Interventional atrial septal defect closure using a totally bioresorbable occluder matrix: development and preclinical evaluation of the BioSTAR device.

Christian Jux·Harald Bertram·Peter Wohlsein·Michael Bruegmann·Thomas Paul
View original source ↗Export metadata ↓

Abstract

OBJECTIVES: We sought to test the hypothesis that interventional atrial septal defect (ASD) closure can be performed safely and effectively using a bioresorbable occluder matrix. BACKGROUND: The ideal septal occluder scaffold should promote the healthiest and most complete healing response while eventually facilitating the full resorption of the material and leaving "native" tissue behind, thus minimizing the potential for future complications from chronic foreign body and maintaining the possibility for later unobstructed transseptal access to the left atrium. METHODS: The STARFlex occluders (NMT Medical Inc., Boston, Massachusetts) were modified by substituting the conventional polyester fabric for a bioengineered, acellular type-I collagen matrix derived from porcine submucosa with a heparin-coated surface (BioSTAR occluder, NMT Medical Inc.). Comparative transcatheter closure of ASDs was performed in young sheep (n = 36). Gross pathology and histopathology were obtained after follow-up periods ranging from 7 days to 2 years. RESULTS: The STARFlex (control) devices were encapsulated time-dependently by ingrown fibrous tissue. Histology showed a mild but chronically persisting foreign body reaction. By contrast, BioSTAR devices exhibited a mild-to-moderate transient cellular immune response. Heparin coating of the BioSTAR surface improved the biocompatibility of the device by reducing surface thrombogencity. A remodeling process of the collagen scaffold, starting after 30 days in vivo, resulted in the full replacement of the matrix by host tissue after 2 years of follow-up. CONCLUSIONS: The BioSTAR device is the first septal occluder with a totally bioresorbable matrix that is fully replaced by host tissue during the healing process. The promising results of this study support testing of the BioSTAR device in clinical trials.

Explore related subjects

Absorbable ImplantsAnimalsCardiac CatheterizationCoated Materials, BiocompatibleCollagen Type IFemaleHeart Septal Defects, AtrialHeparinProstheses and ImplantsSheepTissue EngineeringEvaluation StudyJournal ArticleResearch Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Christian Jux, Harald Bertram, Peter Wohlsein, Michael Bruegmann, Thomas Paul. 2006-06-09. Interventional atrial septal defect closure using a totally bioresorbable occluder matrix: development and preclinical evaluation of the BioSTAR device.. https://doi.org/10.1016/j.jacc.2006.02.057

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Encapsulation of proteins in biodegradable polymeric microparticles using electrospray in the Taylor cone-jet mode.

Solvent extraction (or evaporation from a W(1)/O/W(2)-dispersion), coacervation, and spray drying methods are commonly employed to encapsulate protein drugs in polymeric microparticles for sustained delivery applications. To overcome the limitations of these methods, a novel electrospray method was developed to encapsulate a model protein drug-bovine serum albumin (BSA) in biodegradable polymeric microparticles and examine the feasibility of the process in not denaturing the protein. Microparticles of approximately 20 microm diameter with corrugated surfaces and smooth surfaces were observed by scanning electron microscope. Confocal laser scanning microscope images showed that BSA was distributed evenly in microparticles. Sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE) was employed to investigate the protein integrity of BSA released from the polymer matrix after 38 days. No protein degradation was observed during the 38 days release. The secondary structure of released BSA was characterized by Fourier transform infrared (FTIR) and circular dichroism (CD), which suggested that the released BSA was almost identical to native BSA. The encapsulation efficiency could reach 76% by adjusting the amount of the additive Pluronic F127 and processing parameters. The release profile could be tailored by the fabrication process and the sustained release of BSA could endure for more than 1 month. More than 80% of the bioactivity of BSA (evaluated by BSA ELISA kit) could be maintained after releasing from polymer matrix. Findings of the present study demonstrate that this novel electrospray method is a promising approach to encapsulate bioactive materials such as proteins, enzymes, antibiotics, and DNA fragments in biodegradable polymeric particles.

Absorbable Implants↗
PubMed2007

A novel poly(ethylene glycol)-fibrinogen hydrogel for tibial segmental defect repair in a rat model.

The aim of this study is to investigate regeneration in a segmental bone defect using a novel fibrinogen-based hydrogel material. The use of hydrogels made from poly(ethylene glycol) (PEG) conjugated to fibrinogen for this purpose may be better to conventional fibrin-based materials as it offers an additional degree of control over the structural characteristics and biodegradation of the material. At the same time, it maintains some of the inherent biofunctionality of the fibrinogen molecule. PEGylated fibrinogen hydrogels with various degrees of proteolytic resistance based on PEG and fibrinogen composition were designed for slow, intermediate, and fast biodegradation. The hydrogels were implanted into 7-mm segmental rat tibial defects without additional osteoinductive factors with the rationale that the ingrowth matrix will displace the normal fibrin clot while sustaining a similar healing effect for a longer duration. Histological and X-ray results confirmed that the extent and distribution of newly formed bone in the defect after 5 weeks strongly parallels the biodegradation pattern of the implanted material. When compared to nonunions in animals treated with the fast-degrading implants and untreated control animals, the rats implanted with the intermediate-degrading material exhibited osteoneogenesis. This data supports the hypothesis that the perseverance of the PEGylated fibrinogen material can be synchronized with the optimal healing characteristics of a segmental osseous defect and that the consequent sustained release of fibrinogen fragments facilitates the osteogenic response at the injury site. The PEGylated fibrinogen material may, therefore, be a highly efficacious material for promoting the healing of bone defects and especially nonunion fractures.

Absorbable Implants↗
PubMed2007

Pores in synthetic nerve conduits are beneficial to regeneration.

Current opinion holds that pores in synthetic nerve guides facilitate nerve regeneration. Solid factual support for this opinion, however, is absent; most of the relevant studies assessed only morphological parameters and results have been contradictory. To evaluate the effect of pores, the rat sciatic nerve was either autografted or grafted with nonporous, macroporous (10-230 mum), and microporous (1-10 microm) biodegradable epsilon-caprolactone grafts. Twelve weeks later, the grafted nerves were resected, and the electrophysiological properties were determined in vitro. Subsequently midgraft-level sections were inspected, and peroneal nerve sections were evaluated morphometrically. Finally, the gastrocnemic and tibial muscle morphometrical properties were quantified. The microporous nerve graft performed much better than the nonporous and macroporous grafts with respect to most parameters: it was bridged by a free floating bundle that contained myelinated nerve fibers, there were more nerve fibers present distal to the graft, the electrophysiological response rate was higher, and the decrease in muscle cross-sectional area was markedly smaller. Hence, the present study demonstrates the beneficial effect of synthetic nerve guide pores on nerve regeneration, although with the caveat that not pores per se, but only small (1-10 microm) pores were effective.

Absorbable Implants↗