Method for jet polishing two-phase materials.

Abstract

A two-stage jet polishing technique is described which, utilising the effects of the characteristic current-voltage behaviour of electropolishing solutions, can produce excellent TEM foils of relatively coarse two-phase materials.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

M J Witcomb, U Dahmen. 1995-09-01. Method for jet polishing two-phase materials.. https://doi.org/10.1002/jemt.1070320107

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

Effects of solution pH and electrical parameters on hydroxyapatite coatings deposited by a plasma-assisted electrophoresis technique.

Hydroxyapatite (HA) coatings can be deposited using a hybrid process of plasma electrolysis and electrophoresis, called plasma-assisted electrophoretic deposition (PEPD). HA aqueous suspensions with various pH values were prepared using a modified ultrasonic cleaning bath as an agitator/stirrer. Both DC and unbalanced AC power supplies were used to bias the titanium alloy substrate materials employed in this work. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffractometry (XRD), and Fourier transform infrared spectroscopy (FTIR) were used to observe and analyze coating morphology and microstructure. It was shown that the morphology and composition of the calcium phosphate coatings were significantly influenced by solution pH values; the level of "pure" HA in the coatings' composition corresponded to both solution pH and the type of power supply employed. Loss of hydroxyl radials (i.e., dehydroxylation), which degrades the performance of the hydroxyapatite coating in terms of long-term chemical and mechanical stability, can be virtually eliminated by a combination of high pH and unbalanced AC plasma power. In addition, the underlying TiO2 coatings used to support the HA layer (preproduced by plasma electrolysis process) have a nanoscaled (10-20 nm) polycrystalline structure. TEM studies also revealed a dense, continuous amorphous titania layer (10 nm in thickness) at the interface between the Ti alloy substrate and the TiO2 layer, which may play a role in improving the corrosion resistance of the substrate. Such a nanophase TiO2 layer (if used as a coating alone) may also provide a further improvement in osteoinductive properties, compared to a conventional TiO2 coating on the Ti alloy substrate.

Alloys↗

Biomimetic coprecipitation of calcium phosphate and bovine serum albumin on titanium alloy.

Titanium alloy implants were precoated biomimetically with a thin and dense layer of calcium phosphate and then incubated either in a supersaturated solution of calcium phosphate or in phosphate-buffered saline, each containing bovine serum albumin (BSA) at various concentrations, under physiological conditions for 48 h. Coated implants then underwent scanning electron microscopy, immunohistochemical evaluation, Fourier transform infrared spectroscopy, and X-ray diffraction. The quantity of BSA taken up by coatings and the kinetics of protein release were monitored colorimetrically. In coatings prepared by the coprecipitation of calcium phosphate and BSA, protein had become incorporated into the mineral crystal latticework. With increasing BSA concentration, matrices decreased in thickness, became more dense, showed lower crystallinity, and underwent a change in crystal geometry. The octacalcium phosphate structure manifested in the absence of protein was gradually transformed into a carbonated apatite form. Preformed mineral coatings became only superficially mantled with a layer of BSA, and the morphology of the mineral matrices themselves remained unchanged. At equivalent protein concentrations, coatings prepared by the coprecipitation of calcium phosphate released only a minute fraction of its protein component under physiological conditions, whereas preformed mineral matrices showed a "burst" release of their associated protein within a single 2-h period. The biomimetic coating can be a carrier for osteoinductive agents.

Alloys↗

Sequential magnetic resonance monitoring of pulmonary flow with endovascular stents placed across the pulmonary valve in growing Swine.

BACKGROUND: Patients with endovascular stent implantation for the treatment of right ventricular outflow tract obstruction are often left with incomplete relief of the obstruction and significant pulmonary regurgitation. A noninvasive and reproducible method for monitoring such patients is desirable. MRI in the presence of a stent, however, has to overcome the problem of potential metallic artifacts. METHODS AND RESULTS: Under x-ray fluoroscopic guidance, endovascular nitinol stents were placed across the pulmonary valve in 6 young pigs to induce pulmonary regurgitation. Five additional pigs served as controls. Initial MRI was performed after 2 days (13.5+/-1.8 kg) and follow-up after 3 months (32+/-2.9 kg). Pulmonary flow volumes and regurgitant fraction were quantified by velocity-encoded cine (VEC) MRI through (VEC-TS) and distal to (VEC-DS) the stent. VEC-TS was compared with VEC-DS and volumetric measurements of left and right ventricular stroke volumes provided by cine MRI ("gold standard"). Antegrade and retrograde pulmonary flow volumes by VEC-TS were slightly but significantly less than those with VEC-DS and cine MRI. Excellent correlations (r>0.97) for phasic pulmonary flow volumes as measured by VEC-TS and VEC-DS were shown. Pulmonary regurgitant fraction increased from 32.8+/-15% to 49.6+/-17% (P<0.05) over the course of 3 months with VEC-TS. CONCLUSIONS: MRI demonstrates the progression of pulmonary regurgitation in growing swine. VEC MRI has the ability to quantify pulmonary blood flow inside the lumen of nitinol stents. MRI appears to be ideally suited for monitoring patients with endovascular nitinol stents in the pulmonary artery or pulmonary valve position.

Alloys↗