PubMed · 14618706

Coating modulus and barnacle bioadhesion.

Mattias Berglin·Nina Lönn·Paul Gatenholm
View original source ↗Export metadata ↓

Abstract

The effect of coating modulus on the strength of pseudobarnacle adhesive bonding was investigated. A radical polymerized poly(butylmethacrylate) coating cross-linked with allylmethacrylate was used as a model coating. The coating Tg was determined to be 18 degrees C by differential scanning calorimetry (DSC). Dynamic contact angle measurements (DCA) at different temperatures indicated that the surface chemistry was not significantly affected in the range investigated (5-50 degrees C). However, an increased noise level in the force vs. displacement curves indicated an increased molecular mobility with a fast reorganization of hydrophilic ester groups during the measurement. Dynamic mechanical analysis (DMA) as a function of temperature revealed a large drop in storage modulus (G') from 20 degrees C to 70 degrees C, as expected. A good correlation between the coating storage modulus and the detachment stress of pseudobarnacles was observed even though energy dissipation during the analysis was observed. The decreased adhesion might be a result of the increased molecular flexibility as determined by DCA and DMA at increased temperature. The increased molecular mobility might increase the tendency for interfacial slip, which ultimately results in decreased adhesion strength.

Explore related subjects

AdhesivenessAnimalsBiofilmsCalorimetry, Differential ScanningMaterials TestingMechanicsMethacrylatesPaintTemperatureThoracicaComparative StudyJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Mattias Berglin, Nina Lönn, Paul Gatenholm. 2003. Coating modulus and barnacle bioadhesion.. https://doi.org/10.1080/0892701021000048774

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2006

Influence of a pre-blended antibiotic (gentamicin sulfate powder) on various mechanical, thermal, and physical properties of three acrylic bone cements.

The aim of this work was to determine an array of mechanical, physical, and thermal properties of three pairs of commercially available acrylic bone cement brands, with the brands in each pair having the same compositions except that one contains 4.22 wt/wt% gentamicin sulfate blended with the powder by the manufacturer and the other one does not. The difference between the pairs was in the viscosity of the curing cement dough, with one pair of 'low-viscosity', one pair of 'medium-viscosity', and one pair of 'high-viscosity' brands being used. Thus, the brands studied cover the range of those used in anchoring some total joint replacements (TJRs). The properties determined were the strength, modulus, and work-to-fracture (all under four-point bending), plane-strain fracture toughness, Weibull mean fatigue life (fatigue conditions: 15 MPa; 2 Hz), activation energy and frequency factor for the cement polymerization process (both determined, using differential scanning calorimetry, at heating rates of 5, 10, 15, and 20 K min (1)), and the diffusion coefficient for the absorption of phosphate-buffered saline at 37 C by the cured cement. For each property determined, there was no significant difference in the mean values for the brands in each of the pairs. These results indicate that over the range of cement brands that are widely used in the anchoring of cemented TJRs, the addition of gentamicin sulfate powder does not degrade the properties of the cement, and, hence, may not adversely affect the in vivo longevity of the replacement.

Adhesiveness↗
PubMed2006

Tensile bond strength of dual curing resin-based cements to commercially pure titanium.

OBJECTIVES: The aim of this study was to evaluate the tensile bond strength of dual curing luting resin cements to commercially pure titanium at 10 min and 24h after removal of the oxide layer. METHODS: One hundred and twenty titanium discs were obtained by casting and polishing with silicon carbide papers. The titanium discs were sandblasted with 50 microm aluminum oxide, ultrasonic cleaned and bonded in pairs with the resin-based cements Panavia F and Rely X ARC at 10 min and 24h after the sandblasting. The tensile test was performed with a crosshead speed of 0.5mm/min in an Instron Universal testing machine. RESULTS: The Rely X ARC reached the highest tensile strength value at 24h after sandblasting (18.27 MPa), but there was no statistically significant difference between the two dual curing resin cements for both times tested. All specimens showed a mixture of cohesive fracture in the resin cement and adhesive failure. However, the predominant failure mode for Panavia F was cohesive in resin cement, and the Rely X ARC exhibited a greater proportion of specimens with adhesive failure between the alloy and resin luting cement at 10 min and 24h. SIGNIFICANCE: Both cements had, statistically, the same tensile bond strength. But in the fracture mode analysis, the adhesive predominant fracture mode of Rely X ARC cement indicates a premature clinical adhesive failure. On the other hand, the cohesive predominant fracture mode of Panavia F indicates a longer clinical adhesive bond with titanium.

Adhesiveness↗
PubMed2006

Air classifier technology (ACT) in dry powder inhalation Part 4. Performance of air classifier technology in the Novolizer multi-dose dry powder inhaler.

In this study, the in vitro fine particle deposition from a multi dose dry powder inhaler (Novolizer) with air classifier technology has been investigated. It is shown that different target values for the fine particle fraction (fpf<5 microm) of the same drug can be achieved in a well-controlled way. This is particularly relevant to the application of generic formulations in the inhaler. The well-controlled and predictable fpf is achieved through dispersion of different types of formulations in exactly the same classifier concept. On the other hand, it is shown that air classifier-based inhalers are less sensitive to the carrier surface and bulk properties than competitive inhalers like the Diskus. For 10 randomly selected lactose carriers for inhalation from four different suppliers, the budesonide fpf (at 4 kPa) from the Novolizer varied between 30 and 46% (of the measured dose; R.S.D.=14.2%), whereas the extremes in fpf from the Diskus dpi were 7 and 44% (R.S.D.=56.2%) for the same formulations. The fpf from a classifier-based inhaler appears to be less dependent of the amount of lactose (carrier) fines (<15 microm) in the mixture too. Classifier-based inhalers perform best with coarse carriers that have relatively wide size distributions (e.g. 50-350 microm) and surface discontinuities inside which drug particles can find shelter from press-on forces during mixing. Coarse carrier fractions have good flow properties, which increases the dose measuring accuracy and reproducibility. The fpf from the Novolizer increases with increasing pressure drop across the device. On theoretical grounds, it can be argued that this yields a more reproducible therapy, because it compensates for a shift in deposition to larger airways when the flow rate is increased. Support for this reasoning based on lung deposition modelling studies has been found in a scintigraphic study with the Novolizer. Finally, it is shown that this inhaler produces a finer aerosol than competitor devices, within the fpf<5 microm, subfractions of particles (e.g. <1, 1-2, 2-3, 3-4 and 4-5 microm) are higher.

Adhesiveness↗