Biomedical subjects

Mattias Berglin

Publications and source records attributed to Mattias Berglin.

6 recordsLinked to original sources

PubMed2005

Immune complement activation on polystyrene and silicon dioxide surfaces. Impact of reversible IgG adsorption.

We have studied aspects of the molecular background to immune complement activation on solid surfaces. Quartz crystal microbalance with dissipation monitoring (QCM-D) sensor surfaces were modified by means of spin coating with polystyrene (PS) or sputtering of silicon dioxide (SiO2). The IC activation on modified QCM-D surfaces was investigated by incubation in serum, followed by determinations of the amounts of bound C3 fragments (C3c) at the surface. Determinations of soluble C3a and soluble C5b-9 complex (sC5b-9) were made with enzyme immunoassay (EIA) method. We found that IC activation was high on PS surfaces, independent of the method used for measurements. On the SiO2 surfaces, IC activation was generally lower, but still detectable with anti-C3c as well as sC5b-9 and C3a determinations. Pre-coating the surfaces with a layer of IgG resulted in that IC activation became very high on PS surface, while the IC response remained low on SiO2 surfaces. The lower level of IC activation on the SiO2 surfaces was explained by a low surface concentration of IgG as measured with QCM-D. This was a result of the high reversibility of the IgG protein adsorption as well as absence of sufficient conformational changes of adsorbed IgG molecules. The QCM-D method was as sensitive as the C3a and sC5b-9 determinations to reveal surface associated IC-activation on these model surfaces. Additional advantages of the QCM-D method are the broad dynamic measurement window, i.e. the high precision and the ability to perform time resolved measurements and the ease of making different surface modifications.

Adsorption↗

PubMed2004

Quartz crystal microbalance-with dissipation monitoring (QCM-D) for real time measurements of blood coagulation density and immune complement activation on artificial surfaces.

A recently developed variant of quartz crystal microbalance (QCM) called QCM-with dissipation monitoring (QCM-D) allows simultaneous and simple measurements of changes in adsorbed mass as well as the viscoelastic property (D-factor) of deposited protein layers on the sensor surface. We have taken the QCM-D technology a step further and demonstrated its advantages in the study of protein assembly as a consequence of surface induced immune complement activation, or contact activated blood coagulation. In the present study we have continued our QCM-D investigations of surface assembly of fibrin clot formation and complement activation and incubated differently modified quartz sensor surfaces in blood plasma and sera. Polymer surfaces used were spin-coated polyethylene, poly(ethylene terephtalate), poly(methylmetacrylate) and poly(dimethylsiloxane). Also used were sputtered titanium and heparin grafted surfaces. In this investigation we found that we could describe the surface induced coagulation with four independent parameters: (1) Time of onset of coagulation, (2) fibrin deposition rate, (3) total frequency shift at stable plateau, and (4) fibrin clot density. The most important finding was that the blood plasma clot density can be assessed with the use of D determinations and that the clot density varied significantly with the chemical composition of the surface. However, the D-factor did not give any new analytical information about the possible complement activation mechanisms. Nevertheless, the QCM-D was found to be a reliable tool for the analysis of surface induced complement activation. We also compared the QCM-D technique with traditional enzyme immuno assay (EIA) measurements of soluble products from the surface activation of the complement and coagulation systems. We found that the results from EIA and QCM-D measurements corresponded well for the complement activation but not for the coagulation, probably due to the biological complexity of the coagulation system.

Adsorption↗

PubMed2004

The effect of substrate molecular mobility on surface induced immune complement activation and blood plasma coagulation.

Changing the length of the alkyl ester side chain in poly(alkyl methacrylates) provides a unique opportunity to systematically vary the mobility of the polymer chains, or in other words vary the glass transition temperature (T(g)), without greatly affect the solid surface energy (gamma(s)) of the polymer. A series of poly(alkyl methacrylate) coatings was therefore analysed with regard to the human immune complement (IC) activation and the surface associated blood plasma coagulation cascade (CC) properties. For the IC and CC measurements we used a quartz crystal microbalance (QCM) where we modified the chemistry of the sensor surface by applying 10-30 nm thick poly(alkyl methacrylate) coatings. The surface energy was calculated from water contact angles and small differences between the coatings were observed. The surface chemistry of the coatings, as determined with X-ray photoelectron spectroscopy (XPS), showed no deviation from expected compositions. Tapping mode atomic force microscopy (TM-AFM) measurements revealed that all coatings displayed similar morphology and the roughness was in the range of 0.7-0.9 nm. Increased polymer mobility correlated with a decrease in IC activation, measured as a decreased C3c deposition at the surface. The surface induced CC, measured as fibrin clot formation at the surface, was different between the different coatings but no correlation with molecular mobility was observed. Thus, the molecular mobility of the polymer chains had a major effect on both the IC and the CC and it seems that different aspects of the chemistry of the solid surface regulate activation of the IC and the CC.

Biocompatible Materials↗

PubMed2003

Fouling-release coatings prepared from alpha,omega-dihydroxypoly(dimethylsiloxane) cross-linked with (heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane.

Surface properties of pristine and water-aged polymeric films made of alpha,omega-dihydroxypoly(dimethylsiloxane) (PDMS) cross-linked with (heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane (FTEOS17) or tetraethoxysilane (TEOS) were investigated. The FTEOS17-cured coatings showed stable advancing and receding contact angles over a period of 3 months of water exposure, compared to a 70 degrees decrease in receding contact angle for the TEOS-cured coatings. After immersion in water, hydroxyl groups were detected on the TEOS-cured coatings with attenuated total reflection infrared spectroscopy (ATR-FT/IR). Tapping-mode atomic force microscopy (TM-AFM) on pristine FTEOS17-cured coatings showed surfaces topologies ranging from smooth and featureless to topologically complex, depending on FTEOS17 concentration. The fluorinated coatings showed a stable surface morphology after water immersion, which we believe is due to the formation of a fluorinated siliceous phase that prevented the surface reconstruction, water penetration, and hydrolysis. The smooth pristine TEOS-cured coatings showed an increased roughness with cracks and erosion pits present on the surface after water immersion.

Cross-Linking Reagents↗

PubMed2003

Coating modulus and barnacle bioadhesion.

The effect of coating modulus on the strength of pseudobarnacle adhesive bonding was investigated. A radical polymerized poly(butylmethacrylate) coating cross-linked with allylmethacrylate was used as a model coating. The coating Tg was determined to be 18 degrees C by differential scanning calorimetry (DSC). Dynamic contact angle measurements (DCA) at different temperatures indicated that the surface chemistry was not significantly affected in the range investigated (5-50 degrees C). However, an increased noise level in the force vs. displacement curves indicated an increased molecular mobility with a fast reorganization of hydrophilic ester groups during the measurement. Dynamic mechanical analysis (DMA) as a function of temperature revealed a large drop in storage modulus (G') from 20 degrees C to 70 degrees C, as expected. A good correlation between the coating storage modulus and the detachment stress of pseudobarnacles was observed even though energy dissipation during the analysis was observed. The decreased adhesion might be a result of the increased molecular flexibility as determined by DCA and DMA at increased temperature. The increased molecular mobility might increase the tendency for interfacial slip, which ultimately results in decreased adhesion strength.

Adhesiveness↗

PubMedDate not supplied

Enzymatic cross-linking of a phenolic polymer extracted from the marine alga Fucus serratus.

We have shown that a phenolic polymer (PP) extracted from Fucus serratus can be cross-linked using a vanadium-dependent bromoperoxidase (BPO). The methanol extracted PP was adsorbed to a quartz crystal sensor and the cross-linking was initiated by the addition of BPO, KBr, and H2O2. The decreased dissipation upon addition of the cross-linking agents, as measured with the quartz crystal microbalance with dissipation monitoring (QCM-D) method, was interpreted as intramolecular cross-links were formed between different phloroglucinol units in the PP. With surface plasmon resonance, it was shown that no desorption occurred from the sensor surface during the cross-linking. UV/vis spectroscopy verified the results achieved with QCM-D that all components, i.e., BPO, KBr, and H2O2, were necessary in order to achieve intramolecular oxidative cross-linking of the polymer.

Adsorption↗