An evaluation of elastomeric impression materials based on surface compressive strength.

K Omori·H Arikawa·K Inoue
View original source ↗Export metadata ↓

Abstract

The setting times of seven commercially available elastomeric impression materials were determined using Wilson's reciprocating rheometer at temperatures 23 +/- 0.5 or 32 +/- 0.5 degrees C. The surface compressive strength and depression of these materials after setting time were measured using a rheometer (Fudoh). Each material was mixed according to the mixing proportion (base/accelerator or catalyst ratio) recommended by the manufacturer. The surface compressive strength and the depression of each material were measured by using a method which pressed the material to the edge of a sensitive rod (2.0 mm in diameter) connected to a load cell. In the case of silicone impression materials (additional type) at a temperature of 23 +/- 0.5 degrees C, the surface compressive strength and the depression of these materials were extremely stable after the setting time. However, the surface compressive strength of other materials except additional type materials increased markedly after setting time and the depression corresponding to the surface compressive strength decreased. These increased largely with the increase, in pressing speed to the sensitive rod. At 450 s from the setting time of all materials, there was an adequate correlation (r = 0.84) between measured values and theoretical values derived using the theory of elasticity.

Explore related subjects

Compressive StrengthDental Impression MaterialsElasticityElastomersEthersMaterials TestingRheologySiliconesSulfidesSurface PropertiesTime FactorsComparative StudyJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

K Omori, H Arikawa, K Inoue. 2001. An evaluation of elastomeric impression materials based on surface compressive strength.. https://doi.org/10.1046/j.1365-2842.2001.00660.x

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Depth-dependent mechanical properties of enamel by nanoindentation.

Nanoindentation has recently emerged to be the primary method to study the mechanical behavior and reliability of human enamel. Its hardness and elastic modulus were generally reported as average values with standard deviations that were calculated from the results of multiple nanoindentation testing. In such an approach, it is assumed that the mechanical properties of human enamel are constant, independent of testing parameters, like indent depth and loading rate. However, little is known if they affect the measurements. In this study, we investigated the dependence of the hardness and elastic modulus of human enamel on the indent depth. We found that in a depth range from 100 to 2000 nm the elastic moduli continuously decreased from approximately 104 to 70 GPa, and the hardnesses decreased from approximately 5.7 to 3.6 GPa. We then considered human enamel as a fiber-reinforced composite, and used the celebrated rule of mixture theory to quantify the upper and lower bounds of the elastic moduli, which were shown to cover the values measured in the current study and previous studies. Accordingly, we attributed the depth dependence of the hardness and modulus to the continuous microstructure evolution induced by the nanoindenter tip.

Compressive Strength↗
PubMed2007

Mechanical loading of rigid intramuscular implants.

Several groups are developing different versions of a new class of leadless, permanently implanted electronic devices with a size and form factor that allows them to be injected into muscles (BIONs). Their circuitry is protected from body fluids by thin-walled hermetic capsules made from rigid and brittle materials (glass or ceramic) that include feedthroughs to their electrodes. These packages experience repetitive stresses from the very contractions that they excite. We here provide a worst-case analysis of such stresses and methods for testing and validation of devices intended for such usage, along with the failure analysis and remediation strategy for a design that experienced unanticipated failures in vivo.

Compressive Strength↗
PubMed2006

Physiologically based boundary conditions in finite element modelling.

Finite element analysis has been used extensively in the study of bone loading and implant performance, such as in the femur. The boundary conditions applied vary widely, generally producing excessive femoral deformation, and although it has been shown that the muscle forces influence femoral deflections and loading, little consideration has been given to the displacement constraints. It is hypothesised that careful application of physiologically based constraints can produce physiological deformation, and therefore straining, of the femur. Joint contact forces and a complete set of muscle forces were calculated based on the geometry of the Standardised Femur using previously validated musculoskeletal models. Five boundary condition cases were applied to a finite element model of the Standardised Femur: (A) diaphyseally constrained with hip contact and abductor forces; (B) case A plus vasti forces; (C) case A with complete set of muscle forces; (D) distally constrained with all muscle forces; (E) physiological constraints with all muscle forces. It was seen that only the physiological boundary conditions, case E, produced physiological deflections (< 2.0mm) of the femoral head in both the coronal and sagittal planes, which resulted in minimal reaction forces at the constrained nodes. Strains in the mid-diaphysis varied by up to 600 micro-strain under walking loads and 1000 micro-strain under stair climbing loads. The mode of loading, as indicated by the strain profiles on the cortex also varied substantially under these boundary conditions, which has important consequences for studies that examine localised bone loading such as fracture or bone remodelling simulations.

Compressive Strength↗