PubMed2006

Frequency-dependent complex modulus of the uterus: preliminary results.

The frequency-dependent complex moduli of human uterine tissue have been characterized. Quantification of the modulus is required for developing uterine ultrasound elastography as a viable imaging modality for diagnosing and monitoring causes for abnormal uterine bleeding and enlargement, as well assessing the integrity of uterine and cervical tissue. The complex modulus was measured in samples from hysterectomies of 24 patients ranging in age from 31 to 79 years. Measurements were done under small compressions of either 1 or 2%, at low pre-compression values (either 1 or 2%), and over a frequency range of 0.1-100 Hz. Modulus values of cervical tissue monotonically increased from approximately 30-90 kPa over the frequency range. Normal uterine tissue possessed modulus values over the same range, while leiomyomas, or uterine fibroids, exhibited values ranging from approximately 60-220 kPa.

Adult↗

PubMed2006

Stability of heterogeneous elastography phantoms made from oil dispersions in aqueous gels.

A set of five tissue-mimicking phantoms with cylindrical inclusions were produced for assessing long-term stability of geometry and elastic properties and assessing accuracy of determination of elastic properties. The base aqueous materials were either gelatin or a mixture of agar and gelatin. Stiffness was controlled by selection of the volume percent consisting of microscopic safflower oil droplets. Cylinder diameters remained unchanged within 1% or 2% over many months. Strain ratios from elastograms of the phantoms were stable over many months, implying that elastic contrasts were also stable. Test samples, called production samples, for measurement of Young's moduli were made at the time of manufacture of each phantom and were stored separately from one another. Each production sample was homogeneous and consisted of either inclusion material or background material. For all five phantoms, it was found that the elastic contrast computed using Young's modulus values determined using the production samples accurately represented the true elastic contrasts in the corresponding phantom. This finding was established by the fact that the (true) elastic contrasts determined using samples excised from the phantoms themselves agreed with the elastic contrasts obtained using the homogeneous production samples.

Agar↗

PubMed2006

Anthropomorphic breast phantoms for testing elastography systems.

Two equivalent anthropomorphic breast phantoms were constructed, one for use in ultrasound elastography and the other in magnetic resonance (MR) elastography. A complete description of the manufacturing methods is provided. The materials used were oil-in-gelatin dispersions, where the volume percent oil differentiates the materials, primarily according to Young's moduli. Values of Young's moduli are in agreement with in vitro ranges for the corresponding normal and abnormal breast tissues. Ultrasound and nuclear magnetic resonance (NMR) properties are reasonably well represented. Phantoms of the type described promise to aid researchers who are developing hardware and software for elastography. Examples of ultrasound and MR elastograms of the phantoms are included to demonstrate the utility of the phantoms. Also, the level of stability of elastic properties of the component materials is quantified over a 15-month period. Such phantoms can serve as performance-assessing intermediaries between simple phantoms (consisting, for example, of homogeneous cylindrical inclusions in a homogeneous background) and a full-scale clinical trial. Thus, premature clinical trials may be avoided.

Anthropometry↗

PubMed2005

Spherical lesion phantoms for testing the performance of elastography systems.

A set of three cubic one-litre phantoms containing spherical simulated lesions was produced for use in comparing lesion detection performance of different elastography systems. The materials employed are known to be stable in heterogeneous configurations regarding geometry and elastic contrast identical with (storage modulus of lesion material) / (storage modulus of background material), and regarding ultrasound and NMR properties. The materials mimic soft tissues in terms of elastic, ultrasound and NMR properties. Each phantom has only one value of elastic contrast (3.3, 4.6 or 5.5) and contains arrays of 1.6 mm, 2 mm, 3 mm and 4 mm diameter spherical simulated lesions. All the spheres of a given diameter are arranged in a regular array with coplanar centres. Elastograms of an array made with ultrasound allow determination of the depth range over which lesions of that diameter and elastic contrast can be detected. Two phantoms are made from agar-plus-gelatin-based materials, and one is made from oil-in-gelatin dispersions. The methods for producing the phantoms are described in detail. Lesion detection performances for two ultrasound systems, both operating at about 7.5 MHz and focused at about 5 cm, were quantified with distinctions between the two systems demonstrated. Neither system was capable of detecting any of the 1.6 mm lesions. Phantoms such as these should be useful in research labs that are refining hardware and/or software for elastography.

Agar↗

PubMed2005

Tissue-mimicking agar/gelatin materials for use in heterogeneous elastography phantoms.

Five 9 cm x 9 cm x 9 cm phantoms, each with a 2-cm-diameter cylindrical inclusion, were produced with various dry-weight concentrations of agar and gelatin. Elastic contrasts ranged from 1.5 to 4.6, and values of the storage modulus (real part of the complex Young's modulus) were all in the soft tissue range. Additives assured immunity from bacterial invasion and can produce tissue-mimicking ultrasound and NMR properties. Monitoring of strain ratios over a 7 to 10 month period indicated that the mechanical properties of the phantoms were stable, allowing about 1 month for the phantom to reach chemical equilibrium. The only dependable method for determining the storage moduli of the inclusions is to make measurements on samples excised from the phantoms. If it is desired to produce and accurately characterize a phantom with small inclusions with other shapes, such as an array of small spheres, an auxiliary phantom with the geometry of the cylindrical inclusion phantoms or the equivalent should be made at the same time using the same materials. The elastic contrast can then be determined using samples excised from the auxiliary phantom. A small increase of about 10% in volume of the cylindrical inclusions occurred-a tolerable increase. Interestingly, the smallest increase (about 5%) occurred in the phantom with the largest elastic contrast.

Adhesives↗