Direct bonding to typodont teeth.

M J Titshall·M M McKnight·N P Hunt
View original source ↗Export metadata ↓

Abstract

Three methods of bonding orthodontic brackets to acrylic teeth were investigated for use with a typodont. One-hundred-and-twenty Dentaurum 0.018 x 0.025 inch standard Edgewise brackets were bonded to Crylopax cross-linked acrylic teeth using three cements: Concise composite, Concise with acrylic primer, and GAC acrylic cement on a previously roughened tooth surface. Half the specimens in each group was immersed in a thermostatically controlled water bath for 15 min on 20 occasions over a 5-day period, to simulate the conditions of a typodont, prior to measuring tensile bond strength on an Instron machine. Under dry conditions Concise composite was significantly stronger than either Concise with acrylic primer or GAC cold cure acrylic resin. Under wet conditions, however, the mean bond strength of the acrylic resin increased significantly compared to the other cements. The bond strength of both Concise and Concise composite with primer deteriorated following water immersion. It is suggested that when setting up typodont teeth with brackets bonded with GAC acrylic resin, immersion of the bonded teeth in hot water prior to positioning of the teeth in the typodont may greatly reduce the risk of subsequent bracket loss.

Explore related subjects

Acrylic ResinsBisphenol A-Glycidyl MethacrylateDental BondingDental CementsHumansImmersionMaterials TestingOrthodontic BracketsOrthodonticsStatistics, NonparametricTeaching MaterialsTensile StrengthTooth, ArtificialWaterComparative StudyJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

M J Titshall, M M McKnight, N P Hunt. 1996. Direct bonding to typodont teeth.. https://doi.org/10.1179/bjo.23.1.65

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Influence of the activator in an acrylic bone cement on an array of cement properties.

In all but one of the acrylic bone cement brands used in cemented arthroplasties, N,N-dimethyl-4-toluidine (DMPT) serves as the activator of the polymerization reaction. However, many concerns have been raised about this activator, all related to its toxicity. Thus, various workers have assessed a number of alternative activators, with two examples being N,N-dimethylamino-4-benzyl laurate (DMAL) and N,N-dimethylamino-4-benzyl oleate (DMAO). The results of limited characterization of cements that contain DMAL or DMAO have been reported in the literature. The present work is a comprehensive comparison of cements that contain one of these three activators, in which the values of a large array of their properties were determined. These properties range from the setting time and maximum exotherm temperature of the curing cement to the variation of the loss elastic modulus of the cured cement with frequency of the applied indenting force in dynamic nanoindentation tests. The present results, taken in conjunction with those presented in previous reports by the present authors and co-workers on other properties of these cements, indicate that both DMAL and DMPT are suitable alternatives to DMPT.

Acrylic Resins↗
PubMed2007

Dynamic scaling of polymer gels comprising nanoparticles.

We present dynamic light scattering (DLS) measurements of soft poly(methyl-methacrylate) (PMMA) and polyacrylamide (PA) polymer gels prepared with trapped bodies (latex spheres or magnetic nanoparticles). We show that the anomalous diffusivity of the trapped particles can be analyzed in terms of a fractal Gaussian network gel model for the entire time range probed by DLS technique. This model is a generalization of the Rouse model for linear chains extended for structures with power law network connectivity scaling, which includes both percolating and uniform bulk gel limits. For a dilute dispersion of strongly scattering particles trapped in a gel, the scattered electric field correlation function at small wavevector ideally probes self-diffusion of gel portions imprisoning the particles. Our results show that the time-dependent diffusion coefficients calculated from the correlation functions change from a free diffusion regime at short times to an anomalous subdiffusive regime at long times (increasingly arrested displacement). The characteristic time of transition between these regimes depends on scattering vector as approximately q(-2), while the time decay power exponent tends to the value expected for a bulk network at small q. The diffusion curves for all scattering vectors and all samples were scaled to a single master curve.

Acrylic Resins↗