Processing dentures using a microwave technique.

S G Ilbay·S Güvener·H N Alkumru
View original source ↗Export metadata ↓

Abstract

In this research the technique of curing denture base acrylic resins by microwave energy was investigated with respect to polymerization method, hardness, mechanical and physical properties. Twenty-one different polymerization methods were used by varying radiation power and curing time. The Vickers hardness test was applied to the samples which were polymerized. The average value was found to be 22.46 VHN (Vicker hardness number), that is, almost the same as conventionally cured acrylic. The recommended polymerization method of curing acrylic was 3 min at 550 W in a microwave oven. Mechanical and physical tests were applied to the samples which were cured by the recommended polymerization method. The average transverse load to fracture value was found to be 7.6 kg, and the transverse deflection value was 1.5 mm at 3500 g, and 2.9 mm at 5000 g. Water sorption of acrylic resin cured by microwave energy was 0.72 mg cm-2 and the solubility rate in water was 0.038 mg cm-2. Results conformed with the ADA specification. The findings showed that acrylic resin cured by microwave energy is more resistant to mechanical failure than conventionally cured acrylic and this technique can safely be applied to the production of denture bases.

Explore related subjects

Acrylic ResinsChemical PhenomenaChemistry, PhysicalDenture BasesHardnessHardness TestsMaterials TestingMicrowavesSolubilityJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

S G Ilbay, S Güvener, H N Alkumru. 1994. Processing dentures using a microwave technique.. https://doi.org/10.1111/j.1365-2842.1994.tb01129.x

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Influence of the activator in an acrylic bone cement on an array of cement properties.

In all but one of the acrylic bone cement brands used in cemented arthroplasties, N,N-dimethyl-4-toluidine (DMPT) serves as the activator of the polymerization reaction. However, many concerns have been raised about this activator, all related to its toxicity. Thus, various workers have assessed a number of alternative activators, with two examples being N,N-dimethylamino-4-benzyl laurate (DMAL) and N,N-dimethylamino-4-benzyl oleate (DMAO). The results of limited characterization of cements that contain DMAL or DMAO have been reported in the literature. The present work is a comprehensive comparison of cements that contain one of these three activators, in which the values of a large array of their properties were determined. These properties range from the setting time and maximum exotherm temperature of the curing cement to the variation of the loss elastic modulus of the cured cement with frequency of the applied indenting force in dynamic nanoindentation tests. The present results, taken in conjunction with those presented in previous reports by the present authors and co-workers on other properties of these cements, indicate that both DMAL and DMPT are suitable alternatives to DMPT.

Acrylic Resins↗
PubMed2007

Dynamic scaling of polymer gels comprising nanoparticles.

We present dynamic light scattering (DLS) measurements of soft poly(methyl-methacrylate) (PMMA) and polyacrylamide (PA) polymer gels prepared with trapped bodies (latex spheres or magnetic nanoparticles). We show that the anomalous diffusivity of the trapped particles can be analyzed in terms of a fractal Gaussian network gel model for the entire time range probed by DLS technique. This model is a generalization of the Rouse model for linear chains extended for structures with power law network connectivity scaling, which includes both percolating and uniform bulk gel limits. For a dilute dispersion of strongly scattering particles trapped in a gel, the scattered electric field correlation function at small wavevector ideally probes self-diffusion of gel portions imprisoning the particles. Our results show that the time-dependent diffusion coefficients calculated from the correlation functions change from a free diffusion regime at short times to an anomalous subdiffusive regime at long times (increasingly arrested displacement). The characteristic time of transition between these regimes depends on scattering vector as approximately q(-2), while the time decay power exponent tends to the value expected for a bulk network at small q. The diffusion curves for all scattering vectors and all samples were scaled to a single master curve.

Acrylic Resins↗