Polyacrylic cements in dentistry.

Abstract

The polyacrylic cements were first introduced to dentistry in the middle 1960's when Smith showed the value of the polyacids, in developing adhesion to enamel and dentine. Within 10 years, Wilson had advanced the concept by changing the powder from a zinc oxide to glass and at the same time varying the poly-acid used. Both cements depend on the development of complex polyacrylate chains which can be linked with metal ions and in turn can form dynamic linkages with both enamel and dentine. The original polycarboxylate cement has many desirable characteristics and is still a useful cement for luting crowns and bridges and for lining cavities. However it is no longer widely used because it has been somewhat overshadowed by the glass ionomer cements which are even more versatile and have superior physical properties. By varying the type of glass, the fluoride content of the glass and the powder/liquid ratio as well as adding inclusions of other metals such as silver they can fulfil a variety of roles in restorative dentistry. However, as with any restorative material, it is essential that the operator fully understand the requirements for successful placement. The basic rules are reviewed for each of the types currently available and the steps for clinical success are detailed.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

G J Mount. 1990. Polyacrylic cements in dentistry.. https://pubmed.ncbi.nlm.nih.gov/2076229/

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

Influence of the activator in an acrylic bone cement on an array of cement properties.

In all but one of the acrylic bone cement brands used in cemented arthroplasties, N,N-dimethyl-4-toluidine (DMPT) serves as the activator of the polymerization reaction. However, many concerns have been raised about this activator, all related to its toxicity. Thus, various workers have assessed a number of alternative activators, with two examples being N,N-dimethylamino-4-benzyl laurate (DMAL) and N,N-dimethylamino-4-benzyl oleate (DMAO). The results of limited characterization of cements that contain DMAL or DMAO have been reported in the literature. The present work is a comprehensive comparison of cements that contain one of these three activators, in which the values of a large array of their properties were determined. These properties range from the setting time and maximum exotherm temperature of the curing cement to the variation of the loss elastic modulus of the cured cement with frequency of the applied indenting force in dynamic nanoindentation tests. The present results, taken in conjunction with those presented in previous reports by the present authors and co-workers on other properties of these cements, indicate that both DMAL and DMPT are suitable alternatives to DMPT.

Acrylic Resins↗

Dynamic scaling of polymer gels comprising nanoparticles.

We present dynamic light scattering (DLS) measurements of soft poly(methyl-methacrylate) (PMMA) and polyacrylamide (PA) polymer gels prepared with trapped bodies (latex spheres or magnetic nanoparticles). We show that the anomalous diffusivity of the trapped particles can be analyzed in terms of a fractal Gaussian network gel model for the entire time range probed by DLS technique. This model is a generalization of the Rouse model for linear chains extended for structures with power law network connectivity scaling, which includes both percolating and uniform bulk gel limits. For a dilute dispersion of strongly scattering particles trapped in a gel, the scattered electric field correlation function at small wavevector ideally probes self-diffusion of gel portions imprisoning the particles. Our results show that the time-dependent diffusion coefficients calculated from the correlation functions change from a free diffusion regime at short times to an anomalous subdiffusive regime at long times (increasingly arrested displacement). The characteristic time of transition between these regimes depends on scattering vector as approximately q(-2), while the time decay power exponent tends to the value expected for a bulk network at small q. The diffusion curves for all scattering vectors and all samples were scaled to a single master curve.

Acrylic Resins↗