Topographical characterization and microstructural interface analysis of vacuum-plasma-sprayed titanium and hydroxyapatite coatings on carbon fibre-reinforced poly(etheretherketone).

S W Ha·A Gisep·J Mayer·E Wintermantel·H Gruner·M Wieland
View original source ↗Export metadata ↓

Abstract

In the present study, topographical characterization and microstructural interface analysis of vacuum-plasma-sprayed titanium and hydroxyapatite (HA) coatings on carbon fibre-reinforced polyetheretherketone (CF/PEEK) was performed. VPS-Ti coatings with high roughness values (Ra=28.29+/-3.07 microm, Rz=145.35+/-9.88 microm) were obtained. On this titanium, intermediate layer HA coatings of various thicknesses were produced. With increasing coating thickness, roughness values of the HA coatings decreased. A high increase of profile length ratio, Lr, of the VPS-Ti coatings (Lr=1.45) compared to the grit-blasted CF/PEEK substrate (Lr=1.08) was observed. Increasing the HA coating thickness resulted in a reduction of the Lr values similar to the roughness values. Fractal analysis of the obtained roughness profiles revealed that the VPS-Ti coatings showed the highest fractal dimension of D=1.34+/-0.02. Fractal dimension dropped to a value of 1.23-1.25 for all HA coatings. No physical deterioration of the CF/PEEK substrate was observed, indicating that substrate drying and the used VPS process parameter led to the desired coatings on the composite material. Cross-section analysis revealed a good interlocking between the titanium intermediate layer and the PEEK substrate. It is therefore assumed that this interlocking results in suitable mechanical adhesive strength. From the results obtained in this study it is concluded that VPS is a suitable method for manufacturing HA coatings on carbon fibre-reinforced PEEK implant materials.

Explore related subjects

Journal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

S W Ha, A Gisep, J Mayer, E Wintermantel, H Gruner, M Wieland. 1997. Topographical characterization and microstructural interface analysis of vacuum-plasma-sprayed titanium and hydroxyapatite coatings on carbon fibre-reinforced poly(etheretherketone).. https://doi.org/10.1023/a%3A1018562023599

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2027

Effectiveness of high-dose versus standard-dose influenza vaccines against hospitalisation according to frailty risk: a prespecified analysis of the randomised trial DANFLU-2.

BACKGROUND: Frailty is a major risk factor for influenza-related complications and can influence vaccine effectiveness. We aimed to assess the relative vaccine effectiveness (rVE) of high-dose (HD-IIV) versus standard-dose inactivated influenza vaccine (SD-IIV) in older adults aged 65 years or older according to frailty risk. METHODS: This study was a prespecified analysis of DANFLU-2, an open-label, individually randomised trial, conducted in Denmark during three consecutive influenza seasons (2022-23, 2023-24, and 2024-25). Adults aged 65 years or older were randomised (1:1) to the HD-IIV or SD-IIV group. The primary endpoint was hospitalisation for influenza or pneumonia. Frailty was defined according to the validated Hospital Frailty Risk Score (HFRS) based on ICD-10 codes within 10 years before randomisation. Participants were stratified into three HFRS categories, namely low (<5 points), intermediate (5-15 points), and high (>15 points) frailty risk. The rVE of HD-IIV versus SD-IIV against the primary endpoint was assessed across prespecified HFRS categories and treating HFRS as a continuous variable. Pearson's chi-square test was used to compare safety events across frailty risk groups and randomisation groups. FINDINGS: Among 332&#x2009;438 randomised participants (mean age 73&#xb7;7 years [SD 5&#xb7;8]; 161&#x2009;538 [48&#xb7;6%] were female), 276&#x2009;173 (83&#xb7;1%) had low frailty risk, 52&#x2009;395 (15&#xb7;8%) had intermediate frailty risk, and 3861 (1&#xb7;2%) had high frailty risk. The primary endpoint of hospitalisation for influenza or pneumonia occurred in 1424 (0&#xb7;5%) of 276&#x2009;173 participants with low frailty risk, 761 (1&#xb7;5%) of 52&#x2009;395 with intermediate frailty risk, and 163 (4&#xb7;2%) of 3861 with high frailty risk (relative risk [RR] for intermediate vs low frailty risk 2&#xb7;8 [95% CI 2&#xb7;6-3&#xb7;1]; RR for high vs low frailty risk 8&#xb7;2 [7&#xb7;0-9&#xb7;6]). HFRS as a continuous variable significantly modified the effect of HD-IIV versus SD-IIV against the primary endpoint with higher rVE estimates with increasing HFRS (pinteraction=0&#xb7;020). The rVE was 0&#xb7;2% (95% CI -10&#xb7;8 to 10&#xb7;2) among those with low frailty risk, 13&#xb7;1% (-0&#xb7;4 to 24&#xb7;8) among those with intermediate frailty risk, and 19&#xb7;9% (-10&#xb7;3 to 42&#xb7;1) among those with high frailty risk. No significant interaction was observed when HFRS was assessed according to the prespecified categorical frailty groups (pinteraction=0&#xb7;17). The proportion of participants with at least one serious adverse event increased across frailty risk groups (13&#x2009;366 [4&#xb7;8%] of 275&#x2009;795 for low frailty risk, 5475 [10&#xb7;5%] of 52&#x2009;315 for intermediate frailty risk, and 777 [20&#xb7;2%] of 3850 for high frailty risk; p<0&#xb7;0001), with similar proportions of serious adverse events in the HD-IIV and SD-IIV groups for each frailty risk group. INTERPRETATION: Among adults aged 65 years or older in Denmark, frailty risk might modify the effects of HD-IIV versus SD-IIV against hospitalisation for influenza or pneumonia, with higher rVE estimates with increasing frailty risk. These findings might support considering high-dose influenza vaccines for frail older adults. However, effect modification was not evident when frailty was assessed using prespecified categorical subgroups, and subgroup-specific estimates were imprecise, with 95% CIs crossing the null. These results should be considered exploratory, warranting further investigation. FUNDING: The DANFLU-2 trial was funded by Sanofi.

Journal Article↗