PubMed · 9659600

Elastomers for biomedical applications.

R Yoda
View original source ↗Export metadata ↓

Abstract

Current topics in elastomers for biomedical applications are reviewed. Elastomeric biomaterials, such as silicones, thermoplastic elastomers, polyolefin and polydiene elastomers, poly(vinyl chloride), natural rubber, heparinized polymers, hydrogels, polypeptides elastomers and others are described. In addition biomedical applications, such as cardiovascular devices, prosthetic devices, general medical care products, transdermal therapeutic systems, orthodontics, and ophthalmology are reviewed as well. Elastomers will find increasing use in medical products, offering biocompatibility, durability, design flexibility, and favorable performance/cost ratios. Elastomers will play a key role in medical technology of the future.

Explore related subjects

Biocompatible MaterialsBiomechanical PhenomenaBlood Vessel ProsthesisEquipment and SuppliesHeart-Assist DevicesHumansOrthotic DevicesProstheses and ImplantsRubberSterilizationSurgical InstrumentsJournal ArticleReview

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

R Yoda. 1998. Elastomers for biomedical applications.. https://doi.org/10.1163/156856298x00046

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2002

Biodegradable polyurethanes for implants. II. In vitro degradation and calcification of materials from poly(epsilon-caprolactone)-poly(ethylene oxide) diols and various chain extenders.

Linear, biodegradable, aliphatic polyurethanes with various degrees of hydrophilicity were synthesized in bulk at 50-100 degrees C. The ratios between the hydrophilic and hydrophobic segments were 0:100, 30:70, 40:60, 50:50, and 70:30, respectively. The hydrophilic segment consisted of poly(ethylene oxide) (PEO) diol (molecular weight = 600 or 2000) or the poly(ethylene-propylene-ethylene oxide) (PEO-PPO-PEO) diol Pluronic F-68 (molecular weight = 8000). The hydrophobic segment was made of poly(epsilon-caprolactone) diol (molecular weight = 530, 1250, or 2000). The chain extenders were 1,4-butane diol and 2-amino-1-butanol. The diisocyanate was aliphatic hexamethylene diisocyanate. The polymers absorbed water in an amount that increased with the increasing content of the PEO segment in the polymer chain. The total amount of absorbed water did not exceed 2% for the poly(ester urethane)s and was as high as 212% for some poly(ester ether urethane)s that behaved in water like hydrogels. The polymers were subjected to in vitro degradation at 37 +/- 0.1 degrees C in phosphate buffer solutions for up to 76 weeks. The poly(ester urethane)s showed 1-2% mass loss at 48 weeks and 1.1-3.8% mass loss at 76 weeks. The poly(ester ether urethane)s manifested 1.6-76% mass loss at 48 weeks and 1.6-96% mass loss at 76 weeks. The increasing content and molecular weight of the PEO segment enhanced the rate of mass loss. Similar relations were also observed for polyurethanes from PEO-PPO-PEO (Pluronic) diols. Materials obtained with 2-amino-1-butanol as the chain extender degraded at a slower rate than similar materials synthesized with 1,4-butane diol. All the materials already manifested a progressive decrease in the molecular weight in the first month of in vitro aging. The rate of molecular weight loss was higher for poly(ester ether urethane)s than for poly(ester urethane)s. For poly(ester ether urethane)s, the rate of molecular weight loss was higher for materials containing Pluronic than for those containing PEO segments. All polymers calcified in vitro. The susceptibility to calcification increased with material hydrophilicity. The progressive deposition of calcium salt on the film surfaces resulted in the formation of large crystal aggregates, the structure of which depended on the chemical composition of the calcified material. Needle-like aggregates, resembling brushite, formed on the hydrophobic polyurethane, and plate-like crystals formed on the highly hydrophilic material. The calcium-to-phosphorus atomic ratio of the crystals growing on the samples was dependent on the chemical composition of the material and varied from 0.94 to 1.55.

Biocompatible Materials↗
PubMed2002

Effect of grooved titanium substratum on human osteoblastic cell growth.

Various surface treatments have been developed to increase the clinical performance of titanium-based implants. Many in vitro tests have been carried out on substrates with varied surface topography for a complete understanding of osteoblasts. In previous research, we made the observation that surface roughness must be taken into account, not only in terms of amplitude but also in terms of organization. In this study, we tested the adhesion and proliferation of human primary osteoblasts on grooved titanium surfaces with various amplitudes and organizations of topography. The roughness was described at a scale above (macro-roughness) or below (micro-roughness) the cell size. We observed better orientation and proliferation of human osteoblasts on surfaces with a micro-roughness characterized by a lower Order (parameter describing the organization of topography) and by a higher Ra and Rz (parameters describing the amplitude of topography). It appears that cultured human osteoblasts prefer surfaces with relatively high micro-roughness amplitude and with a low level of repeatability.

Biocompatible Materials↗
PubMed2002

The porosity dependence of the dielectric constant for sintered hydroxyapatite.

Hydroxyapatite (HAp) is the major mineral constituent of bone, and as such, the dielectric properties of HAp are of interest because electromagnetic fields have been shown to accelerate healing in bone fractures. In addition, an interest in the dielectric properties of HAp stems from the suggestion that electrically insulating HAp coatings might be used on implantable devices. In this study, the dielectric constant of polycrystalline hexagonal HAp was measured at nine different frequencies, from 45 kHz to 7.3 MHz for relative porosities ranging from 0.05 to 0.42. At a fixed frequency, the decrease in k as a function of increasing porosity is described well by an exponential function of porosity such that k = k(0)exp(-bP), where k(0) is the dielectric constant at zero porosity and b is a constant. In addition, the entire data set of 108 data points (representing the 12 specimens of differing porosity measured at each of the nine frequencies) was fit to a candidate function formed from the product k(0)exp(-bP) and a simple expression relating frequency to the dielectric constant. The candidate function fit the data relatively well, with a coefficient of determination of 0.91.

Biocompatible Materials↗