High-flow-rate hydroxylapatites.

H Hirano·T Nishimura·T Iwamura
View original source ↗Export metadata ↓

Abstract

We have established a novel and simple method for preparing rigidly crystallized or granulated hydroxylapatites, which showed flow rates one order of magnitude higher in column chromatography than those of the Tiselius specimen (1). The essential difference in the procedures from the Tiselius method is that calcium phosphate, the precursor of hydroxylapatite, is generated not at room temperature but at either 45 or 95 degrees C. The capacities of the two hydroxylapatites for binding and fractionating protein, RNA, and DNA upon column chromatography were similar to those of Tiselius's hydroxylapatite. The 95 degrees C specimen can be dried with no change in the properties. Because of the reproducibly observed properties, including the extremely high flow rate with ease in handling as well as low cost and simple procedures with no additives and with no special equipment in preparation, our hydroxylapatites seem to be best so far for routine laboratory use.

Explore related subjects

Calcium PhosphatesChromatographyCrystallizationDurapatiteHydroxyapatitesMicroscopyTemperatureTime FactorsJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

H Hirano, T Nishimura, T Iwamura. 1985. High-flow-rate hydroxylapatites.. https://doi.org/10.1016/0003-2697(85)90463-4

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Effect of particle size of an amorphous calcium phosphate filler on the mechanical strength and ion release of polymeric composites.

The random clustering of amorphous calcium phosphate (ACP) particles within resin matrices is thought to diminish the strength of their polymerized composites. The objective of this study was to elucidate the effect of ball-milling on the particle size distribution (PSD) of ACP fillers and assess if improved dispersion of milled ACP in methacrylate resin sufficiently enhanced filler/matrix interactions to result in improved biaxial flexure strength (BFS), without compromising the remineralizing potential of the composites. Unmilled and wet-milled zirconia-hybridized ACP (Zr-ACP) fillers were characterized by PSD analysis, X-ray diffraction, thermogravimetric and chemical analysis, infrared spectroscopy, and scanning electron microscopy. Composite specimens made from a photoactivated, ternary methacrylate resin admixed with a mass fraction of 40% of un-milled or milled Zr-ACP were evaluated for the BFS (dry and wet) and for the release of calcium and phosphate ions into saline solutions. While having no apparent effect on the structure, composition, and morphology/topology of the fillers, milling significantly reduced the average size of Zr-ACP particulates (median diameter, d(m) = 0.9 +/- 0.2 microm) and the spread of their PSD. Better dispersion of milled Zr-ACP in the resins resulted in the improved BFS of the composites, even after aqueous soaking, and also gave a satisfactory ion release profile. The demonstrated improvement in the mechanical stability of anti-demineralizing/remineralizing ACP composites based on milled Zr-ACP filler may be beneficial in potentially extending their dental utility.

Calcium Phosphates↗
PubMed2007

Effects of incorporating nanosized calcium phosphate particles on properties of whisker-reinforced dental composites.

Clinical data indicate that secondary caries and restoration fracture are the most common problems facing tooth restorations. Our ultimate goal was to develop mechanically-strong and caries-inhibiting dental composites. The specific goal of this pilot study was to understand the relationships between composite properties and the ratio of reinforcement filler/releasing filler. Nanoparticles of monocalcium phosphate monohydrate (MCPM) were synthesized and incorporated into a dental resin for the first time. Silicon carbide whiskers were fused with silica nanoparticles and mixed with the MCPM particles at MCPM/whisker mass ratios of 1:0, 2:1, 1:1, 1:2, and 0:1. The composites were immersed for 1-56 days to measure Ca and PO4 release. When the MCPM/whisker ratio was changed from 0:1 to 1:2, the composite flexural strength (mean +/- SD; n = 5) decreased from 174 +/- 26 MPa to 138 +/- 9 MPa (p < 0.05). A commercial nonreleasing composite had a strength of 112 +/- 14 MPa. When the MCPM/whisker ratio was changed from 1:2 to 1:1, the Ca concentration at 56 days increased from 0.77 +/- 0.04 mmol/L to 1.74 +/- 0.06 mmol/L (p < 0.05). The corresponding PO4 concentration increased from 3.88 +/- 0.21 mmol/L to 9.95 +/- 0.69 mmol/L (p < 0.05). Relationships were established between the amount of release and the MCPM volume fraction v(MCPM) in the resin: [Ca]= 42.9 v(MCPM) (2.7), and [PO4] = 48.7 v(MCPM) (1.4). In summary, the method of combining nanosized releasing fillers with reinforcing fillers yielded Ca- and PO4-releasing composites with mechanical properties matching or exceeding a commercial stress-bearing, nonreleasing composite. This method may be applicable to the use of other Ca-PO4 fillers in developing composites with high stress-bearing and caries-preventing capabilities, a combination not yet available in any dental materials.

Calcium Phosphates↗