Intrapulpal temperature increases with temporary crown and bridge materials.

Sean Whalen; Murray Bouschlicher

PubMed · 15055650

Intrapulpal temperature increases with temporary crown and bridge materials.

Abstract

The exothermic setting reaction of provisional composites and acrylics that occurs during the intraoral fabrication of temporary crowns or bridges may cause a significant heat buildup. Intrapulpal temperature increases of 5.5 degrees C may elicit a marked intrapulpal response, both immediately and after prolonged intervals. This study compared the maximum intrapulpal temperature increase associated with the exothermic setting reaction of six temporary crown and bridge materials. The roots of a mandibular molar were prepared for a full crown and suspended in a water bath. A peristaltic pump perfused the pulp chamber with water (37.0 degrees C), simulating a blood flow of 40-50 mL/100 g of tissue/min. Maximum temperature increases among groups were compared using a one-way ANOVA and Tukey HSD post hoc test (alpha = 0.05).

Explore related subjects

Acrylic Resins Body Temperature Crowns Dental Pulp Dental Restoration, Temporary Hot Temperature Humans Journal Article Research Support, Non-U.S. Gov't Research Support, U.S. Gov't, P.H.S.

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Sean Whalen, Murray Bouschlicher. Intrapulpal temperature increases with temporary crown and bridge materials.. https://pubmed.ncbi.nlm.nih.gov/15055650/

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Calcium polycarbophil improves constipation in primary autonomic failure and multiple system atrophy subjects.

Explore the source record for details and available documents.

Acrylic Resins↗

PubMed2007

Influence of the activator in an acrylic bone cement on an array of cement properties.

In all but one of the acrylic bone cement brands used in cemented arthroplasties, N,N-dimethyl-4-toluidine (DMPT) serves as the activator of the polymerization reaction. However, many concerns have been raised about this activator, all related to its toxicity. Thus, various workers have assessed a number of alternative activators, with two examples being N,N-dimethylamino-4-benzyl laurate (DMAL) and N,N-dimethylamino-4-benzyl oleate (DMAO). The results of limited characterization of cements that contain DMAL or DMAO have been reported in the literature. The present work is a comprehensive comparison of cements that contain one of these three activators, in which the values of a large array of their properties were determined. These properties range from the setting time and maximum exotherm temperature of the curing cement to the variation of the loss elastic modulus of the cured cement with frequency of the applied indenting force in dynamic nanoindentation tests. The present results, taken in conjunction with those presented in previous reports by the present authors and co-workers on other properties of these cements, indicate that both DMAL and DMPT are suitable alternatives to DMPT.

Acrylic Resins↗

PubMed2007

Dynamic scaling of polymer gels comprising nanoparticles.

We present dynamic light scattering (DLS) measurements of soft poly(methyl-methacrylate) (PMMA) and polyacrylamide (PA) polymer gels prepared with trapped bodies (latex spheres or magnetic nanoparticles). We show that the anomalous diffusivity of the trapped particles can be analyzed in terms of a fractal Gaussian network gel model for the entire time range probed by DLS technique. This model is a generalization of the Rouse model for linear chains extended for structures with power law network connectivity scaling, which includes both percolating and uniform bulk gel limits. For a dilute dispersion of strongly scattering particles trapped in a gel, the scattered electric field correlation function at small wavevector ideally probes self-diffusion of gel portions imprisoning the particles. Our results show that the time-dependent diffusion coefficients calculated from the correlation functions change from a free diffusion regime at short times to an anomalous subdiffusive regime at long times (increasingly arrested displacement). The characteristic time of transition between these regimes depends on scattering vector as approximately q(-2), while the time decay power exponent tends to the value expected for a bulk network at small q. The diffusion curves for all scattering vectors and all samples were scaled to a single master curve.

Acrylic Resins↗