in cellulose degradation. Composting trials showed that degradation was strongly influenced by both composting system and fibre composition. Community composting achieved near-complete textile disintegration, while shredded textiles exhibited the highest degradation rates, reaching up to 97%. Shotgun metagenomic revealed a bacterial-dominated community enriched in Actinomycetota and Bacillota and characterised by an abundance of glycoside hydrolases. Culture-based screening recovered 62 microbial isolates, of which Neurospora and Aspergillus exhibited the highest cellulolytic activity (>60%). In vitro assays further showed that cotton was more readily degraded than lyocell, with several isolates achieving >70% mass loss. Metagenomic approach revealed a predominantly bacterial composting community at the sampled stage, whereas cultivation preferentially recovered fungi that, despite their low relative abundance in situ, exhibited strong cellulolytic potential. These findings highlight the potential of composting as a sustainable end-of-life strategy for cellulosic textiles and identify compost microbiomes as valuable reservoirs of cellulolytic microorganisms for the development of sustainable bioprocesses for textile waste treatment.

Cellulose↗

PubMed2007

Optimization of enzyme complexes for lignocellulose hydrolysis.

The ability of a commercial Trichoderma reesei cellulase preparation (Celluclast 1.5L), to hydrolyze the cellulose and xylan components of pretreated corn stover (PCS) was significantly improved by supplementation with three types of crude commercial enzyme preparations nominally enriched in xylanase, pectinase, and beta-glucosidase activity. Although the well-documented relief of product inhibition by beta-glucosidase contributed to the observed improvement in cellulase performance, significant benefits could also be attributed to enzymes components that hydrolyze non-cellulosic polysaccharides. It is suggested that so-called "accessory" enzymes such as xylanase and pectinase stimulate cellulose hydrolysis by removing non-cellulosic polysaccharides that coat cellulose fibers. A high-throughput microassay, in combination with response surface methodology, enabled production of an optimally supplemented enzyme mixture. This mixture allowed for a approximately twofold reduction in the total protein required to reach glucan to glucose and xylan to xylose hydrolysis targets (99% and 88% conversion, respectively), thereby validating this approach towards enzyme improvement and process cost reduction for lignocellulose hydrolysis.

Cellulose↗

PubMed2007

Wax removal for accelerated cotton scouring with alkaline pectinase.

A rational approach has been applied to design a new environmentally acceptable and industrially viable enzymatic scouring process. Owing to the substrate specificity, the selection of enzymes depends on the structure and composition of the substrate, i.e. cotton fibre. The structure and composition of the outer layers of cotton fibre has been established on the basis of thorough literature study, which identifies wax and pectin removal to be the key steps for successful scouring process. Three main issues are discussed here, i.e. benchmarking of the existing alkaline scouring process, an evaluation of several selected acidic and alkaline pectinases for scouring, and the effect of wax removal treatment on pectinase performance. It has been found that the pectinolytic capability of alkaline pectinases on cotton pectin is nearly 75% higher than that of acidic pectinases. It is concluded that an efficient wax removal prior to pectinase treatment indeed results in improved performance in terms of hydrophilicity and pectin removal. To evaluate the hydrophilicity, the structural contact angle (theta) was measured using an auto-porosimeter.

Cellulose↗