Calcifiability comparison among selected microorganisms.

J Ennever·J L Streckfuss·M C Goldschmidt
View original source ↗Export metadata ↓

Abstract

Seven ATCC strains of bacteria were examined for apatite formation in a chemically-defined calcification-supporting medium and also in a metastable calcium phosphate solution. One, E. coli, calcified in both. One, S. aureus, calcified in the solution, but not in the medium. The other five did not calcify in either. The results substantiate the belief that calcification is restricted to certain microorganisms. However, they do not rule out the possibility that a noncalcifiable microorganism has the potential to calcify, and the activity is prevented by a cell component. Additionally, the findings emphasize that determining microbiologic calcifiability only in a calcification-supporting culture medium is inadequate. In culture, an efficient calcium pump might preclude calcification by establishing a cytoplasmic calcium level too low for nucleation activation. Calcifiability assays should be done by incubating minimally-metabolizing freeze-dried cells in metastable calcium phosphate solution.

Explore related subjects

ApatitesBacteriaCalcification, PhysiologicCalcium PhosphatesEscherichia coliStaphylococcus aureusComparative StudyJournal ArticleResearch Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

J Ennever, J L Streckfuss, M C Goldschmidt. 1981. Calcifiability comparison among selected microorganisms.. https://doi.org/10.1177/00220345810600101001

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed1999

Relationships among carbonated apatite solubility, crystallite size, and microstrain parameters.

The use of the metastable equilibrium solubility (MES) concept to describe the solubility properties of carbonated apatites (CAPs) and human dental enamel (HE) has been well established in previous studies using a range of CAPs with varying carbonate contents and crystallinities. It was shown in these studies that the mean value of the CAP MES is directly related to the broadening parameter full width at half maximum (FWHM) of the 002 reflection of the X-ray diffraction profile. The apparent solubility of the CAPs increased monotonically with an increase in the broadening of the diffraction peaks, and when this peak broadening was taken into account, carbonate had no additional effect upon the MES. The broadening of the diffraction peaks has been used as an indicator of crystallinity, and is generally influenced by both crystallite size and microstrain. The purpose of the present study was to extract the crystallite size and microstrain parameters separately from the X-ray diffraction peaks and then to determine their relationships to the corresponding MES values. The samples studied were CAPs synthesized by precipitation from Ca(NO3)2 and NaH2PO4 solutions in carbonate containing media at temperatures of 95, 80, and 70 degrees C, and powdered HE. The crystallite size and microstrain parameters were determined simultaneously with the refinement of the structural parameters with the Rietveld method of whole-pattern-fitting structure-refinement. A modified pseudo-Voigt function was used to model the observed peak profiles. The MES distributions for the CAPs and HE were determined by a previously described method. The results of this study showed that the CAPs possessed an MES distribution and therefore provided further support that MES distribution is a common phenomenon, regardless of the method of CAP synthesis. The crystallite size decreased and the microstrain increased with increasing carbonate content and decreasing temperature of synthesis of the CAPs. A plot of the mean of the MES distribution versus the microstrain parameter showed that the apparent solubility of the CAPs and HE correlated very well with the microstrain parameter. On the other hand, a plot of the mean of the MES distribution versus the crystallite size parameter showed a poor correlation between MES and crystallite size. These findings support a view that microstrain, rather than crystallite size, is the dominant factor governing the effective solubility of the CAPs and dental enamel.

Apatites↗
PubMed1999

Sol-gel modification of silicone to induce apatite-forming ability.

Silicones formed with silanol groups on their surfaces were prepared by partial hydrolysis and polycondensation of tetraethoxysilane (TEOS) dispersed in silicones in molecular scale. Although the silanol-modified silicones thus prepared formed no apatite in a simulated body fluid (SBF) with ion concentrations nearly equal to those of human blood plasma within 21 d, they formed a bone-like apatite layer in situ on their surfaces in a solution (1.5 SBF) with ion concentrations 1.5 times the SBF within 7 d. This indicates that the silanol groups formed on the silicones by the present method can induce the apatite nucleation in 1.5 SBF and hence, apatite-coated silicones can be fabricated by a biomimetic process. Apatite-silicone composites thus prepared could exhibit mechanical properties analogous to the natural bone as well as bioactivity.

Apatites↗
PubMed1999

Enamel erosion by some soft drinks and orange juices relative to their pH, buffering effect and contents of calcium phosphate.

The capability of a soft drink or a juice to erode dental enamel depends not only on the pH of the drink, but also on its buffering effect. As the latter is the ability of the drink to resist a change of pH it may add to the effects of the actual pH. The aim of the present study was to compare the pH and the buffering effect of various soft drinks with their erosive effects and the solubility of apatite. In 18 soft drinks, mineral waters and juices available on the Danish market, pH and the concentrations of calcium, phosphate and fluoride were determined. The buffering effect was determined by titration with NaOH. Human teeth (n = 54) covered with nail varnish except for 3x4-mm windows were exposed to 1.5 liters of the drink for either 7 days or 24 h under constant agitation. The depth of the erosions was assessed in longitudinal sections. The depth was found to vary greatly from 3 mm eroded by the most acidic drinks and fresh orange juice to only slightly affected surfaces by most of the mineral waters. The dissolution of enamel increased logarithmically inversely with the pH of the drink and parallel with the solubility of enamel apatite. Orange juice, pH 4.0, supplemented with 40 mmol/l calcium and 30 mmol/l phosphate did not erode the enamel as the calcium and phosphate saturated the drink with respect to apatite. Generally, the lower the pH the more NaOH was necessary to bring the pH to neutrality. In particular the buffering effect of the juice was high. For all drinks, no effect of their low fluoride concentrations was observed.

Apatites↗