Fluoride-releasing acrylics.

H R Rawls
View original source ↗Export metadata ↓

Abstract

There are numerous examples in dentistry where demineralization, or even frank caries, develops near or in association with restorative or prosthetic materials. Leaking cavity margins and demineralization under bite splints are two examples. A slow-release source of fluoride could help to prevent these problems and provide added protection throughout the mouth. For this purpose a family of fluoride-releasing resins has been developed for use in various adhesive applications, and also for preparing temporary crowns and removable acrylic devices. These materials contain fluoride ions held to covalently bound positive charge sites within the polymer network. Release is by a diffusion/exchange mechanism in which anions from oral fluids diffuse to the charge sites and exchange with fluoride. Fluoride then diffuses to the surface and is released into solution. This method of release allows for the retention of adequate physical properties and is capable of a linear release rate for terms ranging from days to years.

Explore related subjects

Acrylic ResinsBiocompatible MaterialsComposite ResinsDelayed-Action PreparationsDental CariesFluoridesHumansPit and Fissure SealantsJournal ArticleResearch Support, Non-U.S. Gov'tResearch Support, U.S. Gov't, P.H.S.Review

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

H R Rawls. 1987. Fluoride-releasing acrylics.. https://doi.org/10.1177/088532828600100406

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Influence of the activator in an acrylic bone cement on an array of cement properties.

In all but one of the acrylic bone cement brands used in cemented arthroplasties, N,N-dimethyl-4-toluidine (DMPT) serves as the activator of the polymerization reaction. However, many concerns have been raised about this activator, all related to its toxicity. Thus, various workers have assessed a number of alternative activators, with two examples being N,N-dimethylamino-4-benzyl laurate (DMAL) and N,N-dimethylamino-4-benzyl oleate (DMAO). The results of limited characterization of cements that contain DMAL or DMAO have been reported in the literature. The present work is a comprehensive comparison of cements that contain one of these three activators, in which the values of a large array of their properties were determined. These properties range from the setting time and maximum exotherm temperature of the curing cement to the variation of the loss elastic modulus of the cured cement with frequency of the applied indenting force in dynamic nanoindentation tests. The present results, taken in conjunction with those presented in previous reports by the present authors and co-workers on other properties of these cements, indicate that both DMAL and DMPT are suitable alternatives to DMPT.

Acrylic Resins↗
PubMed2007

Dynamic scaling of polymer gels comprising nanoparticles.

We present dynamic light scattering (DLS) measurements of soft poly(methyl-methacrylate) (PMMA) and polyacrylamide (PA) polymer gels prepared with trapped bodies (latex spheres or magnetic nanoparticles). We show that the anomalous diffusivity of the trapped particles can be analyzed in terms of a fractal Gaussian network gel model for the entire time range probed by DLS technique. This model is a generalization of the Rouse model for linear chains extended for structures with power law network connectivity scaling, which includes both percolating and uniform bulk gel limits. For a dilute dispersion of strongly scattering particles trapped in a gel, the scattered electric field correlation function at small wavevector ideally probes self-diffusion of gel portions imprisoning the particles. Our results show that the time-dependent diffusion coefficients calculated from the correlation functions change from a free diffusion regime at short times to an anomalous subdiffusive regime at long times (increasingly arrested displacement). The characteristic time of transition between these regimes depends on scattering vector as approximately q(-2), while the time decay power exponent tends to the value expected for a bulk network at small q. The diffusion curves for all scattering vectors and all samples were scaled to a single master curve.

Acrylic Resins↗