Extremely long period-stacking structure in the Sb-Te binary system.

Kouichi Kifune·Yoshiki Kubota·Toshiyuki Matsunaga·Noboru Yamada
View original source ↗Export metadata ↓

Abstract

The crystal structure of the delta-phase in the Sb-Te binary system has been determined by synchrotron powder diffraction. It is clearly shown that many intermetallic compounds, which have different stacking periods depending on compound composition, exist in this phase. These structures are based on the cubic ABC stacking structure, and two kinds of fundamental structural units form an intergrowth along the stacking direction at the atomic level. The chemical formulae of these compounds are expressed as Sb(2n)Te3, where n is an integer and the number of stacking layers is 2n + 3. There is a relationship of inverse proportionality between the stacking period and the Te concentration.

Explore related subjects

AntimonyCrystallography, X-RayElectronsGlassModels, ChemicalMolecular ConformationPhysicsSynchrotronsTelluriumTemperatureX-Ray DiffractionJournal ArticleResearch Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Kouichi Kifune, Yoshiki Kubota, Toshiyuki Matsunaga, Noboru Yamada. 2005-09-23. Extremely long period-stacking structure in the Sb-Te binary system.. https://doi.org/10.1107/s0108768105017714

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2006

Electrochemical treatment of paper mill wastewater using three-dimensional electrodes with Ti/Co/SnO2-Sb2O5 anode.

The properties of the interlayer and outer layer of Ti/Co/SnO2-Sb2O5 electrode were studied, and the electrochemical behavior was examined as well. As a result of unsatisfactory treatment using Ti/Co/SnO2-Sb2O5 electrode, electrochemical disposal of paper mill wastewater employing three-dimensional electrodes, combining active carbon granules serving as packed bed particle electrodes, with Ti/Co/SnO2-Sb2O5 anode, was performed. The outcome demonstrates that efficient degradation was achieved. The residual dimensionless chemical oxygen demand (COD) concentration reached 0.137, and color removal 75% applying 167 mA cm(-2) current density at pH 11 and 15 g l(-1) NaCl. The instant current efficiency, energy cost, electrochemical oxidation index (EOI) and kinetic constant of the reaction were calculated. At the same time, the influence of pH and current density on COD abatement and decolorization was also investigated, respectively.

Antimony↗
PubMed2006

Comparison of antimony behavior with that of arsenic under various soil redox conditions.

The oxidation states and host phases of Sb and As in soil samples of mine tailing (Ichinokawa mine, Ehime, Japan) and in laboratory soil-water systems were determined by X-ray absorption fine structure (XAFS) spectroscopy. HPLC-ICP-MS was used for speciation of Sb and As in soil water. In the Ichinokawa soil water system, Sb was present exclusively as the oxidized form, Sb(V), over a wide redox range (from Eh = 360 to -140 mV, pH 8), while As was present as a mixture of As(III) and As(V). This finding was confirmed in the laboratory experiments. These results suggest that Sb(V) is a very stable form in the environment and that Sb is oxidized at more negative Eh than As. Combining the results of Fe and Mn XAFS analyses and a positive correlation among Sb, As, and Fe abundances in the soil, the host phases of Sb and As in soil were Fe(III) hydroxide. XAFS analyses of Sb and As are also consistent with this finding. Under reducing conditions, the concentration of As in the soil water increased whereas that of Sb decreased in both the Ichinokawa and laboratory systems. This suggests that this contrasting behavior is controlled mainly by the different redox properties of Sb and As.

Antimony↗