How to optimize the experimental design of quantitative atomic resolution TEM experiments?

S Van Aert; A J den Dekker; D Van Dyck

doi:10.1016/j.micron.2004.01.007

Home/Archive/PubMed

PubMed · 15120126

How to optimize the experimental design of quantitative atomic resolution TEM experiments?

S Van Aert·A J den Dekker·D Van Dyck

View original source ↗Export metadata ↓

Abstract

A quantitative measure is proposed to evaluate and optimize the design of quantitative atomic resolution TEM experiments. It aims at precise measurement of unknown structure parameters. Specifically, the proposed measure quantifies the statistical precision with which positions of atom columns can be estimated. The optimal design is then given by the combination of microscope settings for which this precision is highest. The proposed measure is also used to find out if new instrumental developments improve the precision as compared to existing methods.

Explore related subjects

Microscopy, Electron Reproducibility of Results Research Design Sensitivity and Specificity Journal Article Research Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

S Van Aert, A J den Dekker, D Van Dyck. 2004. How to optimize the experimental design of quantitative atomic resolution TEM experiments?. https://doi.org/10.1016/j.micron.2004.01.007

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2006

In-plane large single-walled carbon nanotube films: in situ synthesis and field-emission properties.

Explore the source record for details and available documents.

Microscopy, Electron↗

PubMed2006

Synthesis of soluble phosphate polymers by RAFT and their in vitro mineralization.

Soluble linear (non-cross-linked) poly(monoacryloxyethyl phosphate) (PMAEP) and poly(2-(methacryloyloxy)ethyl phosphate) (PMOEP) were successfully synthesized through reversible addition-fragmentation chain transfer (RAFT)-mediated polymerization and by keeping the molecular weight below 20 K. Above this molecular weight, insoluble (cross-linked) polymers were observed, postulated to be due to residual diene (cross-linkable) monomers formed during purification of the monomers, MOEP and MAEP. Block copolymers consisting of PMAEP or PMOEP and poly(2-(acetoacetoxy)ethyl methacrylate) (PAAEMA) were successfully prepared and were immobilized on aminated slides. Simulated body fluid studies revealed that calcium phosphate (CaP) minerals formed on both the soluble polymers and the cross-linked gels were very similar. Both the PMAEP polymers and the PMOEP gel showed a CaP layer most probably brushite or monetite based on the Ca/P ratios. A secondary CaP mineral growth with a typical hydroxyapatite (HAP) globular morphology was found on the PMOEP gel. The soluble PMOEP film formed carbonated HAP according to Fourier transform infrared (FTIR) spectroscopy. Block copolymers attached to aminated slides showed only patchy mineralization, possibly due to the ionic interaction of negatively charged phosphate groups and protonated amines.

Microscopy, Electron↗

PubMed2005

Porous structure of natural and modified clinoptilolites.

The evaluation of the pore-size distribution (PSD) of natural and modified mesoporous zeolites, i.e., clinoptilolites is presented. We demonstrate the SEM results showing that the pores of fracture-type from 25-50 nm to 100 nm in size between clinoptilolite grains, as well as pores between crystal aggregates up to 500 nm in size are present in the studied material. The detailed distribution of pore sizes and tortuosity factor of the above-mentioned materials are determined from the adsorption-desorption isotherms of nitrogen measured volumetrically at 77 K. To obtain the reliable pore size distribution (PSD) of the above-mentioned materials both adsorption and desorption branches of the experimental hysteresis loop are described simultaneously by recently developed corrugated pore structure model (CPSM) of Androutsopoulos and Salmas. Evaluated pore size distributions are characterized by well-defined smooth peaks placed in the region of the mesoporosity. Moreover, the mean pore diameter calculated from the classical static measurement of nitrogen adsorption at 77 K correspond very well to the pore diameters from SEM, showing the applicability of the CPSM for characterization of the porosity of natural zeolites. We conclude that classical static adsorption measurements combined with the proper modeling of the capillary condensation/evaporation phenomena are a powerful method which can be applied for pore structure characterization of natural and modified clinoptilolites.

Microscopy, Electron↗