Fractured surface characterization: wet versus dry bonding.

M Hashimoto·H Ohno·M Kaga·H Sano·K Endo·H Oguchi
View original source ↗Export metadata ↓

Abstract

OBJECTIVE: Fractographic analysis was conducted to evaluate the resin-dentin bond structures made under wet and dry conditions. METHODS: Resin-dentin bonded specimens were prepared using two adhesive resin systems (Single Bond/SB; 3M and All Bond 2/AB2; Bisco Inc) under wet and dry conditions. The specimens were sectioned perpendicular to the adhesive interface to produce a square bar-shaped specimen (adhesive area: 0.9 mm(2)) by means of a diamond saw. The mean bond tensile test was then conducted at a crosshead speed of 1.0 mm/min. The mean bond strengths were statistically compared with two-way ANOVA and Fisher's PLSD test (p<0.05). Subsequently, the fractured surfaces of all specimens were examined using SEM and the area fractions of failure modes (%) were measured using an image analyzer on SEM microphotographs. RESULTS: No significant differences in tensile-bond strength were observed between SB (60.1+/-16.4MPa) and AB2 (69.8+/-17.4MPa) (p>0.05) under wet conditions. However, the bond strength either of SB or AB2 made under wet conditions was significantly greater than those made under dry conditions (SB: 26.2+/-12.5MPa and AB2: 6.8+/-3.3MPa) (p<0.05). Under fractographic analysis, the major portion at the fractured surface was occupied by the cohesive failure of bonding resin and the resin composite for the wet conditions, and the top of the hybrid layer for the dry conditions in both systems. SIGNIFICANCE: The interaction between the top of the hybrid layer and the bonding resin influenced the bond integrity.

Explore related subjects

AdhesivenessAnalysis of VarianceBisphenol A-Glycidyl MethacrylateComposite ResinsDental BondingDentinDentin-Bonding AgentsHumansImage Processing, Computer-AssistedMaterials TestingMethacrylatesMicroscopy, Electron, ScanningStatistics as TopicStress, MechanicalSurface PropertiesTensile StrengthWaterJournal ArticleResearch Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

M Hashimoto, H Ohno, M Kaga, H Sano, K Endo, H Oguchi. 2002. Fractured surface characterization: wet versus dry bonding.. https://doi.org/10.1016/s0109-5641(01)00023-9

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Effect of capillary condensation on friction force and adhesion.

Friction force measurements have been conducted with a colloid probe on mica and silica (both hydrophilic and hydrophobized) after long (24 h) exposure to high-humidity air. Adhesion and friction measurements have also been performed on cellulose substrates. The long exposure to high humidity led to a large hysteresis between loading and unloading in the friction measurements with separation occurring at large negative applied loads. The large hysteresis in the friction-load relationship is attributed to a contact area hysteresis of the capillary condensate which built up during loading and did not evaporate during the unloading regime. The magnitude of the friction force varied dramatically between substrates and was lowest on the mica substrate and highest on the hydrophilic silica substrate, with the hydrophobized silica and cellulose being intermediate. The adhesion due to capillary forces on cellulose was small compared to that on the other substrates, due to the greater roughness of these surfaces.

Adhesiveness↗
PubMed2007

Evaluation of bond strength of soft relining materials to denture base polymers.

OBJECTIVES: To evaluate the initial bonding properties of recently and previously introduced soft relining materials to denture base polymers with different polymerization techniques and different water content. METHODS: The initial tensile bond strength of 10 soft liners (Mollosil Plus, Dentusil, Ufi gel Soft, GC Reline Soft, Silagum Comfort, Vertex Soft, Astron Soft, Molloplast B, Flexacryl Soft, Triad Resiline) to three denture base polymers (Paladon 65, Palapress Vario, Ivocap Plus) were assessed with a modified method. Paladon 65 specimens immersed in water for 3 months were also used to test the effect of water content of denture base polymer on bond strength results. After testing, a visual examination of the fracture surfaces and a SEM investigation of the interface structure were performed. Tensile strength of each soft liner material was also tested. Data were analyzed statistically by two-way ANOVA (alpha = 0.05). RESULTS: Significant differences were found among tensile bond strength results (P < 0.05). Vinyl poly(organosiloxane) soft liners (Mollosil Plus, Dentusil, Ufi gel Soft, GC Reline Soft, Silagum Comfort) and a plasticized PMMA soft liner (Vertex Soft) gave statistically similar bond strength results for different denture base polymers (P>0.05). For the other materials used (Astron Soft, Molloplast B, Flexacryl Soft, Triad Resiline), different denture base polymers caused significantly different results (P < 0.05). Poly(organosiloxane) based materials gave slightly higher bond strength results with water immersed specimens than with the dry specimens. SIGNIFICANCE: A wide variety of newly formulated soft liners used in this study gave comparable or better bond strength results compared to Molloplast B.

Adhesiveness↗
PubMed2007

Flat and sigmoidally curved contact zones in vesicle-vesicle adhesion.

Using the membrane-bending elasticity theory and a simple effective model of adhesion, we study the morphology of lipid vesicle doublets. In the weak adhesion regime, we find flat-contact axisymmetric doublets, whereas at large adhesion strengths, the vesicle aggregates are nonaxisymmetric and characterized by a sigmoidally curved, S-shaped contact zone with a single invagination and a complementary evagination on each vesicle. The sigmoid-contact doublets agree very well with the experimentally observed shapes of erythrocyte aggregates. Our results show that in identical vesicles with large to moderate surface-to-volume ratio, the sigmoid-contact shape is the only bound morphology. We also discuss the role of sigmoid contacts in the formation of multicellular aggregates such as erythrocyte rouleaux.

Adhesiveness↗