Recent progress in the determination of solid surface tensions from contact angles.

Advancing contact angles of different liquids measured on the same solid surface fall very close to a smooth curve when plotted as a function of liquid surface tension, i.e., gamma(lv)costheta versus gamma(lv). Changing the solid surface, and hence gamma(sv), shifts the curve in a regular manner. These patterns suggest that gamma(lv)costheta depends only on gamma(lv) and gamma(sv). Thus, an "equation of state for the interfacial tensions" was developed to facilitate the determination of solid surface tensions from contact angles in conjunction with Young's equation. However, a close examination of the smooth curves showed that contact angles typically show a scatter of 1-3 degrees around the curves. The existence of the deviations introduces an element of uncertainty in the determination of solid surface tensions. Establishing that (i) contact angles are exclusively a material property of the coating polymer and do not depend on experimental procedures and that (ii) contact angle measurements with a sophisticated methodology, axisymmetric drop shape analysis (ADSA), are highly reproducible guarantees that the deviations are not experimental errors and must have physical causes. The contact angles of a large number of liquids on the films of four different fluoropolymers were studied to identify the causes of the deviations. Specific molecular interactions at solid-vapor and/or solid-liquid interfaces account for the minor contact angle deviations. Such interactions take place in different ways. Adsorption of vapor of the test liquid onto the solid surface is apparently the only process that influences the solid-vapor interfacial tension (gamma(sv)). The molecular interactions taking place at the solid-liquid interface are more diverse and complicated. Parallel alignment of liquid molecules at the solid surface, reorganization of liquid molecules at the solid-liquid interface, change in the configuration of polymer chains due to contact with certain probe liquids, and intermolecular interactions between solid and liquid molecules cause the solid-liquid interfacial (gamma(sl)) tension to be different from that predicted by the equation of state, i.e., gamma(sl) is not a precise function of gamma(lv) and gamma(sv). In other words, the experimental contact angles deviate from the "ideal" contact angle pattern. Specific criteria are proposed to identify probe liquids which eliminate specific molecular interactions. Octamethylcyclotetrasiloxane (OMCTS) and decamethylcyclopentasiloxane (DMCPS) are shown to meet those criteria, and therefore are the most suitable liquids to characterize surface tensions of low energy fluoropolymer films with an accuracy of +/-0.2 mJ/m2.

Journal Article↗

PubMed2006

Fabrication of superhydrophobic surfaces of n-hexatriacontane.

Superhydrophobic surfaces of n-hexatriacontane were fabricated in a single-step process. The low surface energy of n-hexatriacontane together with the randomly distributed micro- and nanoscale roughness features guarantees very large contact angles and a small roll-off angle for water drops. The advantage of n-hexatriacontane superhydrophobic surfaces is their stability in the sense that they are impervious to chemical reactions and retain their wetting characteristics over a long period of time, as confirmed by XPS analysis and contact angle measurements.

Coated Materials, Biocompatible↗

PubMed2005

Interpretation of contact angle measurements on two different fluoropolymers for the determination of solid surface tension.

Contact angle measurements with a large number of liquids on the semi-fluorinated acryl polymer EGC-1700 films are reported. The surface tension was determined to be gammasv=13.84 mJ/m2 from contact angles of octamethylcyclotetrasiloxane (OMCTS) and decamethylcyclopentasiloxane (DMCPS). Inertness of these two liquids makes them ideal for determination of surface tension of low-energy fluoropolymers. On the other hand, contact angles of many other liquids deviated somewhat from a smooth contact angle pattern that represents the EGC-1700 surface tension. It is argued that noninertness of the molecules of these liquids gives rise to specific interactions with the polymer film, causing the deviations. Furthermore, contact angles of a series of n-alkanes (n-hexane to n-hexadecane) showed systematic deviations from this curve, similar to the trend observed for n-alkanes/Teflon AF 1600 systems studied earlier. Adsorption of vapor of short-chain liquids onto the polymer film caused their contact angles to fall above the gammasv=13.84 mJ/m2 curve, and a parallel alignment of molecules of the long-chain n-alkanes in the vicinity of the solid was the explanation for the deviation of their contact angles below it. It is found that vapor adsorption effect is more significant in the case of Teflon AF 1600, while the alignment of liquid molecules close to the surface is more pronounced for EGC-1700.

Journal Article↗

PubMed2005

Effect of electric fields on contact angle and surface tension of drops.

Contact angles of sessile drops were experimentally investigated in the electric field. The experimental setup was designed such that the electric field was applied to all three interfaces. The advanced Automated Polynomial Fitting (APF) methodology was employed to measure contact angles with high accuracy. The significance of the observations and trends was examined by conducting statistical tests of hypothesis. It was found that contact angles of polar liquids such as alcohols increase in the electric field. However, no significant trend was observed for nonpolar liquids such as alkanes. The change in the contact angle was found to be stronger for liquids with longer molecules. It was shown that the polarity of the electric field is not an underlying factor in the observed trends. Using the equation of state for interfacial tensions, the observed shift in contact angles was translated into a corresponding change in surface tension of the liquids. The results suggest that the surface tension of alcohols increases by one to two percent (depending on the size of molecules) when an electric field of the order of magnitude of 10(6) V/m is applied.

Journal Article↗

PubMed2004

Contact angle measurements with liquids consisting of bulky molecules.

Well-measured contact angles with different solid-liquid systems fall approximately on smooth patterns when plotted versus liquid surface tension. However, there are deviations of 1 degrees -3 degrees , which are outside the error limits. It is the purpose of this paper to elucidate the reasons for such deviations. Two types of liquids were selected for advancing contact angle measurements on Teflon AF 1600 coated surfaces: a series of n-alkanes ranging from n-hexane to n-hexadecane and five liquids consisting of bulky molecules, octamethylcyclotetrasiloxane (OMCTS), methyl salicylate, tetralin, cis-decalin, and octamethyltrisiloxane (OMTS). It was found that contact angles of the liquids with bulky molecules fall on a perfectly smooth curve corresponding to a solid surface tension of 13.64 +/- 0.1 mJ/m2. However, contact angles of n-alkanes deviated from this curve by up to 3 degrees in a complicated fashion. The observed trend suggests that more than one mechanism is responsible for the deviations. Substrate-induced rearrangement of liquid molecules in the close vicinity of the surface in the case of long-chain n-alkanes and adsorption of vapor onto the solid surface in the case of short-chain n-alkanes are the most likely explanations. The results suggest that liquids with bulky molecules appear to be suitable for contact angle measurements to characterize energetics of polymeric surfaces.

Journal Article↗

PubMed2001

Novel inhibitors of poly(ADP-ribose) polymerase/PARP1 and PARP2 identified using a cell-based screen in yeast.

Multicellular organisms must have means of preserving their genomic integrity or face catastrophic consequences such as uncontrolled cell proliferation or massive cell death. One response is a modification of nuclear proteins by the addition and removal of polymers of ADP-ribose that modulate the properties of DNA-binding proteins involved in DNA repair and metabolism. These ADP-ribose units are added by poly(ADP-ribose) polymerase (PARP) and removed by poly(ADP-ribose) glycohydrolase. Although budding yeast Saccharomyces cerevisiae does not possess proteins with significant sequence similarity to the human PARP family of proteins, we identified novel small molecule inhibitors against two family members, PARP1 and PARP2, using a cell-based assay in yeast. The assay was based on the reversal of growth inhibition caused by the heterologous expression of either PARP1 or PARP2. Validation of the assay was achieved by showing that the growth inhibition was relieved by a mutation in a single residue in the catalytic site of PARP1 or PARP2 or exposure of yeast to a known PARP1 inhibitor, 6(5H)-phenanthridinone. In separate experiments, when a putative protein regulator of PARP activity, human poly(ADP-ribose) glycohydrolase, was coexpressed with PARP1 or PARP2, yeast growth was restored. Finally, the inhibitors identified by screening the yeast assay are active in a mammalian PARP biochemical assay and inhibit PARP1 and PARP2 activity in yeast cell extracts. Thus, our data reflect the strength of using yeast to identify small molecule inhibitors of therapeutically relevant gene families, including those that are not found in yeast, such as PARP. The resultant inhibitors have two critical uses (a) as leads for drug development and (b) as tools to dissect cellular function.

ATP-Binding Cassette Transporters↗