Performed since the 1950s, vascular grafting has opened modern era of vascular surgery. Autologous venous grafts are of first choice for revascularisation of small arteries. Synthetic grafts are mainly modelled using microporous polytetrafluoroethylene or terephtalate polyethylene. These prosthesis are mainly used for revascularization of medium and large size arteries.
OBJECTIVES: To investigate mechanisms of textile failure in explanted human aortic endoprostheses. MATERIALS AND METHODS: Endoprostheses (n31) underwent optical and scanning electron microscopy, filament dynamometry, and saturation index measurement. RESULTS: The macroscopic lesions observed in the Stentor and Vanguard devices were holes at the extremities of the stents and slipping of the warp yarns at the level of sutures or of the longitudinal seams. The macroscopic lesions observed in AneurX endoprostheses were holes, slipping of the warp yarns and ruptures of the ligatures. The macroscopic lesions observed in the two Talent endoprostheses were sections of fibers at the level of the suture holes and few areas lesions of wear, with sometimes holes at the contact of the stent extremities. Stentor, Vanguard and AneurX all demonstrated low saturation indexes of the fabric (44-59%) with an important anisotropy. Whereas the Talent endograft demonstrated a high index of saturation (124-131%) with a low anisotropy. We did not demonstrate significant polymer degradation in any of the endoprostheses. CONCLUSIONS: It is essential to take into account the saturation index to optimally choose a woven textile for the construction of an endoprosthesis since this property of the textile may contribute to explain the macroscopic lesions observed. We did not observe significant polymer degradation by filament dynamometry but further studies are needed to confirm these data.
OBJECTIVES: Previous explant retrieval studies have shown ruptures occurring on the remeshing line and the guide line of two types of warp-knitted grafts. The aim of our study was to characterize the mechanisms these ruptures. MATERIALS AND METHODS: We performed an in vitro study of the mechanical and chemical characteristics of virgin prostheses. We studied 2 virgin polyester warp-knitted grafts models: the Cooley Double Velour and the Microvel Double Velour constructed by Meadox (USA), using the following techniques: characterization and de-knitting of the textile structure, circumferential tensile strength, filament dynamometry, critical dissolution time of the filaments and scanning electron microscopy. RESULTS: Both prostheses were constructed in the same way but the texturized yarns of the Cooley graft included twice as many filaments (54) than the Microvel (27). There was more adsorbed tension in the Cooley structure than in the Microvel. The circumferential tensile strength test demonstrated that the Cooley graft always ruptured on the remeshing line and the Microvel graft always ruptured at the interface between the remeshing line and the standard line. Filament dynamometry demonstrated a heterogeneous behavior of the filaments inside the yarns, mainly at the remeshing line of the Cooley graft (27.1 cN/tex +/- 11.5% versus 26.1 cN/tex +/- 2.2% for the guide line and 28 cN/tex +/- 6.7% for the standard knit). Critical dissolution time of the filaments was significantly lower for the Microvel grafts (2.5 sec versus 17.2 sec for the Cooley). CONCLUSIONS: Rupture of knitted polyester prostheses are probably an underestimated phenomenon. They may occur at specific areas of the graft. Further studies are required to determine whether all grafts of this type are at risk.
Explore the source record for details and available documents.
OBJECTIVE: To examine the durability of the Stentor and Vanguard endovascular devices in human implants. METHODS: The textile covering, the polypropylene ligatures and the stent metal of 34 devices (25 Stentor, 9 Vanguard) with a mean duration of implantation of 28.8 +/- 16 months was examined by means of stereomicroscopy and scanning electron microscopy. RESULTS: The polyester textile covering showed gaps along the sutured seam and isolated holes in the fabric. All of the examined polypropylene ligatures were worn, some ruptured. Four different types of stent corrosion were classified--pits (100%), bizarre craters (68%), large deficiencies (14%) and fractures (32%). CONCLUSION: Holes in the polyester fabric and frame dislocations are specific for the design of Stentor and Vanguard grafts. The early corrosion of the stent metal Nitinol in these devices is surprising. Until more experience is gained with other devices, we have to be reminded, that the "gold standard" for the long-term durability of artificial vascular grafts is still "today's" conventional graft.
UNLABELLED: Protected vascular clamps are not new. Clamp associated damage of human arteries has already been published over 20 years ago. The necessity of protective clamps seems to have been forgotten. In our explant archive (230 explants) we have observed an accumulation of graft ruptures in the groin (13 of 25 ruptures). We presume a multifactorial process. Clamp damage could be part of it. The aim of this study is to prove the clamp induced damage of polyester vascular grafts and to examine whether protected clamps can reduce this. METHOD: Five unprotected (Aesculap(R) FB512R, FB502, FB517, Ulrich CC1235, CV3535) and 5 protected vascular clamp types (Aesculap(R) FB667, FB668, Edwards(R) - formally Baxter(R) - Fogarty(R) CV5050, CV5201, Edwards(R) Cosgrove(R) CV1033) were tested. A longitudinal burst test was performed after maximal clamp closure on 6 different, multifilament polyester yarns of 2 different vascular grafts manufacturers (B. Braun(R), Edwards(R)). RESULTS: The yarn tests with protected clamps showed no difference to those of the unclamped yarns. After clamping with unprotected vascular clamps the stress-strain-diagrams differed significantly. The mean, maximum burst strength was up to 75 % lower. Video documentation revealed filament ruptures. Damage of the yarn surface was seen on a simple woven graft in scanning electron microscopy (SEM). DISCUSSION: The application of unprotected vascular clamps on polyester vascular grafts is common in Germany (56 %). The observed damage of multifilament polyester yarns makes it necessary to re-consider the use of unprotected vascular clamps. The benefit for biological vessels has already been shown.
We report the case of a surgically treated congenital Budd-Chiari syndrome related to agenesia of the retrohepatic inferior vena cava. The first symptoms of the disease were noticed in childhood. The increasing symptomatology led to propose, at the age of 30 years, first a percutaneous transluminal angioplasty which failed, because of the impossibility to recanalize the obstructed segment. Then a surgical procedure consisting of the implantation of ePTFE prosthesis between the right atria and the retrohepatic inferior vena cava was performed. The hepatic biopsy showed a centrolobular fibrosis and an old subglissonian infarction. The patient was improved, allowing him to recover a normal life. However, three years later, an angiographic evaluation performed because of a recurrence of a slight abdominal pain, showed a thrombosis of the bypass. An attempt at thrombolysis failed. Since the patient did not present major clinical and biological consequences we only proposed a surveillance and no endovascular procedure because of the fear of a pulmonary emboli. The purpose of this case report is to review the literature and discuss the etiopathology of congenital Budd-Chiari syndrome with regard to the different therapeutic options.
The aim of this study was to evaluate the effect of insulin on the release of vWf in vivo during an oral glucose tolerance test (OGTT) performed in normal, glucose-intolerant and diabetic subjects and in vitro on human endothelial cells. Twenty-eight subjects exhibiting risk factors for diabetes underwent an OGTT: 11 subjects proved to be normal, 7 were glucose-intolerant and 10 diabetic. In each group, the vWf and PAI-1 plasmatic levels were measured at t = 0, 30 min and 180 min after the beginning of the test. Human endothelial cells from non-diabetic and diabetic subjects were incubated in the presence of human insulin at various concentrations (0.25, 2.5, 25 and 250 mUI/ml). After 1, 4, and 24 hours of incubation, the release of vWf and endothelin 1 was measured in the cell supernatant and the intracellular amount of vWf in the cell lysate. During the OGTT, the vWf levels in plasma were not affected despite a 4.5-, 6-, and 2.5-fold increase in insulin levels in normal, glucose-intolerant and diabetic subjects, respectively. Although raised in all three groups, PAI-1 plasmatic levels remained constant during the test. After 24 hours of exposure to insulin (0.25 mU/ml), the release of vWf by endothelial cells reached 35.94 +/- 23.08 % of the basal value for non-diabetic subjects, and 27.57 +/- 10.05 % for diabetic patients. Similar results were observed in non-stimulated cells. Insulin had no influence on intracellular vWf content, which remained comparable to control values. Regardless of its concentration, insulin failed to stimulate the release of vWf by endothelial cells of non-diabetic and diabetic subjects, while its ability to stimulate the release of endothelin 1 was preserved. In conclusion, hyperinsulinemia had no adverse effect on circulating vWf in normal or diabetic subjects. Neither release nor intracellular vWf content in non-diabetic or diabetic endothelial cells was influenced by insulin in vitro.
PURPOSE: To analyze surface alterations and fractures observed in the nitinol stent wires of explanted endovascular grafts used for treatment of abdominal aortic aneurysm. METHODS: Twenty-one explanted Stentor devices and 1 Cragg stent were received from investigators in Germany and France. After macroscopy and photography, the explants were cleaned and the polyester coating removed. The frame was examined completely by stereomicroscopy, and irregularities were assayed by scanning electron microscopy and energy dispersive x-ray analysis (EDAX). The observed alterations were classified according to stereomicroscopic and electron microscopic morphology. RESULTS: The mean implantation interval for the endografts was 29.1 +/- 13.2 months (range 5-46). All examined explants, even those retrieved after only a few months in situ, showed pitlike surface damage 10-25 microm in diameter. Larger, irregularly shaped surface alterations were observed in approximately 70% of the explants. Older explants (age >32 months) presented vast regions of decay, with bending of the wire and stress cracks in some areas. EDAX examination revealed decreased nickel concentration in the corroded regions. CONCLUSIONS: Corrosion of the nitinol wire in endovascular grafts is confirmed. Presumably, the observed pitting and irregularly shaped corrosion defects are the precursors of material failure. They weaken the thin wire, which leads to stress cracks and eventually fracture of the stent wire under circulatory pulsation. Cell-induced electrochemical corrosion and active cellular destruction of surfaces are well-known mechanisms that must be investigated for their possible roles in the corrosion of stent metals.
The follow-up of 273 AAA patients operated 1981-1985 showed a mean dilation of polyester grafts of 17.4% in 12 days and 34.8% in 3 years. This early dilation is due to mesh expansion of the warp knitted grafts. It has no clinical relevance. In contrary the late dilation after approximately 10 years is due to degradation. The evaluation of 436 explanted grafts attained from 75 hospitals showed graft rupture to be the cause of the explanation for 42/255 (16%) polyester grafts and 2/42 (5%) PTFE grafts. The most ruptures were observed in the surrounding of the inguinal ligament after 10 to 20 years of duration. In comparison to modern endovascular grafts the conventional polyester and PTFE grafts still are the gold standard of durability.
The purpose of this study was to develop a sealing technique for polyester prosthetic grafts able to promote healing and reduce intimal hyperplasia. The porcine experimental model was aortoiliac bypass with a 6-mm diameter knitted polyester prosthetic graft implanted for 14 and 90 days. Animals were divided into three groups according to sealing technique as follows: pre-clotting with blood (group I, n = 12), sealing with autologous fibrin glue (group II, n = 14), and sealing with autologous fibrin glue and bone marrow cells (group III, n = 16). Feasibility and quality of sealing were evaluated by scanning electron microscopy prior to implantation and by assessment of blood loss. After removal, prostheses were cut into three segments comprising the proximal anastomosis, midsection, and distal anastomosis. Pieces were fixed, embedded in paraffin, and serially sectioned for histologic study. Histological study focused on the degree of stenosis and hyperplasia of the neointima of each prosthesis. The results of this short-term study indicate that sealing of polyester vascular prosthetic grafts with autologous fibrin glue and bone marrow cells is effective in reducing intimal hyperplasia. However further study will be needed to assess long-term healing.
PURPOSE: The purpose of this study was to assess the feasibility of insertion of endovascular stents and the precision of an open-field interventional magnetic resonance imaging (iMRI) system in an in vivo model. METHODS: A feasibility study was undertaken at a university-affiliated hospital. Three male piglets with an average age of 6 months and a weight between 70 and 77 kg and two 3-month-old male piglets that weighed 40 to 44 kg were anesthetized. The five piglets underwent placement of nitinol stents inserted through the right femoral artery, under the guidance of a SIGNA-SP 0. 5T open-configuration iMRI unit. With a dedicated high-resolution near-real-time MRI sequence, the stent was guided and deployed onto a predefined target. RESULTS: The main outcome measures were the duration of the procedure from the beginning of positioning to the end of deployment of the stent, the final position of the stent in relation to the target on the iMRI screen, and comparison with autopsy findings. Three stents were deployed within the aorta at the level of the renal arteries, and two were deployed within the right iliac artery just below the aortic trifurcation. The average duration of the endovascular deployment was 13 minutes. There was an agreement of 0.6 mm in the position of the stent as observed on iMR images and found at autopsy. When the piglets were sacrificed, the average distance between the stents and the predefined target was 7. 8 mm, mostly because of the migration of one stent. Axial views allowed for accurate determination of stent impaction on the vascular wall. CONCLUSIONS: This study confirms the feasibility of stent deployment under near-real-time MRI guidance. It also emphasizes some inherent characteristics that hold promise with regard to other conventional techniques: stents and vascular structures are visualized in near-real-time in any desired plane, and the technique is performed without the potential adverse effects of ionizing radiations and iodinated contrast agents.
UNLABELLED: Vascular grafts are available since the middle of the 50's. Explant retrieval studies still reveal not published material degradation today, after over 40 years of product development. Endovascular grafts exist since the beginning of the 90's. New developments and modifications have lead to numerous devices. The importance of explant retrieval studies grows. MATERIALS AND METHODS: Among 33 stentgrafts, retrieved 5 to 43 months after implantation, the majority were 18 MinTec devices (17 Stentor, 1 Cragg). These 18 explants were examined by endoscopy, stereomicroscopy and scanning electron microscopy. RESULTS: The following material degradation was observed. The textile coating showed holes along the longitudinal seam, the ligatures in-between the stentframes burst, allowing the frames to dislocate. Occasional fractures of the stent wire were seen accompanied by bowl-shaped alterations of the surface. CONCLUSION: The Stentor device is, since its modification 1996, not available any longer. It was one of the most applied devices world-wide. The possible material deficiencies must be known by those performing patient follow-up. The occurrence of alterations within 43 months shows the importance of a continued follow-up besides clinical trials.
Impregnated polyester arterial prostheses have gained wide acceptance by most vascular surgery teams, probably because these prostheses are easy to use, without any preclotting. We offer here a synthesis of the main studies that have appraised the experimental and clinical performance of these prostheses, and we delineate their major prospects.
OBJECTIVE: Adrenomedullin (ADM), secreted by the failing human heart, is a newly discovered potent endogenous vasorelaxing and natriuretic peptide that may play a role in cardiorenal regulation. No data are available on ADM in heart-transplant recipients (Htx) and the aim of this study was to determine the short- and long-term responses of ADM after heart transplantation. METHODS: Circulating ADM and its relationship with parameters of cardiovascular hemodynamics, humoral factors and renal function were determined in normal subjects and Htx early (1, 2, 4, 8, 15 and 30 days) and late (32 +/- 16 months) after transplantation. Additionally, ADM was obtained in matched hypertensive and renal-transplant patients (n = 9 in each group). RESULTS: Plasma ADM, elevated in heart failure patients, further increased transiently at day 1 after transplantation (from 37.9 +/- 15.9 to 125.8 +/- 15.3 pmol/l, P < 0.01) and, although decreasing thereafter, remained elevated until the 30th day after transplantation (52.1 +/- 25.2 pmol/l). Late after transplantation. ADM concentrations were still increased compared to normal values (31.3 +/- 5.3 vs. 19.4 +/- 2.7 pmol/l, P < 0.001). ADM positively correlated with endothelin, atrial natriuretic peptide (ANP) and cyclosporine. ADM was also correlated with increased diastolic (r = 0.68, P < 0.04) and systolic (r = 0.66, P < 0.05) blood pressure in late Htx. No relationship was observed between ADM and left ventricular mass index, aldosterone and creatinine. ADM elevation was similar in hypertensive, renal-transplant patients and in Htx. CONCLUSIONS: Circulating ADM is increased after heart transplantation, in relation to hypertension, endothelin, cyclosporine and ANP. In view of ADM's biological properties, these results might suggest a compensatory role for ADM against further development of vasoconstriction and fluid retention states after heart transplantation.
A 7 cm diameter tumor of the left atrium is reported in a 78 year-old woman with a past history of pT3N1M0 colonic adenocarcinoma. The histological examination of the atrial tumor disclosed areas of highly vascularized myxoid stroma with cells strongly reactive for vimentin. Multiple mucoid spaces lined by a single layer of goblet cells were scattered among those typical areas of myxoma. No nuclear atypia was observed. Cytoplasm of the glandular cells was immunoreactive for epithelial antisera (keratin, EMA), CEA and CA19.9. Two years later, the patient was doing well, with no local recurrence of the cardiac myxoma and no secondary location of the colonic adenocarcinoma. The histological characteristics, the absence of atypia, the absence of tumoral extension or neoplastic lymphatic vascular thrombi in the pedicle or in the interatrial septum, and the finding of typical myxomatous areas supported the diagnosis of cardiac myxoma with glandular component. To our knowledge, 21 cases of myxoma with glandular mucinous component, focal or prominent, have been previously published in the literature. These myxoma were generally sporadic cases with the same clinical features and prognosis as typical myxoma. Immunoreactivity of these glandular structures was constant for epithelial markers. The positive immunostaining by CEA, and by CA19.9 in our case, reflects the histogenetic endodermal origin.
OBJECTIVES: To understand the cause, and propose a mechanism for frame dislocation in endovascular grafts. MATERIALS AND METHODS: Five tube grafts were explanted due to secondary distal leakage 15-21 months after operation. One bifurcated graft was removed during emergency operation after aortic rupture caused by secondary leakage. A second bifurcated graft was harvested from a patient with thrombotic occlusion of one limb, who died after transurethral prostatic resection. The inside of the grafts were examined endoscopically. The stent was inspected after removal of the fabric, broken ligatures were counted and examined by scanning electron microscopy. The fabric strength was tested by probe puncture. RESULTS: We found 17-44% of the stent ligatures of the body middle rings to be loose. The knots were intact. Degradation of the polyester textile was not observed. CONCLUSIONS: Continuous movements in the grafted aorta and blood pressure impose permanent stress to the stent frame and the polyester fabric resulting in morphological changes in the body middle ring of grafts. The clinical implications of the suture breakages are unknown although they may be related to distal secondary leakage in tube grafts.
OBJECTIVES: to evaluate an alternative and simple technique which consists in impregnation of a synthetic prosthesis with either autogenic omental fat or bone marrow. These tissues have been selected based on previous works and because they contain multiple cellular and extracellular compounds with biological healing properties (i.e. angiogenesis, endothelialisation, etc.). DESIGN: PTFE grafts of Group 1 were impregnated with fatty tissue, those of Group 2 with bone marrow and those of Group 3 served as controls. MATERIALS: nine mongrel dogs divided among these three groups. PTFE grafts are 3 mm in diameter. METHODS: in each animal, both iliac arteries were submitted to an end-to-side ilio-iliac bypass. At 3 months, pathology assessment was performed. RESULTS: group 1: all grafts were thrombosed and intimal hyperplasia was found occluding the anastomotic sites. Group 2: 4/6 grafts were patent and their mid-portion presented a thin neointima which did not totally cover the anastomotic sites. Group 3: 2/5 grafts were patent and their mid-portion as well as the anastomotic sites were covered with neointima which was hyperplastic in some areas. CONCLUSIONS: addition of bone marrow cells may contribute to improve the quality of the healing process.