Mapping patterned potential energy landscapes with diffusing colloidal probes.

Hung-Jen Wu·W Neil Everett·Samartha G Anekal·Michael A Bevan
View original source ↗Export metadata ↓

Abstract

We report a new method for mapping patterned surfaces based on monitoring the interactions of freely diffusing colloidal probes with pattern features to generate measured potential energy landscapes. Evanescent wave scattering and video microscopy are used to track 3D center positions of nominal 2 microm silica colloids as they diffuse over 5-20-nm-thick patterned gold films. An analysis of ensemble-averaged particle height histograms on different pattern features using Boltzmann's equation produces local electrostatic and van der Waals potentials in good agreement with independent measurements and predictions. Absolute separation is obtained from theoretical fits to measured potential-energy profiles and direct measurement by depositing silica colloids onto gold surfaces via electrophoretic deposition. As colloidal probe and pattern feature dimensions become comparable, potential energy profiles suffer some distortion due to the increased probability of probes sampling pattern feature edges. An analysis of interfacial colloidal probe diffusion in conjunction with potential energy measurements demonstrates a consistent interpretation of dissipative and conservative forces in these measurements. Future extensions of this work should produce similar approaches for interrogating physical, chemical, and biomolecular heterogeneous/patterned surfaces and structures with diffusing colloidal probes.

Explore related subjects

ColloidsGoldMetal NanoparticlesModels, ChemicalSilicon DioxideStatic ElectricityJournal ArticleResearch Support, Non-U.S. Gov'tResearch Support, U.S. Gov't, Non-P.H.S.

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Hung-Jen Wu, W Neil Everett, Samartha G Anekal, Michael A Bevan. 2006-08-01. Mapping patterned potential energy landscapes with diffusing colloidal probes.. https://doi.org/10.1021/la060501j

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2006

Ultrafast fluorescence resonance energy transfer in a reverse micelle: excitation wavelength dependence.

Fluorescence resonance energy transfer (FRET) from coumarin 480 (C480) to fluorescein 548 (F548) in a sodium dioctyl sulfosuccinate (AOT) reverse micelle is studied by picosecond and femtosecond emission spectroscopy. In bulk water, at the low concentration of the donor (C480) and the acceptor (F548), no FRET is observed. However, when the donor (C480) and the acceptor (F548) are confined in a AOT reverse micelle very fast FRET is observed. The time constants of FRET were obtained from the rise time of the emission of the acceptor (F548). In a AOT microemulsion, FRET is found to occur in multiple time scales--3, 200, and 2700 ps. The 3 ps component is assigned to FRET in the water pool of the reverse micelle with a donor-acceptor distance, 16 A. The 200 ps component corresponds to a donor-acceptor distance of 30 A and is ascribed to the negatively charged acceptor inside the water pool and the neutral donor inside the alkyl chains of AOT. The very long 2700 ps component may arise due to FRET from a donor outside the micelle to an acceptor inside the water pool and also from diffusion of the donor from bulk heptane to the reverse micelle. With increase in the excitation wavelength from 375 to 405 nm the relative contribution of the FRET due to C480 in the AOT reverse micelle (the 3 and 200 ps components) increases.

Colloids↗
PubMed2006

Metal-enhanced fluorescence from gold surfaces: angular dependent emission.

The first observation of Metal-Enhanced Fluorescence (MEF) from large gold colloids is presented. Gold colloids, 40 and 200 nm diameter, were deposited onto glass substrates in a homogeneous fashion. The angular-dependent fluorescence emission of FITC-HSA, adsorbed onto gold colloids, was measured on a rotating stage which was used to evaluate MEF at all spatial angles. The emission intensity of FITC-HSA was found to be up to 2.5-fold brighter than the emission on bare glass substrates at an angle of 270 degrees. This is explained by the Radiating Plasmon Model, whereby the combined system, composed of the fluorophore and the metal colloids, emits with the photophysical characteristics of the fluorophore, after the excitation and the partial radiationless energy transfer between the excited states of the fluorophore and the surface plasmons of the gold colloids. The fluorescence enhancement was found to be higher with 200 nm gold colloids as compared to 40 nm colloids due to the increased contribution of the scattering portion of the 200 nm gold colloid extinction spectrum. These observations suggest that gold colloids could be used in MEF applications, offering more stable surfaces than the commonly used silvered surfaces, for applications requiring longer term storage and use.

Colloids↗
PubMed2006

Application of cross-flow ultrafiltration for the determination of colloidal abundances in suboxic ferrous-rich ground waters.

A suboxic groundwater from a sandy coastal aquifer was sampled using a new air free, large volume sampling method. Subsequent processing for size fractionation was completed with a modified cross-flow ultrafiltration (CFF) system equipped with a 1 kDa CFF membrane. By purging the CFF system with nitrogen, no oxygen was able to reach the sample. With this optimization, the sample was processed with higher than 90% recovery in terms of both iron and phosphate. Only about 4% of iron and 20% of phosphate in the filtered (0.2 microm) groundwater sample was found to be in colloidal form in the groundwater. In contrast, if no care was taken to maintain the suboxic environment of the original sample, iron was rapidly and completely oxidized and subsequently adsorbed to the CFF membrane. Other elements, such as phosphorus, were also lost to the CFF membrane to a substantial degree, and the mechanism is most likely coprecipitation with iron oxides. This study thus strongly supports the importance of maintaining ambient redox conditions during sampling and fractionation, especially for the determinations of colloid abundances in groundwater.

Colloids↗