PubMed · 12867364
The source did not provide an abstract. Follow the original record for more information.
Explore connections, maps & timelines
Julian D Perry. 2003. Hydroxyapatite implants.. https://doi.org/10.1016/s0161-6420(03)00656-0
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
Novel gold/poly-(1,3-divinyl-imidazolid-2-one)/silica [poly-bisvinylethyleneurea (poly-BVU)/silica)] hybrid particles have been produced by adsorption and spontaneously occurring in situ reduction of Au(3+) cations on the surface of poly-BVU/silica hybrid particles. The successful functionalization of the poly-BVU/silica particles with gold nanoclusters has been evidenced by UV/vis and XPS spectroscopy as well as scanning electron microscopy. The size of the resulting gold clusters, estimated by means of the Mie-Drude theory on the full peak width at half-maximum of the surface plasmon UV/vis absorbance, correlates with the polymer content of the poly-BVU/silica hybrid particles used for the modification. Therefore, it is possible to control the size of the gold clusters simply by adjusting the monomer/silica ratio in the polymerization process, which corresponds with the polymer content of the hybrids.
Biodegradable networks of poly(propylene fumarate) (PPF) and the crosslinking reagent poly(propylene fumarate)-diacrylate (PPF-DA) were prepared with thermal- and photo-initiator systems. Thermal-crosslinking was performed with benzoyl peroxide (BP), which is accelerated by N,N-dimethyl-p-toluidine (DMT) and enables injection and in situ polymerization. Photo-crosslinking was accomplished with bis(2,4,6-trimethylbenzoyl) phenylphosphine oxide (BAPO), which is activated by long-wavelength UV light and facilitates material processing with rapid manufacturing techniques, such as stereolithography. Networks were evaluated to assess the effects of the initiators and the PPF/PPF-DA double bond ratio on the mechanical properties. Regardless of the initiator system, the compressive properties of the PPF/PPF-DA networks increased as the double bond ratio decreased from 2 to 0.5. BAPO/UV-initiated networks were significantly stronger than those formed with BP/DMT. The compressive modulus of the photo- and thermal-crosslinked PPF/PPF-DA networks ranged from 310 +/- 25 to 1270 +/- 286 MPa and 75 +/- 8 to 332 +/- 89 MPa, respectively. The corresponding fracture strengths varied from 58 +/- 7 to 129 +/- 17 MPa and 31 +/- 13 to 105 +/- 12 MPa. The mechanical properties were not affected by the initiator concentration. Characterization of the network structures indicated that BAPO was a more efficient initiator for the crosslinking of PPF/PPF-DA, achieving a higher double bond conversion and crosslinking density than its BP counterpart. Estimated average molecular weights between crosslinks (Mc) confirmed the effects of the initiators and PPF/PPF-DA double bond ratio on the mechanical properties. This work demonstrates the capability to control the properties of PPF/PPF-DA networks as well as their versatility to be used as an injectable material or a prefabricated implant.
The electrical stability of a novel polypyrrole (PPy)/poly(D,L-lactide) (PDLLA) composite was studied in vitro and compared with that of PPy-coated polyester fabrics. Specimens were incubated in Ringer's solution at 37 degrees C for up to 8 weeks with or without the circulation of DC current under a constant 100 mV voltage. In situ current variation with incubation time was recorded. The AC volume electrical conductivity of the specimens before and after incubation in phosphate-buffered saline was recorded using a frequency analyzer. Water absorption and weight loss were monitored metrologically. Changes in the oxidation state of incubated PPy were analyzed with X-ray photoelectron spectroscopy. The morphological changes were observed with scanning electron microscopy, and the glass transition temperature of the PDLLA was investigated using differential scanning calorimetry. The PPy/PDLLA composite in Ringer's solution sustained a relatively stable conductivity up to 8 weeks after an initial period of "conditioning." The PPy-coated fabrics experienced a rapid loss of conductivity when subjected to electrical circulation and regained part of it when disconnected. The volume conductivity of the nonincubated PPy/PDLLA membrane behaved as a typical conductor in the low-frequency range. The mechanisms involved in the various electrical behaviours of the PPy/PDLLA composite and PPy-coated fabrics are discussed. In conclusion, the PPy/PDLLA composite was able to deliver a biologically significant electrical current in a simulated biological solution for up to 8 weeks and therefore may be considered as a first-generation synthetic biodegradable bioconductor.