Dialkylnitrosamines in elastomers.

F W Yeager·N N Van Gulick·B A Lasoski
View original source ↗Export metadata ↓

Abstract

Accelerators and stabilizers used in natural rubber and many types of synthetic rubber are often derived from dialkylamines. It has been found that raw polymers, compounded uncured elastomers, and cured rubber parts containing these dialkylamino compounds emit low concentrations of the corresponding dialkylnitrosamine (R2N-N = O) when they are heated. Exposure of operators working with these materials can be reduced below a level of 50 parts per trillion by volume in air by use of ventilation velocities of about 50 ft/min. around the operation. The analytical method is described.

Explore related subjects

ElastomersNitrosaminesOccupational HealthJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

F W Yeager, N N Van Gulick, B A Lasoski. 1980. Dialkylnitrosamines in elastomers.. https://doi.org/10.1080/15298668091424519

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2006

High-performance elastomeric nanocomposites via solvent-exchange processing.

The incorporation of nanoparticles into engineering thermoplastics affords engineers an opportunity to synthesize polymer nanocomposites that potentially rival the most advanced materials in nature. Development of these materials is difficult because thermodynamic and kinetic barriers inhibit the dispersal of inorganic, often hydrophilic nanoparticles in hydrophobic polymer matrices. Using a new solvent-exchange approach, we preferentially reinforce the hard microdomains of thermoplastic elastomers with smectic clay of similar characteristic dimensions. The strong adhesion between the clay and the hard microdomains coupled with the formation of a percolative network not only stiffens and toughens, but increases the heat distortion temperature of the material and induces reversible thermotropic liquid-crystalline transitions. The discotic clay platelets induce morphological ordering over a range of length scales, which results in significant thermomechanical enhancement and expands high-temperature applications. Merging block-copolymer processing techniques with this method for preferential ordering of nanoparticle facilitates the development of new, hierarchically ordered materials.

Elastomers↗
PubMed2006

ASAXS, SAXS and SANS investigations of vulcanized elastomers filled with carbon black.

Small-angle X-ray scattering (SAXS) performed down to small q values (q <or= 10(-3) A(-1)) is a powerful method for investigating the arrangement of filler aggregates in filled elastomers under uniaxial strain. Meanwhile, for vulcanized samples, zinc oxide is used as an additive. Owing to their high contrast, the ZnO particles remaining in the manufactured composite are strong X-ray scatterers. In the low-q domain, their scattering hides that of filler aggregates (carbon black, pyrogenic silica) and must be quantified in order to be suppressed. To this end, anomalous SAXS (ASAXS) and small-angle neutron scattering (SANS) have been performed. It is shown that ASAXS measurements can be performed down to small q values (q <or= 10(-3) A(-1)). Therefore ASAXS is well adapted to separate the contributions of ZnO and filler scattering. For neutron scattering the contrast of the ZnO particles is similar to that of carbon. Because the amount of ZnO is much smaller than that of filler, ZnO scattering can be neglected. Owing to multiple scattering effects, however, SANS can only be used for very thin samples (less than about 0.25 mm). It is shown that, providing multiple scattering is avoided, ASAXS and SANS yield similar scattering curves for the filler aggregates.

Elastomers↗
PubMed2006

Hydrophilic composite elastomeric mold for high-resolution soft lithography.

Here, we introduce a nanopatternable hydrophilic composite elastomer highly desirable for both nanostructure patterning via solvent-assisted micromolding (SAMIM) and microcontact printing of polar inks. This composite precursor is prepared by blending two UV-curable materials, Norland Optical Adhesives (NOA) 63 and poly(ethylene glycol) diacrylate (PEGDA), in an appropriate ratio; upon UV polymerization, a nanopatternable elastomer with preferential permeability both to aqueous and organic solvent is fabricated. Using this composite mold, nanoscale SAMIM of poly(4-vinylpyridine) (P4VP) and microcontact printing of a polar biomolecule, bovine serum albumin (BSA), was successfully demonstrated, paving the way for facile and efficient reproduction of various nanopatterns and a biomolecule-printed array platform.

Elastomers↗