Hidetoshi Takashima | PubMed Health

PubMedDate not supplied

Hydroxyapatite coating on a titanium metal substrate by a discharging method in modified artificial body fluid.

PURPOSE: The aim of this study was to evaluate the formation of a hydroxyapatite coating on titanium plate by discharging in typical and modified artificial body fluids. MATERIALS AND METHODS: Japanese Industrial Standard Grade 2 titanium plates were used as specimens. Discharging was performed on the specimens in each solution, and the surface topography of each coating was observed with a scanning electron microscope. The Ca/P atomic ratio and surface characterization of each coating were evaluated by x-ray photoelectron spectroscopy, and crystal phases of each coating were analyzed by Fourier transform infrared spectroscopy and x-ray diffraction. RESULTS: Tricalcium phosphate formed on the titanium surface in a 1.5 Ca/P solution with high ion concentrations of calcium (2.5 mmol/L) and phosphorous (1.67 mmol/L). Crystalline HA was formed on the titanium surface in a 1.5 Ca/P solution (Hanks' balanced salt solution without organic molecules) with low ion concentrations of calcium (1.26 mmol/L) and phosphorus (0.83 mmol/L). DISCUSSION: A solution containing organic pH buffer was insufficient to form stable coatings on the titanium surface. Coating properties strongly depended on the Ca/P chemical ratio of the applied solution. A Ca/P ratio of 1.5 was appropriate for preparing a calcium phosphate coating on a titanium surface, whereas a Ca/P ratio of 2.5 was excessively high. CONCLUSION: These findings suggest that Hanks' balanced salt solution without organic molecules is the most suitable solution for forming crystalline hydroxyapatite coatings on titanium surfaces by the discharging method.

Body Fluids↗

PubMedDate not supplied

Functionally gradient bonelike hydroxyapatite coating on a titanium metal substrate created by a discharging method in HBSS without organic molecules.

PURPOSE: This study evaluated the quality of coatings on titanium surfaces prepared by discharging in Hanks' balanced salt solution without organic molecules (HBSS-). MATERIALS AND METHODS: 10 x 10 x 1.0-mm titanium plates were used as cathodes of a coating device developed in the laboratory and immersed in HBSS-. A piece of platinum foil was used as a counterelectrode. Discharging was maintained at 1 A and 10 V (416 mA/cm2) for periods of 90, 270, and 540 seconds. Crystal phases of the coatings were identified by x-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). In addition, the surface characterization and Ca/P atomic ratio of the titanium surfaces were determined by x-ray photoelectron spectroscopy (XPS). Furthermore, the surface topography, the thickness of the coatings, and the bonds between coatings and titanium substrates were observed by scanning electron microscopy. RESULTS: The FTIR and XRD studies demonstrated that the deposits on the titanium after 540 seconds of discharging were crystalline hydroxyapatite. In addition, the thickness of the titanium suboxide layer increased during discharging. The XPS studies indicated that after 540 seconds of processing, the mean Ca/P ratio of the coatings on the titanium was 1.71, which is similar to that of human bone. DISCUSSION: In addition, the replacement of sodium ions with calcium ions seemed important for the promotion of crystallization of the coating. Furthermore, the XPS studies demonstrated that the coatings had a gradient function. Scanning electron microscopy showed that adhesion between coatings and the titanium substrate was close. The coatings were approximately 1 microm thick. CONCLUSION: These findings suggest that a very thin crystalline bonelike hydroxyapatite coating with a gradient function could be prepared on a titanium metal substrate in HBSS- by a discharging method.

Adhesiveness↗