J F Orr

Publications and source records attributed to J F Orr.

At least 19 recordsLinked to original sources

PubMed2006

Validation of the small-punch test as a technique for characterizing the mechanical properties of acrylic bone cement.

This paper examines the validity of using the small-punch test technique as a means of quantifying the mechanical properties of acrylic bone cement under different test conditions. The elastic moduli calculated using the small-punch test method were compared with data measured using the international standard for acrylic bone resin, ISO 5833. Conclusions from the study indicate that the small-punch test is a reproducible miniature specimen test method that can be used to characterize the mechanical properties of retrieved acrylic bone cement as used in total joint replacement surgery. Moreover, the test conditions were found to influence the elastic modulus of acrylic bone cement. The test temperature had a greater effect on the elastic behaviour of the bone cement than the test medium.

Bone Cements↗

PubMed2005

Engineering properties and performance of dental crowns.

Dental crowns are used to replace damaged natural crowns of teeth and are fixed to prepared teeth with luting cements, which should provide an adhesive bond to the tooth structure giving reliable retention and minimal microleakage. Mechanical testing of crowns in vitro gives failure load distributions that are well described by Weibull models, comparing probabilities of survival and reliability. Fatigue testing of crowns is time consuming, but regression analysis to interpolate functions through data points quoting probability limits or applying Weibull analysis is achievable. A complementary approach is to conduct materials tests with appropriate interfacial geometries. Luting cements are used in thin layers of 40-150 microm. Contraction during polymerization is restrained by adhesion to substrates, allowing little relaxation of stresses. Conventional and resin-modified glass ionomer cements create thin zones of interaction with dentine and fail cohesively. The chevron notch short rod technique has been used to measure fracture toughness and rank cements. A development of this method, using chevron notch short bar specimens, permitted fracture toughness to be determined for luting cement--dentine substrate interfaces. Representative fracture experiments need to be developed to apply mixed mode conditions. The basic challenge to predict long-term performance from short-term laboratory tests remains.

Biomedical Engineering↗

PubMed2004

Processing, annealing and sterilisation of poly-L-lactide.

Poly-L-lactide (PLLA) is one of the most significant members of a group of polymers regarded as bioabsorbable. Degradation of PLLA proceeds through hydrolysis of the ester bonds in the polymer chains and is influenced significantly by the polymer's molecular weight and crystallinity. To evaluate the effects of processing and sterilisation on these properties, PLLA pellets were either compression moulded or extruded, subjected to annealing at 120 degrees C for 4h and sterilised by ethylene oxide (EtO) gas. Procedures were used to evaluate the mechanical properties, molecular weight and crystallinity. Upon processing, the crystallinity of the material fell from 61% for the PLLA pellets to 12% and 20% for the compressed and extruded components, respectively. After annealing, crystallinity increased to 43% for the compression-moulded material and 40% for the extruded material. Crystallinity further increased upon EtO sterilisation. A slight decrease in molecular weight was observed for the extruded material through processing, annealing and sterilisation. Young's modulus generally increased with increasing crystallinity, and extension at break and tensile strength decreased. The results from this investigation suggest that PLLA is sensitive to processing and sterilisation, altering properties critical to its degradation rate.

Absorbable Implants↗

PubMed2004

Degradation of poly-L-lactide. Part 1: in vitro and in vivo physiological temperature degradation.

Poly-L-lactide (PLLA) is one of the most significant members of a group of polymers regarded as bioresorbable. The degradation of PLLA proceeds through hydrolysis of the ester linkage in the polymer's backbone and is influenced by the polymer's initial molecular weight and degree of crystallinity. To evaluate its degradation PLLA pellets were processed by compression moulding into tensile test specimens and by extrusion into 2 mm diameter lengths of rod, prior to being sterilized by ethylene oxide gas (EtO) and degraded in both in vitro and in vivo environments. On retrieval at predetermined time intervals, procedures were used to evaluate the material's molecular weight, crystallinity, mechanical strength, and thermal properties. Additionally, the in vivo host tissue's biological response was analysed. The results from this study suggest that in both the in vitro and in vivo environments, degradation proceeded at the same rate and followed the general sequence of aliphatic polyester degradation, ruling out enzymes contributing and accelerating the degradation rate in vivo. Additionally, the absence of cells marking an inflammatory response suggests that the PLLA rods investigated in vivo were biocompatible throughout the 44 weeks duration of the study, before any mass loss was observed.

Absorbable Implants↗

PubMed2004

Degradation of poly-L-lactide. Part 2: increased temperature accelerated degradation.

Poly-L-lactide (PLLA) is one of the most significant members of a group of polymers regarded as bioresorbable. The degradation of PLLA proceeds through hydrolysis of the ester linkages in the polymer's backbone; however, the time for the complete resorption of orthopaedic devices manufactured from PLLA is known to be in excess of five years in a normal physiological environment. To evaluate the degradation of PLLA in an accelerated time period, PLLA pellets were processed by compression moulding into tensile test specimens, prior to being sterilized by ethylene oxide gas (EtO) and degraded in a phosphate-buffered solution (PBS) at both 50 degrees C and 70 degrees C. On retrieval, at predetermined time intervals, procedures were used to evaluate the material's molecular weight, crystallinity, mechanical strength, and thermal properties. The results from this study suggest that at both 50 degrees C and 70 degrees C, degradation proceeds by a very similar mechanism to that observed at 37 degrees C in vitro and in vivo. The degradation models developed also confirmed the dependence of mass loss, melting temperature, and glass transition temperature (Tg) on the polymer's molecular weight throughout degradation. Although increased temperature appears to be a suitable method for accelerating the degradation of PLLA, relative to its physiological degradation rate, concerns still remain over the validity of testing above the polymer's Tg and the significance of autocatalysis at increased temperatures.

Absorbable Implants↗

PubMed2004

Assessment of cement introduction and pressurization techniques.

The objective of this study was to measure the medullary pressures generated during bone cement injection, pressurization and femoral prosthesis insertion. The measurements were recorded throughout the length of an in vitro femoral model while implanting a series of prosthetic hip stems using different pressurization techniques. The prostheses used were a Charnley 40 flanged stem (Johnson & Johnson DePuy International Limited), an Exeter No. 3 stem (Stryker Howmedica Osteonics, Howmedica International Limited), and a customized femoral component (Johnson & Johnson DePuy International Limited). The following parameters were derived from the pressure data recorded: peak pressure, decay pressure and duration above optimum pressure of 76 kPa to predict adequate penetration. The custom and Exeter stems generated cement pressures throughout the length of the cavity model that were predicted to achieve adequate bone cement interdigitation into cancellous bone. For all the conditions investigated in this study, when using the Charnley femoral component, an adequate level of cement pressurization was generated in the medial-distal portion of the femoral cavity. It is postulated that this could result in reduced integration of the cement mantle with bone and less effective transmission of functional loads applied during a patient's normal activity, postoperatively.

Arthroplasty, Replacement, Hip↗

PubMed2003

The influence of inert packaging on the shelf ageing of gamma-irradiation sterilised ultra-high molecular weight polyethylene.

Ultra-high molecular weight polyethylene (UHMWPE) is used for wear applications in total hip prostheses and total knee prostheses. Sterilisation of these prostheses is commonly by gamma-irradiation. This process creates reactive free radicals in the UHMWPE, greatly increasing its susceptibility to oxidative degradation. This study has investigated the influence of air and vacuum packaging on the properties of gamma-irradiated UHMWPE (GUR1050) following 3 years of shelf ageing. The findings indicate that vacuum packaging minimises oxidative degradation reactions that occur for UHMWPE during shelf ageing. However, gamma-irradiation of vacuum-packaged UHMWPE promotes a degree of cross-linking. It is proposed that this may enhance the wear performance of UHMWPE. Accelerated ageing studies indicate that 3 years of shelf ageing would also seem to reduce the susceptibility of gamma-irradiated UHMWPE to oxidative degradation upon removal from its vacuum packaging.

Biocompatible Materials↗

PubMed2003

The relationship between porosity and fatigue characteristics of bone cements.

In this study, the fatigue strengths of acrylic cement prepared by various commercially available reduced pressure mixing systems were compared with the fatigue strength of cement mixed by hand (control) under atmospheric conditions. The following observations were made from this investigation. The mean fatigue strength of reduced pressure mixed acrylic bone cement is double that of cement mixed by hand using an open bowl, 11,354+/-6,441 cycles to failure for reduced pressure mixing in comparison with 5,938+/-3,199 cycles for mixing under atmospheric conditions. However, the variability in mean fatigue strengths of reduced pressure mixed bone cement is greater for some mixing devices. The variation in fatigue strengths for the different mixing techniques is explained by the different porosity distributions. The design of the reduced pressure mixing system and the technique employed during mixing strongly contribute to the porosity distribution within the acrylic bone cement. The level of reduced pressure applied during cement mixing has an effect on the fatigue strength of bone cement, but the mixing mechanism is significantly more influential.

Biocompatible Materials↗

PubMed2003

Shrinkage stresses in bone cement.

Shrinkage of bone cement is reported primarily as a consequence of polymerisation, however thermal shrinkage also occurs as a result of its exothermic reaction. It is proposed that the latter effect is important, since it occurs late in the curing cycle at a time when the cement has attained its mechanical properties as a solid, and that residual stresses result. Observations from experiments and literature reports suggest that residual stresses may be sufficient to initiate cracks at the interface between hip replacement stems and cement.A theoretical model has been developed to calculate interference stresses, using thick-walled cylinder theory, on the basis of thermal and total shrinkages. Thermal shrinkage values were calculated using the coefficient of linear thermal expansion of bone cement, while total shrinkages were measured. Moduli of elasticity values were measured for acrylic bone cements ranging from 2.1 to 2.7GPa, as were Poisson's ratio values ranging from 0.38 to 0.46. Theoretical calculation of stresses in a cement mantle, based on assumptions of thermal shrinkage alone, predicted circumferential stresses of 8.4-25.2MPa for cement curing temperatures in the range 60-140 degrees C. It is concluded that cracks observed around hip prosthesis stems in laboratory specimens of bone cement are due to shrinkage and that residual stresses are sufficient to cause crack initiation prior to functional loading.

Bone Cements↗

PubMed2003

Fracture characteristics of acrylic bone cement-bone composites.

In this study, the fracture properties of Perspex, acrylic bone cement prepared using a commercially available reduced pressure mixing system and a bone cement-bone composite were compared under different test conditions. The method used was the double-torsion (DT) test. The observations made from this investigation are as follows. The fracture toughness and critical crack length for Perspex significantly increased (ANOVA, p = 0.001) when tested in water compared to air. An increase in test temperature from 19 to 37 degrees C resulted in a decrease in the fracture properties in water, this reduction being also statistically significant (ANOVA, p = 0.02). The mean fracture toughness and standard deviation of CMW3 bone cement when mixed under reduced pressure was 2.19 +/- 0.11 MN m(-3/2) compared to 3.89 +/- 0.10 MN m(-3/2) for the cement-bone composite (ANOVA, p = 0.004). The crack length determined for CMW3 bone cement and the cement bone composite were 0.323 +/- 0.031 and 1.1434 +/- 0.61 mm respectively. The plateau loads of the composite material were higher than measured for the monolithic acrylic bone cement, 249.66 +/- 67.75 N compared with 140.83 +/- 6.82 N. The high level of variation recorded for the plateau loads of the bone cement bone composite is due to the orientation and volume fraction of the cancellous bone. It can be concluded from this investigation that acrylic bone cement interdigitation into the cancellous bone results in a superior material with respect to crack resistance in comparison with the bone cement as a lone entity. Therefore it is an advantage if there is sufficient cancellous bone stock available within the intermedullary canal to allow bone cement penetration to occur, for the transfer of loads during daily activity. Additionally, it is paramount that the clinician ensures that adequate pressure is applied and maintained for an appropriate time during cement injection and prosthesis insertion in order to ensure optimum cement penetration into the pore openings of the cancellous bone, thus improving the resistance of the cement mantle to fracture and ultimately improving the longevity of the joint replacement.

Animals↗

PubMed2002

Curing characteristics of acrylic bone cement.

Commercial acrylic bone cements are supplied as two components, a polymer powder and a liquid monomer. Mixing of the two components is followed by a progressive polymerization of the liquid monomer to yield a solid mass, a high level of heat being generated during this exothermic reaction. The exposure of bone to high temperatures has led to incidences of bone necrosis and tissue damage, ultimately resulting in failure of the prosthetic fixation. The aim of this study was to determine the thermal properties of two acrylic bone cements as they progress through their polymerization cycles. It was also felt that there was a need to quantify the variations in the curing characteristics as a function of preparing bone cement by different techniques, hand mixing and vacuum mixing. A number of parameters were calculated using the data gathered from the investigation: peak temperature, cure temperature, cure time, and the cumulative thermal necrosis damage index. The results show the temperature profile recorded during polymerization was lowest when the cement was prepared using the Howmedica Mix-Kit I system: 36 degrees C for Palacos R and 41 degrees C for CMW3 respectively. When the acrylic cements were prepared in any vacuum mixing system there was evidence of an increase in the cure temperature. The main factor that contributed to this rise in temperature was an imbalance in the polymer powder : liquid monomer ratio, there was a high incidence of unmixed powder visible in the mixing barrel of some contemporary vacuum mixing devices. Observing the thermal characteristics of the polymethyl methacrylate (PMMA) bone cements assessed, it was found that particular formulations of bone cements are suited to certain mixing methodologies. It is vital that a full investigation is conducted on a cement mixing/delivery system prior to its introduction into the orthopaedic market.

Journal Article↗

PubMed2002

The influence of shape and sliding distance of femoral head movement loci on the wear of acetabular cups in total hip arthroplasty.

Wear of the polyethylene acetabular component is the most serious threat to the long-term success of total hip replacements (THRs). Greatly reduced wear rates have been reported for unidirectional, compared to multidirectional, articulation in vitro. This study considers the multidirectional motions experienced at the hip joint as described by movement loci of points on the femoral head for individual THR patients. A three-dimensional computer program determined the movement loci of selected points on the femoral head for THR patients and normal subjects using kinematic data obtained from gait analysis. The sizes and shapes of these loci were quantified by their sliding distances and aspect ratios with substantial differences exhibited between individual THR patients. The average sliding distances ranged from 10.0 to 18.1 mm and the average aspect ratios of the loci ranged from 2.5 to 9.2 for the THR patients. Positive correlations were found between wear rate and average sliding distance, the inverse of the average aspect ratio of the loci and the product of the average sliding distance and the inverse of the average aspect ratio of the loci. Patients with a normal hip joint range of motion produce multidirectional motion loci and tend to experience more wear than patients with more unidirectional motion loci. Differing patterns of multidirectional motion at the hip joint for individual THR patients may explain widely differing wear rates in vivo.

Acetabulum↗

PubMed2002

Fracture mechanics analysis of the dentine-luting cement interface.

The objectives of this study were to determine the fracture toughness of adhesive interfaces between dentine and clinically relevant, thin layers of dental luting cements. Cements tested included a conventional glass-ionomer, F (Fuji 1), a resin-modified glass-ionomer, FP (Fuji Plus) and a compomer cement, D (DyractCem). Ten miniature short-bar chevron notch specimens were manufactured for each cement, each comprising a 40 microm thick chevron of lute, between two 1.5 mm thick blocks of bovine dentine, encased in resin composite. The interfacial K(IC) results (MN/m3/2) were median (range): F; 0.152 (0.14-0.16), FP; 0.306 (0.27-0.37), D; 0.351 (0.31-0.37). Non-parametric statistical analysis showed that the fracture toughness of F was significantly lower (p <0.05) than those of FP or D, and all were significantly lower than values for monolithic cement specimens. Scanning electron microscopy of the specimens suggested crack propagation along the interface. However, energy dispersive X-ray analysis indicated that failure was cohesive within the cement. It is concluded that the fracture toughness of luting cement was lowered by cement-dentine interactions.

Animals↗

PubMed2001

Influence of mixing techniques on the physical properties of acrylic bone cement.

Palacos R bone cement was prepared using three commercially available mixing techniques, first generation, second generation and third generation, to determine the mechanical properties and porosity contents of the bone cement. The compressive strengths, bending strengths and flexural moduli were expressed as a function of void content. The volume of pores within the cement structure was found to be a contributing factor to the physical properties of acrylic bone cement. The lower the volume of voids in the cement the better the compressive and flexural properties, hence stronger bone cement. It was found that the best results were obtained from cement that had been mixed using the Mitab Optivac or Summit HiVac Syringe systems at a reduced pressure level of between -72 and -86 kPa below atmospheric pressure, resulting in cement of porosity 1.44-3.17%; compressive strength 74-81 MPa; flexural modulus 2.54-2.60 GPa; and flexural strength 65-73 MPa.

Acrylates↗

PubMed2001

A comparative evaluation of dental luting cements by fracture toughness tests and fractography.

In recent years there has been a shift from traditional methods of investigating dental materials to a fracture mechanics approach. Fracture toughness (KIC) is an intrinsic material property which can be considered to be a measure of a material's resistance to crack propagation. Glass-ionomer cements are biocompatible and bioactive dental restorative materials, but they suffer from poor fracture toughness and are extremely susceptible to dehydration. The main objective of this study was to evaluate the fracture toughness of three types of commercially available dental cements (polyacid-modified composite resin, resin-modified and conventional glass ionomer) using a short-rod chevron-notch test and to investigate and interpret the results by means of fractography using scanning electron microscopy. Ten specimens of each cement were fabricated according to manufacturers' instructions, coated in varnish, and stored at ambient laboratory humidity, 100 per cent relative humidity, or in water at 37 degrees C for 7 days prior to preparation for testing. Results indicated that significant differences existed between each group of materials and that the fracture toughness ranged from 0.27 to 0.72 MN/m3/2. It was concluded that the resin-modified glass-ionomer cement demonstrated the highest resistance to crack propagation. Fractographs clearly showed areas of stable and unstable crack growth along the fractured surfaces for the three materials examined.

Compomers↗

PubMed2000

The influence of luting cement on the probabilities of survival and modes of failure of cast full-coverage crowns.

OBJECTIVES: This study compares the probabilities of survival and modes of failure of cast full-coverage crowns bonded with five cements when subjected to tensile pull-off testing. METHODS: Five groups of 25 sound human premolar teeth were prepared for full-coverage crowns, impressions recorded and customized castings fabricated in Ni-Cr-Mb bonding alloy. The cements tested were zinc phosphate, a hand-mixed and capsulated conventional glass-ionomer cement, a resin-modified glass-ionomer cement and a resin composite luting cement. The cemented crowns were stored in water at 37 degrees C for 24 h prior to application of a tensile pull-off force at a strain rate of 10 mm/min. The loads at failure were ranked and modelled by derived Weibull functions each describing the probability of a given specimen failing under a given load. Non-parametric statistical analysis was also applied to the results. RESULTS: There were no significant differences between the loads at failure of zinc phosphate cement, the hand-mixed or the capsulated glass-ionomer cements. The resin-modified glass-ionomer cement and the resin composite cement failed at significantly higher loads than the other three cements, but were not significantly different from each other. The Weibull modulus ranking for each cement from highest to lowest was resin composite = zinc phosphate, resin-modified glass-ionomer, hand-mixed conventional glass-ionomer and capsulated conventional glass-ionomer cement. SIGNIFICANCE: Weibull analysis allows dentists to compare the probability of survival of a crown bonded with different cements at a chosen load giving an indication of cement reliability.

Adhesiveness↗

PubMed2000

Photoelastic stress analysis in perforated (Rochette) resin bonded bridge design.

Rochette described the perforated cast metal bonded design for splinting periodontally compromised teeth. The design was later used for replacing missing teeth. The main causes of failure of the perforated (Rochette) type design were attributed to inappropriate case selection and erosion of the composite from perforations. The aim of this study was to analyse the effect of stress magnitude and direction on failure of perforated resin bonded bridges (RBBs). The objective was to compare stress magnitudes in this design with those reported on the non-perforated RBBs. Photoelastic modelling materials were selected to represent the relative stiffnesses of a posterior mandibular and an anterior maxillary perforated (Rochette) type design. The sizes of the models were scaled to x 2.5 in order to enhance visual analysis of the stress patterns. Stress magnitudes were quantified from isochromatic fringes and stress directions were evaluated from stress trajectories. These revealed a high-stress concentration around the perforations, particularly for those at the proximo-lingual/palatal (connector) areas. This experimental study revealed that the main reason for failure of Rochette designs is deformation at the perforations.

Birefringence↗

PubMed2000

Movement loci of selected points on the femoral head for individual total hip arthroplasty patients using three-dimensional computer simulation.

Wear of ultra-high-molecular-weight polyethylene (UHMWPE) and the subsequent adverse tissue reaction to the wear particles has been cited as the predominant problem affecting total joint arthroplasties. Wear of the UHMWPE acetabular cup in total hip arthroplasties (THAs) is influenced by the sliding distance and direction of individual points on the femoral head, which has as yet been ascertained only for normal subjects. This study seeks to determine the trajectory of specified points on the femoral head for individual THA patients and the distances traversed by these points. A computer program was designed to use gait data from THA patients to simulate the motion of these points. Gait analysis was performed on 19 THA patients at a period of 5 years after operation. The orientation of the acetabular cup was ascertained from radiographs to determine the position of the points on the head most involved in the wear process. The loci of the points differed widely in size, shape, and direction between subjects. The largest average distance traversed was 140% greater than the smallest average distance traversed. Shorter longitudinal paths would tend to cause less wear than larger, wider paths, which cross a greater number of adjacent paths.

Aged↗