PubMed · 14689493

Deproteinizing effects on resin-tooth bond structures.

Eiji Yoshida·Masanori Hashimoto·Minoru Hori·Masayuki Kaga·Hidehiko Sano·Haruhisa Oguchi
View original source ↗Export metadata ↓

Abstract

This study investigated the effects of NaOCl on resin-tooth bonds to simulate the situations of long-term durability and caries invasion. Resin-tooth bonded specimens were produced with the use of two resin adhesives (Excite and One-Bond). Resin-tooth bonded beams (adhesive area; 0.9 mm2) were serially sectioned and the specimens were immersed in 10% NaOCl medium for 0 (control), 2, 4, and 6 h after being stored in water for 24 h. After immersion, microtensile bond tests were performed. SEM fractography was conducted to calculate each failure mode by image analysis. In addition, the adhesive interface was examined with the use of TEM. In the control specimens, enamel bond strengths had no difference between Excite (45.6 +/- 15.0) and One-Bond (56.9 +/- 12.9). On the other hand, dentin bond strengths had significant difference between Excite (80.6 +/- 21.2) and One-Bond (50.7 +/- 11.2). The bond strengths decreased with increased storage time for both systems with enamel and dentin bonds. The deteriorated mineralized dentin of beams resulted in bond-strength reduction for resin-enamel bonds. For dentin bonding, the adhesive interface was gradually dissolved from the outer to the center portion of the beam. The depletion of collagen fibrils within the demineralized dentin or hybrid layer deformation was found under SEM and TEM examinations. These morphological changes are responsible for bond strength reduction of resin-dentin bonds.

Explore related subjects

Dental MaterialsHumansMicroscopy, Electron, ScanningProteinsSodium CompoundsTime FactorsToothJournal ArticleResearch Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Eiji Yoshida, Masanori Hashimoto, Minoru Hori, Masayuki Kaga, Hidehiko Sano, Haruhisa Oguchi. 2004-01-15. Deproteinizing effects on resin-tooth bond structures.. https://doi.org/10.1002/jbm.b.10080

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Interphase effects in dental nanocomposites investigated by small-angle neutron scattering.

Small-angle and ultrasmall-angle neutron scattering (SANS and USANS) were used to characterize silica nanoparticle dispersion morphologies and the interphase in thermoset dimethacrylate polymer nanocomposites. Silica nanoparticle fillers were silanized with varying mass ratios of 3-methacryloxypropyltrimethoxysilane (MPTMS), a silane that interacts with the matrix through covalent and H-bonding, and n-octyltrimethoxysilane (OTMS), a silane that interacts through weak dispersion forces. Interphases with high OTMS mass fractions were found to be fractally rough with fractal dimensions, D(s), between 2.19 and 2.49. This roughness was associated with poor interfacial adhesion and inferior mechanical properties. Mean interparticle distances calculated for composites containing 10 mass % and 25 mass % silica suggest that the nanoparticles treated with more MPTMS than OTMS may be better dispersed than OTMS-rich nanoparticles. The results indicate that the covalent bonding and H-bonding of MPTMS-rich nanoparticles with the matrix are necessary for preparing well-dispersed nanocomposites. In addition, interphases containing equal masses of MPTMS and OTMS may yield composites with overall optimal properties. Finally, the combined SANS/USANS data could distinguish the differences, as a function of silane chemistry, in the nanoparticle/silane and silane/matrix interfaces that affect the overall mechanical properties of the composites.

Dental Materials↗
PubMed2007

Size control of silica nanoparticles and their surface treatment for fabrication of dental nanocomposites.

Nearly monodispersed silica nanoparticles having a controlled size from 5 to 450 nm were synthesized via a sol-gel process, and then the optimum conditions for the surface treatment of the synthesized silica nanoparticles with a silane coupling agent (i.e., 3-methacryloxypropyltrimethoxysilane (gamma-MPS)) were explored to produce dental composites exhibiting enhanced adhesion and dispersion of silica nanoparticles in the resin matrix. The particle size was increased by increasing amounts of the catalyst (NH4OH) and silica precursor (tetraethylorthosilicate, TEOS) and by decreasing the amount of water in the reaction mixtures regardless of solvents used for the synthesis. The particle size prepared by using ethanol as a solvent was significantly larger than that prepared by using methanol as a solvent when the composition of the reaction mixture was fixed. The nanosized particles in the 5-25 nm range were aggregated. The amount of grafted gamma-MPS on the surface of the synthesized silica nanoparticles was dependent on the composition of the reaction mixture when an excess amount of gamma-MPS was used. When surface treatment was performed at optimum conditions found here, the amount of the grafted gamma-MPS per unit surface area of the silica nanoparticles was nearly the same regardless of the particle size. Dispersion of the silica particles in the resin matrix and interfacial adhesion between silica particles and resin matrix were enhanced when surface treated silica nanoparticles were used for preparing dental nanocomposites.

Dental Materials↗