In vivo performance of two different hydroxyapatite coatings on titanium prepared by discharging in electrolytes.

This study reports a discharging method for bone-like carbonated HA (cHA)-coating (Ca/P 1.71) and stoichiometric HA (sHA)-coating (Ca/P 1.67) with micrometer order thicknesses on titanium plates, using modified body fluid and acidic calcium phosphate solutions, respectively. In vivo histological performance of the HA coatings prepared by discharging in electrolytes was evaluated. Bone-contact indexes of HA coatings were measured microscopically. Additionally, bone-coating interface was analyzed by scanning electron microscopy and the use of an electron probe microanalyzer. Results demonstrated that there was no significant difference in contact index between HA coatings. However, the cHA coating was practically replaced by immature bone, and the titanium metal substrate was directly connected to the bone structure whereas the sHA coating layer remained and was partially detached from the titanium metal substrate. Since detached coating particles are pathogens, and can cause peri-implantitis, the cHA coating was more favorable than the sHA coating even if contact index was equivalent to that of the sHA coating. It is thought that coating thickness and chemical composition of coatings are important for biological stability of implants. In conclusion, since bone-like thin cHA coating showed high osteoconductivity and bone replacement, bone-like HA is superior to sHA coating for use in dental implants.

Coated Materials, Biocompatible↗

PubMed2006

Preliminary beta-tricalcium phosphate coating prepared by discharging in a modified body fluid enhances collagen immobilization onto titanium.

Because of its excellent scaffold properties toward bone cells, collagen has been recognized as a promising extracellular matrix protein for surface modification of titanium implants. Hydroxyapatite (HA) coatings have been investigated as a preliminary coating for collagen immobilization on titanium implants. However, the composition of HA-collagen is recognized as being difficult, and while many studies have suggested that biodegradable beta-tricalcium phosphate (beta-TCP) has better osteoconductivity than HA, the efficiency of preliminary beta-TCP coating for collagen immobilization on titanium surfaces has yet to be evaluated. This investigation aimed to evaluate the applicability of HA and beta-TCP coatings, prepared by discharging in modified body fluids, as preliminary collagen coatings. To increase collagen induction on preliminary HA and beta-TCP coatings, we used a new cathodic polarization method. X-ray photoelectron spectroscopy revealed that the bonding strength between the collagen NH(+) amino groups of collagen and phosphate (PO(4) (3-)) was greater on the beta-TCP coating than the HA coating. The preliminary beta-TCP coating was tightly crosslinked with RCOO(-) carboxyl groups of the collagen molecules and showed high cellular responses, even in the early stage of cell cultivation. Thus, this coating was found to be more effective than HA as a preliminary coating for collagen immobilization on titanium implants.

Animals↗

PubMed2004

Glow discharge plasma pretreatment enhances osteoclast differentiation and survival on titanium plates.

Despite the fact that several reports have demonstrated osteoclast activity on various bioactive ceramics, osteoclast functions on surface-modified titanium have not come under focus. This study aimed to examine whether the increasing surface energy of glow discharge plasma (GDP) involved in protein adhesion containing the RGD (Arg-Gly-Asp) sequence affects osteoclast responses on titanium plates. We examined osteoclast differentiation and survival rates on titanium plates with and without GDP. The amounts of osteoclasts on titanium plates were not increased by GDP after 1 week. However, osteoclast differentiation was greatly activated by GDP pretreatment, as tartrate-resistant acid phosphatase synthesis significantly increased on the titanium plates with GDP. Additionally, since the presence of osteoclasts was detected only on the titanium plates with GDP, even after 4h cultivation in a coculture test, the osteoclasts survival rate was increased by GDP pretreatment. As osteoclast responses were affected even on surface modified metallic materials, we concluded that novel approaches are needed not only for osteoclastic resorption on ceramic materials but also for osteoclast responses on surface-modified metallic materials.

Acid Phosphatase↗

PubMedDate not supplied

Glow discharge plasma treatment of titanium plates enhances adhesion of osteoblast-like cells to the plates through the integrin-mediated mechanism.

PURPOSE: Initial adhesion of cells to implant surfaces and subsequent behavior of the cells are important determinants for biocompatibility of the implants. It was previously reported that both adhesion of MC3T3-E1 osteoblast-ike cells to titanium (Ti) plates and their differentiation into more mature cells on the plates were stimulated by treatment of the plates with glow discharge plasma (GDP). However, the mechanisms of these processes have not yet been identified. In this study, the adhesion and differentiation mechanism of osteoblast-like cells to Ti with and without GDP were investigated. MATERIALS AND METHODS: The adhesion and differentiation mechanism of MC3T3-E1 osteoblast-like cells to Ti, with and without GDP, were investigated by cultivation in serum-free medium and use of a competitive inhibition test to examine the influence of extracellular matrix proteins contained in the serum and to identify cell binding proteins. In addition, the amount of fibronectin adsorption on each Ti plate was investigated by enzyme-linked immunosorbent assay and fluorescein isothiocyanate labeling. Furthermore, the stress fiber formation and morphology of cells on each plate were evaluated microscopically. RESULTS: Adherent cells on Ti plates, with and without GDP, were significantly reduced in serum-free conditions and the presence of RGDS (Arg-Gly-Asp-Ser) peptides. Fibronectin adsorption on titanium plates was increased by GDP. Furthermore, stress fiber formation of cells was extremely progressive on the Ti plates treated with GDP and was not observed on the cells inhibited by RGDS peptide. DISCUSSION: These results suggest that RGDS containing serum proteins have a major role in regulating specific adhesion of cells to Ti, and GDP promoted cell adhesion and differentiation on Ti by increasing the adsorption of proteins. CONCLUSION: According to this study, the adhesion and differentiation mechanism of osteoblast-like cells to Ti, with and without GDP, can be obtained.

Argon↗

PubMedDate not supplied

Hydroxyapatite coating on a titanium metal substrate by a discharging method in modified artificial body fluid.

PURPOSE: The aim of this study was to evaluate the formation of a hydroxyapatite coating on titanium plate by discharging in typical and modified artificial body fluids. MATERIALS AND METHODS: Japanese Industrial Standard Grade 2 titanium plates were used as specimens. Discharging was performed on the specimens in each solution, and the surface topography of each coating was observed with a scanning electron microscope. The Ca/P atomic ratio and surface characterization of each coating were evaluated by x-ray photoelectron spectroscopy, and crystal phases of each coating were analyzed by Fourier transform infrared spectroscopy and x-ray diffraction. RESULTS: Tricalcium phosphate formed on the titanium surface in a 1.5 Ca/P solution with high ion concentrations of calcium (2.5 mmol/L) and phosphorous (1.67 mmol/L). Crystalline HA was formed on the titanium surface in a 1.5 Ca/P solution (Hanks' balanced salt solution without organic molecules) with low ion concentrations of calcium (1.26 mmol/L) and phosphorus (0.83 mmol/L). DISCUSSION: A solution containing organic pH buffer was insufficient to form stable coatings on the titanium surface. Coating properties strongly depended on the Ca/P chemical ratio of the applied solution. A Ca/P ratio of 1.5 was appropriate for preparing a calcium phosphate coating on a titanium surface, whereas a Ca/P ratio of 2.5 was excessively high. CONCLUSION: These findings suggest that Hanks' balanced salt solution without organic molecules is the most suitable solution for forming crystalline hydroxyapatite coatings on titanium surfaces by the discharging method.

Body Fluids↗

PubMedDate not supplied

Functionally gradient bonelike hydroxyapatite coating on a titanium metal substrate created by a discharging method in HBSS without organic molecules.

PURPOSE: This study evaluated the quality of coatings on titanium surfaces prepared by discharging in Hanks' balanced salt solution without organic molecules (HBSS-). MATERIALS AND METHODS: 10 x 10 x 1.0-mm titanium plates were used as cathodes of a coating device developed in the laboratory and immersed in HBSS-. A piece of platinum foil was used as a counterelectrode. Discharging was maintained at 1 A and 10 V (416 mA/cm2) for periods of 90, 270, and 540 seconds. Crystal phases of the coatings were identified by x-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). In addition, the surface characterization and Ca/P atomic ratio of the titanium surfaces were determined by x-ray photoelectron spectroscopy (XPS). Furthermore, the surface topography, the thickness of the coatings, and the bonds between coatings and titanium substrates were observed by scanning electron microscopy. RESULTS: The FTIR and XRD studies demonstrated that the deposits on the titanium after 540 seconds of discharging were crystalline hydroxyapatite. In addition, the thickness of the titanium suboxide layer increased during discharging. The XPS studies indicated that after 540 seconds of processing, the mean Ca/P ratio of the coatings on the titanium was 1.71, which is similar to that of human bone. DISCUSSION: In addition, the replacement of sodium ions with calcium ions seemed important for the promotion of crystallization of the coating. Furthermore, the XPS studies demonstrated that the coatings had a gradient function. Scanning electron microscopy showed that adhesion between coatings and the titanium substrate was close. The coatings were approximately 1 microm thick. CONCLUSION: These findings suggest that a very thin crystalline bonelike hydroxyapatite coating with a gradient function could be prepared on a titanium metal substrate in HBSS- by a discharging method.