Arylthiolate-protected silver quantum dots.

Matthew R Branham·Alicia D Douglas·Allan J Mills·Joseph B Tracy·Peter S White·Royce W Murray
View original source ↗Export metadata ↓

Abstract

This paper describes a new, organic-soluble 4-tert-butylbenzyl mercaptan (BBT) monolayer-protected silver cluster (AgBBT MPC) as the first example of a dissolved silver nanoparticle that exhibits quantized one-electron double layer charging (QDL) voltammetry. Polydisperse AgBBT MPCs made by two different synthetic protocols, but with similar average core diameters (2.1 nm), exhibit sharply differing electrochemistry and optical absorbance spectra. A two-phase procedure (organic/aqueous, termed Prep A-AgBBT) produced MPCs exhibiting a 475 nm surface plasmon absorbance and QDL voltammetry. Neither property was seen for MPCs made by a single-phase procedure, termed Prep B-AgBBT. The difference is thought to reflect poor passivation to oxide formation in the latter Prep B procedure, which is supported by X-ray photoelectron spectroscopy results. Thermogravimetry, mass spectra, and electrochemistry results suggest an average stoichiometric formula of Ag140BBT53, but transmission electron microscopy shows that the products are also polydisperse and include polycrystalline aggregates. Dry, cast films of both Ag MPC preparations on interdigitated array electrodes exhibit low electron hopping conductivity, compared to Au MPCs.

Explore related subjects

GoldMaterials TestingQuantum DotsSilverSulfhydryl CompoundsComparative StudyJournal ArticleResearch Support, U.S. Gov't, Non-P.H.S.

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Matthew R Branham, Alicia D Douglas, Allan J Mills, Joseph B Tracy, Peter S White, Royce W Murray. 2006-12-19. Arylthiolate-protected silver quantum dots.. https://doi.org/10.1021/la062329p

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2026

Microalgae-Mediated Synthesis of Gold Nanoparticles from Indonesian Chlorella vulgaris InaCC M205 with Potential Anticancer Properties for Biomedical Application.

Sustainable nanomaterial synthesis has emerged as a critical strategy to reduce the environmental burden associated with conventional chemical synthesis method. Microalgae-derived biomolecules offer a promising platform for the green production of metal nanoparticles due to their rich bioactive compounds capable of acting as natural reducing and stabilizing agents. Here, we report the eco-friendly synthesis of gold nanoparticles (AuNPs) using extract of Indonesian microalga Chlorella vulgaris extract. To optimize the synthesis process, the effects of precursor-to-extract ratio, temperature, and incubation time were evaluated. Optimal synthesis of C5-AuNPs was obtained at 37 °C for 20 h with precursor to extract ratio of 6:4, resulting in moderately stable C5-AuNPs characterized by a surface plasmon resonance (SPR) peak at 541 nm. Furthermore, Fourier-transmission infra-red (FT-IR) analysis revealed the involvement of functional groups of C. vulgaris extract in the interaction with Au+ during the production of C5-AuNPs. Transmission electron microscopy (TEM) demonstrated the formation of uniformly spherical nanoparticles with an average diameter of approximately 8.8 nm. Biological evaluation showed that the synthesized C5-AuNPs exerted pronounced dose-dependent cytotoxicity against MCF-7 breast cancer cells with an IC50 threshold of 21.17 ppm, while no toxicity appears in normal HEK293 cells. Mechanistically, the C5-AuNPs induced early apoptosis and inhibit cell-cycle progression at the stage of G0/G1. Collectively, these findings demonstrate that C. vulgaris-mediated AuNPs represent a promising preliminary in vitro findings for cancer therapy candidate.

Gold↗
PubMed2007

Thin films composed of multiwalled carbon nanotubes, gold nanoparticles and myoglobin for humidity detection at room temperature.

Optically transparent and electrically conductive nanocomposite thin films consisting of multiwalled carbon nanotubes (MWCNTs), gold nanoparticles (GNPs) and myoglobin molecules that glue GNPs and MWCNTs together are fabricated for the first time on glass substrates from aqueous solution. The nanocomposite thin film is capable of varying its resistance, impedance or optical transmittance at room temperature in response to changes in ambient humidity. The conductometric sensitivity to relative humidity (RH) of the nanocomposite thin film is compared with those of the pure and Mb-functionalized MWCNT layers. The pure MWCNT layer shows a small increase in its resistance with increasing RH due to the effect of p-type semiconducting nanotubes present in the film. In contrast, a four times higher sensitivity to RH is observed for both the nanocomposite and Mb-functionalized MWCNT thin films. The sensitivity enhancement is attributable to swelling of the thin films induced by water absorption in the presence of Mb molecules, which increases the inter-nanotube spacing and thereby causes a further increase of the film resistance. A humidity change as low as DeltaRH=0.3 % has been readily detected by conductometry using the nanocomposite thin film.

Gold↗
PubMed2007

pH-controlled reversible assembly of peptide-functionalized gold nanoparticles.

The assembly/disassembly process of carboxylated peptide-functionalized gold nanoparticles (peptide-GNPs) was studied within the pH interval of 2.5 to 10. The assembly process was not well controlled at pH 2.5, leading to the formation of 3D structures of GNPs, whereas at pH 4 we observed controlled assembly with the formation of only a network of 1D chains. In the pH range of 2.5 to 4, the assembly proceeded with the formation of a combination of two extremes (i.e., having both 1D and 2D nanostructures). The assembly process was reversed on changing the pH of the medium to 10. The assembly/disassembly process was monitored using UV-vis spectroscopy and finally confirmed by TEM analysis. This assembly resulted from the intermolecular H-bonding between two carboxylic acid groups of peptides bound to the two adjacent GNPs and were confirmed by FTIR spectroscopy.

Gold↗