Titanium orthodontic brackets: structure, composition, hardness and ionic release.

Christiana Gioka·Christoph Bourauel·Spiros Zinelis·Theodore Eliades·Nikolaos Silikas·George Eliades
View original source ↗Export metadata ↓

Abstract

OBJECTIVES: The aim of the present study was to investigate the composition, morphology, bulk structure and ionic release of two brands of titanium orthodontic brackets: Orthos2 (Ormco, USA) and Rematitan (Dentaurum, Germany). METHODS: Five specimens of each group were examined with computerized X-ray microtomography, to reveal the morphology and structure of brackets, whilst resin-embedded and metallographically polished specimens were subjected to SEM/EDS analysis and Vickers microhardness measurements. Brackets were also maintained in 0.9% saline for 2 months and the ionic release in the immersion medium was determined with Inductively Coupled Plasma Atomic Emission Spectroscopy. The results of the hardness and ionic release measurements were statistically analyzed with two-way ANOVA and Tukey's test (alpha = 0.05). RESULTS: Orthos2 brackets consisted of two parts, the base (commercially pure Ti grade II) and the wing (Ti-6Al-4V alloy), joined together by laser welding, producing large gaps along the base-wing interface. The base was of lower hardness (Hv = 145), than the wing (Hv = 392) and incorporated a standard foil base-mesh pad. Rematitan brackets consisted of commercially pure Ti grade IV, with a single-piece manufacturing pattern of virtually identical hardness (p > 0.05) at the base and wings, featuring a laser-etched base-mesh pad. The hardness of the Rematitan brackets was significantly lower than the hardness of the Orthos2 wings, but double the hardness of the Orthos2 base. Released Ti levels were below the threshold level (1 ng/ml) of analysis for both materials, whilst traces of Al (3 ppm) and V (2 ppm) were found in the immersion media for Ti-6Al-4V alloy. SIGNIFICANCE: The structural and hardness differences found may influence the torque transfer characteristics from activated archwires to the brackets and the crevice corrosion potential at the base-wing interface (Orthos2). The detection of Al and V in the immersion medium (Orthos2) may imply a different biological response from the two types of Ti brackets.

Explore related subjects

AlloysDental AlloysElectron Probe MicroanalysisHardnessIonsOrthodontic Appliance DesignOrthodontic BracketsSpectrophotometry, AtomicTitaniumTomography, X-Ray ComputedJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Christiana Gioka, Christoph Bourauel, Spiros Zinelis, Theodore Eliades, Nikolaos Silikas, George Eliades. 2004. Titanium orthodontic brackets: structure, composition, hardness and ionic release.. https://doi.org/10.1016/j.dental.2004.02.008

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2005

Varying Ti-6Al-4V surface roughness induces different early morphologic and molecular responses in MG63 osteoblast-like cells.

Osteoblast response to Ti implants depends not only on the chemistry of the implant but also on the physical properties of the implant surface, such as microtopography and roughness. This study was undertaken to examine early changes in cell morphology and gene expression during the early phase of osteoblast interaction with titanium alloy (Ti-6Al-4V) surfaces of two different roughnesses. MG63 osteoblast-like cells were cultured for 2, 6, 24, and 72 h on smooth (Ra=0.18+/-0.03 microm) and rough (Ra=2.95+/-0.23 microm) Ti-6Al-4V surfaces. Changes in cell proliferation were assessed by measuring cell number after 72 h in culture. Morphological characteristics were observed by scanning electron microscopy after 2, 6, and 24 h of culture. Changes in gene expression for extracellular signal-regulated kinase 2 (Erk2), type I collagen (alpha2[I] collagen), phospholipase C-gamma2 (Plc-gamma2), and beta-actin were measured by RT-PCR after 6 and 24 h in culture. Cell number was significantly higher on the smooth surface. In scanning electron micrographs, cells on smooth Ti-6Al-4V were spherical and raised up from the surface after 2 h in culture. In contrast, cells on the rough surface adopted an irregular, elongated shape that spanned across pits in the surface. At 24 h, cells on the smooth surface had flattened, become elongate, and covered the surface. In contrast, cells on the rough surface appeared more differentiated in shape and the margins of the cells were irregular, with many processes extending out, following the contour of the surface. Of the genes examined, only Erk2 and beta-actin showed a change in expression with surface roughness. Both genes were upregulated (p<0.05) on the rough surface at 6 h. These results indicate that Ti-6Al-4V surface roughness affects osteoblast proliferation, morphology, and gene expression, and that these effects can be measured after periods as short as 2-6 h.

Alloys↗
PubMed2005

Electrochemical studies on zirconium and its biocompatible alloys Ti-50Zr at.% and Zr-2.5Nb wt.% in simulated physiologic media.

Different electrochemical studies were carried out for Zr and its biocompatible alloys Ti-50Zr at.% and Zr-2.5Nb wt.% in solutions simulating physiologic media, Ringer and PBS (phosphate buffered saline) solutions. The results from rest-potential measurements showed that the three materials are spontaneously passivated in both solutions and that the Ti-50Zr alloy has the greatest tendency for spontaneous oxide formation. Some corrosion parameters (such as the pitting and repassivation potentials) were obtained via cyclic voltammetry in both solutions, revealing that the Ti-50Zr has the best corrosion protection while Zr has the worst. On the other hand, the pre-anodization (up to 8 V vs. SCE) of the alloys in a 0.15 mol/L Na2SO4 solution led to a significant improvement in their protection against pitting corrosion when exposed to the Ringer solution. Elemental analyses by EDX showed that during pitting corrosion, there is no preferential corrosion of any of the alloying elements (Zr, Ti, Nb).

Alloys↗
PubMed2005

In vitro interaction between surface-treated Ti-6Al-4V titanium alloy and human peripheral blood mononuclear cells.

The Ti-6Al-4V titanium alloy is widely employed as an implant material. The effects of Ti-6Al-4V samples, tested in both an untreated state and one in which the samples were subjected to a glow-discharge treatment performed with the use of air, on human peripheral blood mononuclear cells (PBMC) were studied. Apoptosis, undetectable after 24-h contact of PBMC with the two sample types, is induced after 48 h by treated samples, and, after 48 h, but in the presence of 1.5 microg/mL PHA, by both sample types. The expression of intercellular adhesion molecule-1 (ICAM-1) always increases, in comparison with control, in PBMC put in contact with the two sample types. In the same way, a remarkable increase in tumor necrosis-alpha (TNF-alpha) release in the culture medium is registered, when PBMC are put in contact with the two sample types for 24 and 48 h. Human umbilical-vein endothelial cells (HUVEC) cocultured for 48 h with PBMC, previously incubated with the two sample types for 24 h, show an increase in ICAM-1 and vascular cell adhesion molecule-1 (VCAM-1) protein expression in comparison with control (HUVEC cocultured with control PBMC), indicating that inflammatory phenomena might occur. Taken together, these results suggest that, although plasma-treated titanium alloy shows a better biocompatibility in comparison with the untreated one, attention must be paid to the careful control of the first signs of inflammation.

Alloys↗