Study on the dissolution behaviour of calcium fluoride.

C Bruun·D Moe·H E Madsen
View original source ↗Export metadata ↓

Abstract

The dissolution of two analytical calcium fluoride preparations was studied in aqueous solution. Dissolved calcium fluoride was determined from analysis of Ca and F in solution. Original samples of the two preparations and the residue after partial dissolution were studied by X-ray diffractometry in comparison with natural fluorite. The dissolution of calcium fluoride was found to be extremely slow. After a period of 1-15 weeks, depending on the experimental conditions, a state was reached where apparently no further dissolution occurred, although the solution was far from saturation. The dissolution rate was obviously closely related to the crystal size. On partial dissolution the mean crystal size increased, probably due to the disappearance of the finest fractions. Placing the salt in a dialysis bag before immersion in the water lowered the dissolution rate and increased the undissolved fraction considerably. The results seem to support the assertion that calcium fluoride accumulated in early carious lesions after topical applications of fluoride may persist for considerable periods of time.

Explore related subjects

Calcium FluorideChemical PhenomenaChemistry, PhysicalHumansSolubilitySolutionsTime FactorsWaterX-Ray DiffractionJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

C Bruun, D Moe, H E Madsen. 1983. Study on the dissolution behaviour of calcium fluoride.. https://doi.org/10.1111/j.1600-0722.1983.tb00811.x

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2006

Three-dimensional visualization of the inner structure of single crystals by step-scanning white X-ray section topography.

Visualization of the three-dimensional distribution of the crystal defects of large single crystals of calcium fluoride has been demonstrated by white X-ray section topography using sheet-like X-rays (BL28B2 at SPring-8). An image of the three-dimensional distribution of the crystal defects was reconstructed by stacking section topographs, which expressed the images of cross sections of the sample. The section topographs were recorded using a CMOS flat-panel imager or a CCD detector combined with scintillator (Gd(2)O(2)S:Tb) and relay lens system. The section topographs were measured by repeating cycles of exposure and sample translation along the direction perpendicular to the top face of the sample. Using high-brilliance and high-energy white X-rays ( approximately 60 keV) efficiently, visualization of the three-dimensional structure of subgrains of a sample of up to 60 mm in diameter was achieved. Furthermore, the three-dimensional distribution of the glide plane in the crystal was visualized by reconstructing the linear contrast of the glide plane.

Calcium Fluoride↗
PubMed2006

Study on the influence of additives in an industrial calcium fluoride and waterworks sludge co-melting system.

This work explores the effect of additives on the pouring temperature in a waterworks and industrial calcium fluoride sludge co-melting system. Two kinds of sludge were mixed in various ratios to find a mixing ratio at which the operating temperature for subsequent additive tests was relatively low. Various proportions of either sodium carbonate (Na2CO3) or potassium carbonate (K2CO3) reagent were added to the mixed-sludge samples to elucidate the consequent changes in pouring temperature. The experimental results revealed that the pouring temperature was lowest when calcium fluoride was mixed with waterworks sludge in a ratio of 4:6 (w/w). Adding sodium carbonate or potassium carbonate reagent to the mixed-sludge samples further reduced the pouring temperature. Increasing the amount of sodium carbonate did not significantly reduce the pouring temperature beyond that observed when 2% was added, suggesting that 2% was the optimal additional percentage of sodium carbonate. In contrast, the pouring temperature was increased when over 2% potassium carbonate was added to the mixed-sludge samples, revealing that the optimal additional percentage of potassium carbonate was also 2%. These findings indicate that both sodium carbonate and potassium carbonate can be used as additives to increase the energy efficiency of the melting process, but sodium carbonate is more operationally convenient.

Calcium Fluoride↗
PubMed2006

Intercomparison of dosimetry systems based on CaF2:Mn TL detectors.

The responses of readings by the TL dosimetry system MR200 TL developed in-house and used at JSI and the TOLEDO TL system used at RBI are compared. Ten measurements at different doses ranging from 0.01 mSv to 5 Sv were carried out. A set of 36 dosemeters with three pellets of CaF2:Mn were irradiated in radiation fields of 137Cs and 60Co. Analysis of the measured results shows that at doses below 0.1 Sv, readers' outputs do not differ >5% from each other. At doses >1 Sv, the results obtained by the MR200 reader must be corrected with a known factor. Finally, the reproducibility of the results from the MR200 was tested.

Calcium Fluoride↗