Corrosion on spinal implants.

John S Kirkpatrick·Ramakrishna Venugopalan·Preston Beck·Jack Lemons
View original source ↗Export metadata ↓

Abstract

OBJECTIVE: Modular spine implants are used as an aid to obtaining fusion, but fretting and corrosion occur between modular components in a biologic environment. METHODS: Forty-eight spinal implant constructs manufactured by a variety of companies were retrieved from 47 patients and were subjected to surface analysis stereomicroscopy. RESULTS: Stainless-steel implants (n = 23) had either semirigid constructs with mild or no surface alteration (n = 7) or rigid constructs with moderate or severe alteration (n = 16). Surface damage was consistent with previously observed mechanically assisted crevice corrosion phenomena. Titanium alloy implants (n = 25) showed no significant corrosion but had three constructs with fatigue failure of anchoring screws. One cobalt alloy construct showed no evidence of corrosion. CONCLUSIONS: Long-term effects of fretting and corrosion are unclear, and minimization of these phenomena seems justified. Selection of modular components with similar materials and surface finish may help the surgeon minimize localized changes over time. Stainless-steel implants with rigid interconnections and those with different surface finishes between rods and connectors are most susceptible to corrosion.

Explore related subjects

AlloysBone ScrewsCorrosionEquipment DesignEquipment FailureHumansProstheses and ImplantsSpineStainless SteelTitaniumJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

John S Kirkpatrick, Ramakrishna Venugopalan, Preston Beck, Jack Lemons. 2005. Corrosion on spinal implants.. https://pubmed.ncbi.nlm.nih.gov/15905769/

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Electrochemical characterization of albumin protein on Ti-6AL-4V alloy immersed in a simulated plasma solution.

The effect of oxygen and albumin on the electrochemical behavior of a Ti-6Al-4V alloy immersed in a simulated inorganic plasma (SIP) solution was studied with a rotating-cylindrical electrode configuration to focus on the surface/electrolyte reactions. Potentiokinetic scans and electrochemical impedance spectroscopy have been used to characterize the interface by determining the passive current density and capacitance. For the polarization scans, an albumin addition of 37.7 mg/cm(3) to the SIP solution (oxygenated and unoxygenated) decreased the passive current density, indicating a lowering of the corrosive rate. The surface capacitance for the Ti-6Al-4V alloy immersed in a SIP solution averaged 13 microF/cm(2), which transformed after albumin addition (37.7 mg/cm(3)) from a potential independent behavior to the capacitance ranging from 23 to 6 microF/cm(2) with increasing potentials from -800 to 1500 mV(SCE), respectively, indicative of albumin adsorption. Within the same potential range and albumin addition to oxygenated solutions, the capacitances expanded slightly with a similar decreasing trend from 31 to 6 microF/cm(2), although the capacitance depicts an interaction between the hydrated passive film and the adsorbed albumin from -550 to 500 mV(SCE) in which the capacitance plateaued at 15 microF/cm(2). The hydrated porous oxide film results from the porous rutile layer reacting with H(2)O(2) formed as an intermediary component of oxygen reduction at the Ti-6Al-4V surface. The passive film-albumin interaction would affect the processing of titanium alloys in their surface preparation for biocompatibility, as well as determining the reactivity of titanium alloys to proteins.

Alloys↗
PubMed2007

Fatigue-crack growth properties of thin-walled superelastic austenitic Nitinol tube for endovascular stents.

Over the past 10 years, the supereleastic nickel-titanium alloy Nitinol has found widespread application in the manufacture of small-scale biomedical devices, such as self-expanding endovascular stents. Although conventional stress/strain-life (S/N) analyses are invariably used as the primary method for design against fatigue loading and for predicting safe lifetimes, fracture mechanics-based methodologies provide a vital means of assessing the quantitative effect of defects on such lifetimes. Unfortunately, fracture mechanics studies on fatigue in Nitinol are scarce, and most results do not pertain to the (thin-walled tube) product forms that are typically used in the manufacture of endovascular stents. In the current work, we document the basic fatigue-crack growth properties of flattened thin-walled ( approximately 400 microm thick) Nitinol tubing in a 37 degrees C air environment. Crack-growth behavior is characterized over a wide range of growth rates ( approximately 6 orders of magnitude) and load ratios, that is, as a function of the alternating and maximum stress intensities, at 50 Hz. Limited experiments at both 5 and 50 Hz were also performed in 37 degrees C air and simulated body fluid to determine whether the cyclic frequency affects the fatigue behavior. Fatigue-crack growth-rate properties in such thin-walled Nitinol tube are found to be quite distinct from limited published data on other (mainly bulk) product forms of Nitinol, for example, bar and strip, both in terms of the relative fatigue thresholds and the variation in steady-state growth rates.

Alloys↗