[Diffractometric analysis of non-pulverized coherent materials].

G Maddalon; E Occella

PubMed · 1334214

[Diffractometric analysis of non-pulverized coherent materials].

Abstract

The paper presents an initial series of results of diffractometric assays, carried out by directing an X-ray beam on glossy sections of coherent, rigid materials (asbestos-cement blocks, insulation panels, ceramic tiles). The study, which is an introduction to another concerning crystalline rocks, is aimed at assessing the possibility of increasing the diffracted intensities, using samples with high mass concentration, avoiding the consequences of loss of crystallinity following extremely fine grinding, which is considerable especially when compounds having very different mechanical resistance and elastic modulus are simultaneously present. The assays carried out demonstrated the validity of the method for qualitative analysis, whereas in quantitative terms the diffracted intensities were mainly increased (up to 40%), but not in a manner directly connected with the type and macro- and microscopic structure of the compounds under study. Thus, the method guarantees an effective increase in sensitivity only in certain cases.

Explore related subjects

Aluminum Silicates Asbestos Asbestos, Crocidolite Asbestos, Serpentine Calcium Carbonate Construction Materials Ferrous Compounds Powders Quartz X-Ray Diffraction Comparative Study Journal Article

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

G Maddalon, E Occella. [Diffractometric analysis of non-pulverized coherent materials].. https://pubmed.ncbi.nlm.nih.gov/1334214/

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Concentrations of polychlorinated dibenzo-p-dioxins in processed ball clay from the United States.

Processed ball clays commonly used by the ceramic art industry in the United States were collected from retail suppliers and analyzed for the presence and concentration of the 2,3,7,8-Cl substituted polychlorinated dibenzo-p-dioxins and dibenzofurans (PCDDs/PCDFs). The average PCDD toxic equivalent (TEQ) concentrations of these processed ball clays was approximately 800 pg/g (TEQ-WHO) with characteristic congener profiles and isomer distributions similar to patterns of previously analyzed raw and processed ball clays. The PCDF concentrations were below the average limit of detection (LOD) of 0.5 pg/g. Correlation analyses reveal no significant relationship between total organic carbon (TOC) and either individual, homologues, and total tetra-through octa-chlorinated PCDD congeners, or TEQ concentrations of the processed ball clays. The results are consistent with earlier studies on levels of PCDDs in ball clays. Data from earlier studies indicated that dioxins may be released to the environment during the processing of raw clay or the firing process used in commercial ceramic facilities. The presence of dioxin in the clays also raises concerns about potential occupational exposure for individuals involved in the mining/processing of ball clay, ceramics manufacturing and ceramic artwork.

Aluminum Silicates↗

PubMed2007

Dynamics of interactions involving deformable drops: hydrodynamic dimpling under attractive and repulsive electrical double layer interactions.

A model developed previously to analyze force measurements between two deformable droplets in the atomic force microscope [Langmuir 2005, 21, 2912-2922] is used to model the drainage of an aqueous film between a mica plate and a deformable mercury drop for both repulsive and attractive electrical double-layer interactions between the mica and the mercury. The predictions of the model are compared with previously published data [Faraday Discuss. 2003, 123, 193-206] on the evolution of the aqueous film whose thickness has been measured with subnanometer precision. Excellent agreement is found between theoretical results and experimental data. This supports the assumptions made in the model which include no-slip boundary conditions at both interfaces. Furthermore, the successful fit attests to the utility of the model as a tool to explore details of the drainage mechanisms of nanometer-thick films in which fluid flow, surface deformations, and colloidal forces are all involved. One interesting result is that the model can predict the time at which the aqueous film collapses when attractive mica-mercury forces are present without the need to invoke capillary waves or other local instabilities of the mercury/electrolyte interface.

Aluminum Silicates↗

PubMed2007

Biological evaluation of an apatite-mullite glass-ceramic produced via selective laser sintering.

The biological performance of a porous apatite-mullite glass-ceramic, manufactured via a selective laser sintering (SLS) method, was evaluated to determine its potential as a bone replacement material. Direct contact and extract assays were used to assess the cytotoxicity of the material. A pilot animal study, implanting the material into rabbit tibiae for 4 weeks, was also carried out to assess in vivo bioactivity. The material produced by SLS did not show any acute cytotoxic effects by either contact or extract methods. There was no evidence of an apatite layer forming on the surface of the material when soaked in SBF for 30 days, suggesting that the material was unlikely to exhibit bioactive behaviour in vivo. It is hypothesized that the material was unable to form an apatite layer in SBF due to the fact that this glass-ceramic was highly crystalline and the fluorapatite crystal phase was relatively stable in SBF, as were the two aluminosilicate crystal phases. There was thus no release of calcium and phosphorus and no formation of silanol groups to trigger apatite deposition from solution within the test time period. Following implantation in rabbit tibiae for 4 weeks, bone was seen to have grown into the porous structure of the laser-sintered parts, and appeared to be very close to, or directly contacting, the material surface. This result may reflect the local environment in vivo compared to that artificially found with the in vitro SBF test and, furthermore, confirms previous in vivo data on these glass-ceramics.

Aluminum Silicates↗