NaOH treatment of vacuum-plasma-sprayed titanium on carbon fibre-reinforced poly(etheretherketone).

Carbon fibre-reinforced polyetheretherketone (CF-PEEK) substrates were coated with titanium by vacuum-plasma-spraying and chemically treated in 10 M sodium hydroxide (NaOH) solution. After NaOH treatment, the specimens were immersed in simulated body fluid (SBF) containing ions in concentrations similar to those of human blood plasma. Scanning electron microscopy, energy-dispersive X-ray analysis and diffuse reflectance Fourier transformed-infrared spectroscopy were used to analyse the NaOH-treated VPS-Ti surface and the calcium phosphate layer formed during immersion in SBF. It was observed that a carbonate-containing calcium phosphate layer was formed on the NaOH-treated VPS-Ti surface during immersion in SBF, whereas no calcium phosphate precipitation occurred on the untreated surfaces. It is therefore concluded that vacuum-plasma-spraying with titanium and subsequent chemical modification in 10 M NaOH solution at 60 degrees C for 2 h is a suitable method for the preparation of bioactive coatings for bone ongrowth on CF-PEEK.

Journal Article↗
PubMed1997

Topographical characterization and microstructural interface analysis of vacuum-plasma-sprayed titanium and hydroxyapatite coatings on carbon fibre-reinforced poly(etheretherketone).

In the present study, topographical characterization and microstructural interface analysis of vacuum-plasma-sprayed titanium and hydroxyapatite (HA) coatings on carbon fibre-reinforced polyetheretherketone (CF/PEEK) was performed. VPS-Ti coatings with high roughness values (Ra=28.29+/-3.07 microm, Rz=145.35+/-9.88 microm) were obtained. On this titanium, intermediate layer HA coatings of various thicknesses were produced. With increasing coating thickness, roughness values of the HA coatings decreased. A high increase of profile length ratio, Lr, of the VPS-Ti coatings (Lr=1.45) compared to the grit-blasted CF/PEEK substrate (Lr=1.08) was observed. Increasing the HA coating thickness resulted in a reduction of the Lr values similar to the roughness values. Fractal analysis of the obtained roughness profiles revealed that the VPS-Ti coatings showed the highest fractal dimension of D=1.34+/-0.02. Fractal dimension dropped to a value of 1.23-1.25 for all HA coatings. No physical deterioration of the CF/PEEK substrate was observed, indicating that substrate drying and the used VPS process parameter led to the desired coatings on the composite material. Cross-section analysis revealed a good interlocking between the titanium intermediate layer and the PEEK substrate. It is therefore assumed that this interlocking results in suitable mechanical adhesive strength. From the results obtained in this study it is concluded that VPS is a suitable method for manufacturing HA coatings on carbon fibre-reinforced PEEK implant materials.

Journal Article↗