Composites for use in posterior teeth: composition and conversion.

I E Ruyter·H Oysaed
View original source ↗Export metadata ↓

Abstract

The purpose of this investigation was to determine the composition, as well as the conversion after polymerization, of some dental composite materials. Eight posterior composites and two anterior composites were investigated. The weight and volume fractions of inorganic fillers were determined by combustion and pycnometric analyses. The monomers were analyzed qualitatively and quantitatively by high performance liquid chromatography, nuclear magnetic resonance spectroscopy, and gel permeation chromatography. Infrared multiple internal reflection spectroscopy was applied for determination of conversion of the methacrylate groups. The conversion in light activated materials was examined at shallow depths, that is, the level of optimal conversion. This investigation demonstrated that the conversion can be correlated with the composition of monomers and oligomers used in the materials.

Explore related subjects

Acrylic ResinsChemical PhenomenaChemistryChromatography, GelChromatography, High Pressure LiquidComposite ResinsDental MaterialsDental Restoration, PermanentHumansMolecular WeightJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

I E Ruyter, H Oysaed. 1987. Composites for use in posterior teeth: composition and conversion.. https://doi.org/10.1002/jbm.820210107

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Influence of the activator in an acrylic bone cement on an array of cement properties.

In all but one of the acrylic bone cement brands used in cemented arthroplasties, N,N-dimethyl-4-toluidine (DMPT) serves as the activator of the polymerization reaction. However, many concerns have been raised about this activator, all related to its toxicity. Thus, various workers have assessed a number of alternative activators, with two examples being N,N-dimethylamino-4-benzyl laurate (DMAL) and N,N-dimethylamino-4-benzyl oleate (DMAO). The results of limited characterization of cements that contain DMAL or DMAO have been reported in the literature. The present work is a comprehensive comparison of cements that contain one of these three activators, in which the values of a large array of their properties were determined. These properties range from the setting time and maximum exotherm temperature of the curing cement to the variation of the loss elastic modulus of the cured cement with frequency of the applied indenting force in dynamic nanoindentation tests. The present results, taken in conjunction with those presented in previous reports by the present authors and co-workers on other properties of these cements, indicate that both DMAL and DMPT are suitable alternatives to DMPT.

Acrylic Resins↗
PubMed2007

Dynamic scaling of polymer gels comprising nanoparticles.

We present dynamic light scattering (DLS) measurements of soft poly(methyl-methacrylate) (PMMA) and polyacrylamide (PA) polymer gels prepared with trapped bodies (latex spheres or magnetic nanoparticles). We show that the anomalous diffusivity of the trapped particles can be analyzed in terms of a fractal Gaussian network gel model for the entire time range probed by DLS technique. This model is a generalization of the Rouse model for linear chains extended for structures with power law network connectivity scaling, which includes both percolating and uniform bulk gel limits. For a dilute dispersion of strongly scattering particles trapped in a gel, the scattered electric field correlation function at small wavevector ideally probes self-diffusion of gel portions imprisoning the particles. Our results show that the time-dependent diffusion coefficients calculated from the correlation functions change from a free diffusion regime at short times to an anomalous subdiffusive regime at long times (increasingly arrested displacement). The characteristic time of transition between these regimes depends on scattering vector as approximately q(-2), while the time decay power exponent tends to the value expected for a bulk network at small q. The diffusion curves for all scattering vectors and all samples were scaled to a single master curve.

Acrylic Resins↗