Solid surface mapping by inverse gas chromatography.

Abstract

Inverse gas chromatography (IGC) at infinite dilution, is a technique for characterising solid surfaces. Current practice is the injection of n-alkane homologous series to obtain the free energy of adsorption of the CH2 group, from which the London component of the solid surface free energy, gamma(d)s, is calculated. A value around 40 mJ/m2 is obtained for poly(ethylene), and 30 mJ/m2 for a clean glass fibre, while the potential surface interactivity of a glass fibre is far greater than that of poly(ethylene). A specific component of the surface, in mJ/m2, should be calculated in order to obtain significant parameters. As applied up to date, when calculating the specific component of the surface energy, the fact that W(sp)a energy values are in a totally different scale than AN or DN values is a major drawback. Consequently, Ka and Kb values obtained are in arbitrary energy units, different from those of the London component measured by injecting the n-alkane series. This paper proposes a method to obtain Ka and Kb values of the surface in the same energetic scale than the London component. The method enables us to correct the traditional London component of a solid, obtaining a new value, where the amount of WaCH2 accounting for Debye interactions with polar sites, is excluded. As a result, an approach to surface mapping is performed in several different substrate materials. We show results obtained on different solid surfaces: poly(ethylene), clean glass fibre, glass beads, chemically modified glass beads and carbon fibre.