Relationship between blood compatibility and water structure--comparative study between 2-methoxyethylacrylate- and 2-methoxyethylmethacrylate-based random copolymers.

Etsuko Hirota; Masaru Tanaka; Akira Mochizuki

doi:10.1002/jbm.a.31113

Home/Archive/PubMed

PubMed · 17206625

Relationship between blood compatibility and water structure--comparative study between 2-methoxyethylacrylate- and 2-methoxyethylmethacrylate-based random copolymers.

Etsuko Hirota·Masaru Tanaka·Akira Mochizuki

View original source ↗Export metadata ↓

Abstract

We have proposed that the excellent blood compatibility of poly(2-methoxyethylacrylate (MEA)) is caused by freezing bound water contained in it on the basis of results on platelet activation (Tanaka and Mochizuki, J Biomed Mater Res A 2004; 68:684-695). To clarify the applicability of this mechanism to other indexes for blood compatibility, the relationship between complement activation and water structure was investigated by using two copolymers, poly(MEA-2-hydroxyethylmethacrylate (HEMA)) and poly(2-methoxyethylmethacrylate (MEMA)-HEMA), where HEMA content was varied from 25 to 90 mol %. ESCA analysis revealed that the surface compositions of these copolymers (dry state) agreed with the compositions determined by (1)H NMR. However, analysis by water contact angle (wet state) showed that their surfaces were quite different. The contact angle of poly(MEMA-HEMA) depended on the monomer composition, whereas the angle of poly(MEA-HEMA) was close to that of polyHEMA regardless of the monomer composition. The effect of HEMA content in the copolymers on complement activation (production of C3a) was investigated in an in vitro test. The activation by poly(MEMA-HEMA) was enhanced according to the HEMA content, while the activation by poly(MEA-HEMA) with 0-40 mol % of HEMA was weak and did not depend on the HEMA content. These properties are discussed from the viewpoints of the water structure observed by DSC and the surface structure.

Explore related subjects

Calorimetry, Differential Scanning Complement Activation Humans Materials Testing Methacrylates Phase Transition Polymethacrylic Acids Spectrum Analysis Surface Properties Water Comparative Study Journal Article Research Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Etsuko Hirota, Masaru Tanaka, Akira Mochizuki. 2007-06-01. Relationship between blood compatibility and water structure--comparative study between 2-methoxyethylacrylate- and 2-methoxyethylmethacrylate-based random copolymers.. https://doi.org/10.1002/jbm.a.31113

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Shape dependence in the formation of condensed phases exhibited by disubstituted sucrose esters.

We report on the self-organizing properties of sucrose esters that are di-(1',6', 1',6, and 6,6')-substituted with aliphatic chains of identical or different chain lengths and levels of saturation. For the materials possessing two saturated aliphatic chains, the compounds exhibited thermotropic lamellar smectic A phases. A remarkable new phase transition was observed for the di-octadecanoyl homologue in which one smectic A phase transformed into another with a continuous change in layer spacing, but with a discontinuous change in the correlation length. The incorporation of long cis-unsaturated chains led to increased cross-sectional areas of the chains relative to the sucrose head groups and, hence, columnar phases were observed.

Calorimetry, Differential Scanning↗

PubMed2007

Photoluminescence and conductivity of self-assembled pi-pi stacks of perylene bisimide dyes.

The self-assembly of a new, highly fluorescent perylene bisimide dye 2 into pi stacks, both in solution and condensed phase, has been studied in detail by NMR spectroscopy, vapor pressure osmometry (VPO), UV/Vis and fluorescence spectroscopy, differential scanning calorimetry (DSC), optical polarizing microscopy (OPM) and X-ray diffraction. The NMR and VPO measurements revealed the formation of extended pi-pi stacks of the dye molecules in solution. The aggregate size determined from VPO and DOSY NMR measurements agree well with that obtained from the concentration and temperature-dependent UV/Vis spectral data by employing the isodesmic model (equal K model). In the condensed state, dye 2 possesses a hexagonal columnar liquid crystalline (LC) phase as confirmed by X-ray diffraction analysis. The columnar stacking of this dye has been further explored by atomic force microscopy (AFM). Well-resolved columnar nanostructures of the compound are observed on graphite surface. A color-tunable luminescence from green to red has been observed upon aggregation which is accompanied by an increase of the fluorescence lifetime and depolarization. The observed absorption properties can be explained in terms of molecular exciton theory. The charge transport properties of dye 2 have been investigated by pulse radiolysis-time resolved microwave conductivity measurements and a 1D charge carrier mobility up to 0.42 cm(2) V(-1) s(-1) is obtained. Considering the promising self-assembly, semiconducting, and luminescence properties of this dye, it might serve as a useful functional material for nano(opto)electronics.

Calorimetry, Differential Scanning↗

PubMed2007

A calorimetric investigation of thermodynamic and molecular mobility contributions to the physical stability of two pharmaceutical glasses.

The purpose of this work was to investigate the contribution of thermodynamics and mobility to the physical stability of two pharmaceutical glasses with similar glass transition temperatures (Tg), by comparing configurational thermodynamic quantities and molecular relaxation time constants (tau) at temperatures below Tg. Ritonavir and nifedipine were chosen as model glasses because they show excellent and poor physical stability, respectively. Although ritonavir and nifedipine have similar Tg values (50 and 46 degrees C, respectively), amorphous ritonavir is quite stable while nifedipine has been reported to crystallize at temperatures as low as 40 degrees C below Tg. Modulated temperature differential scanning calorimetry (MTDSC) was used to characterize both crystalline phases and freshly prepared glasses. The glasses were then annealed at Tg-Ta = 25 degrees C while monitoring the extent of relaxation and heat capacity change as a function of time via MTDSC. Configurational thermodynamic quantities (Gc, Hc, and Sc) and molecular relaxation time constants, tau, were calculated from the calorimetric data. Interestingly, the Gibbs free energy driving force for crystallization was nearly identical for the two compounds. The largest differences were found in the configurational entropy (Sc) values for the fresh glasses and in the Sc values over time. Configurational entropy values were approximately 50% higher for ritonavir. The tau values of freshly prepared glasses indicated that both materials had similar initial mobility at the annealing temperatures and the temperature dependence of tau was approximately Arrhenius, regardless of age. Although initial tau values were similar, the tau values after 3 days annealing were approximately sixfold greater for ritonavir. The relatively poor physical stability of nifedipine compared to ritonavir is attributed to both the lower entropic barrier to crystallization for fresh and annealed glass, and higher molecular mobility in aged glasses of nifedipine. These observations below Tg are consistent with the previous work on physical stability of amorphous pharmaceuticals performed above Tg.

Calorimetry, Differential Scanning↗