Recent progress in the determination of solid surface tensions from contact angles.

Abstract

Advancing contact angles of different liquids measured on the same solid surface fall very close to a smooth curve when plotted as a function of liquid surface tension, i.e., gamma(lv)costheta versus gamma(lv). Changing the solid surface, and hence gamma(sv), shifts the curve in a regular manner. These patterns suggest that gamma(lv)costheta depends only on gamma(lv) and gamma(sv). Thus, an "equation of state for the interfacial tensions" was developed to facilitate the determination of solid surface tensions from contact angles in conjunction with Young's equation. However, a close examination of the smooth curves showed that contact angles typically show a scatter of 1-3 degrees around the curves. The existence of the deviations introduces an element of uncertainty in the determination of solid surface tensions. Establishing that (i) contact angles are exclusively a material property of the coating polymer and do not depend on experimental procedures and that (ii) contact angle measurements with a sophisticated methodology, axisymmetric drop shape analysis (ADSA), are highly reproducible guarantees that the deviations are not experimental errors and must have physical causes. The contact angles of a large number of liquids on the films of four different fluoropolymers were studied to identify the causes of the deviations. Specific molecular interactions at solid-vapor and/or solid-liquid interfaces account for the minor contact angle deviations. Such interactions take place in different ways. Adsorption of vapor of the test liquid onto the solid surface is apparently the only process that influences the solid-vapor interfacial tension (gamma(sv)). The molecular interactions taking place at the solid-liquid interface are more diverse and complicated. Parallel alignment of liquid molecules at the solid surface, reorganization of liquid molecules at the solid-liquid interface, change in the configuration of polymer chains due to contact with certain probe liquids, and intermolecular interactions between solid and liquid molecules cause the solid-liquid interfacial (gamma(sl)) tension to be different from that predicted by the equation of state, i.e., gamma(sl) is not a precise function of gamma(lv) and gamma(sv). In other words, the experimental contact angles deviate from the "ideal" contact angle pattern. Specific criteria are proposed to identify probe liquids which eliminate specific molecular interactions. Octamethylcyclotetrasiloxane (OMCTS) and decamethylcyclopentasiloxane (DMCPS) are shown to meet those criteria, and therefore are the most suitable liquids to characterize surface tensions of low energy fluoropolymer films with an accuracy of +/-0.2 mJ/m2.