A novel combinatorial approach for understanding microstructural evolution and its relationship to mechanical properties in metallic biomaterials.

S Nag·R Banerjee·H L Fraser
View original source ↗Export metadata ↓

Abstract

The new generation of metallic biomaterials for prosthesis implantation (orthopedic and dental) typically have a Ti base with fully biocompatible alloying additions such as Nb, Ta, Zr, Mo, Fe and Sn. While the binary Ti-Ta and the ternary Ti-Nb-Ta systems are promising, the large composition space afforded by these systems offers tremendous scope in terms of alloy design via optimization of alloy composition and thermomechanical treatment. In the present paper a novel combinatorial approach has been developed for rapidly exploring the microstructural evolution and microstructure-microhardness (or elastic modulus) relationships in these systems. Using directed laser deposition, compositionally graded alloy samples have been fabricated and subsequently heat-treated to affect different microstructures in terms of the volume fraction and distribution of the alpha phase in the beta matrix as a function of composition. Subsequently, composition-specific indentation-based hardness and modulus information has been obtained from these graded samples, and the resulting data have been used to develop relationships between the composition, microstructure and mechanical properties. Such rapid combinatorial assessments can be very useful in optimizing not only the alloy composition but also the desired microstructure for achieving the best combination of properties for specific orthopedic or dental applications.

Explore related subjects

AlloysBiocompatible MaterialsCoated Materials, BiocompatibleCombinatorial Chemistry TechniquesDental ImplantsElasticityHardnessHardness TestsHot TemperatureManufactured MaterialsMaterials TestingMetalsMicroscopy, Electron, ScanningProstheses and ImplantsJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

S Nag, R Banerjee, H L Fraser. 2006-10-27. A novel combinatorial approach for understanding microstructural evolution and its relationship to mechanical properties in metallic biomaterials.. https://doi.org/10.1016/j.actbio.2006.08.005

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Electrochemical characterization of albumin protein on Ti-6AL-4V alloy immersed in a simulated plasma solution.

The effect of oxygen and albumin on the electrochemical behavior of a Ti-6Al-4V alloy immersed in a simulated inorganic plasma (SIP) solution was studied with a rotating-cylindrical electrode configuration to focus on the surface/electrolyte reactions. Potentiokinetic scans and electrochemical impedance spectroscopy have been used to characterize the interface by determining the passive current density and capacitance. For the polarization scans, an albumin addition of 37.7 mg/cm(3) to the SIP solution (oxygenated and unoxygenated) decreased the passive current density, indicating a lowering of the corrosive rate. The surface capacitance for the Ti-6Al-4V alloy immersed in a SIP solution averaged 13 microF/cm(2), which transformed after albumin addition (37.7 mg/cm(3)) from a potential independent behavior to the capacitance ranging from 23 to 6 microF/cm(2) with increasing potentials from -800 to 1500 mV(SCE), respectively, indicative of albumin adsorption. Within the same potential range and albumin addition to oxygenated solutions, the capacitances expanded slightly with a similar decreasing trend from 31 to 6 microF/cm(2), although the capacitance depicts an interaction between the hydrated passive film and the adsorbed albumin from -550 to 500 mV(SCE) in which the capacitance plateaued at 15 microF/cm(2). The hydrated porous oxide film results from the porous rutile layer reacting with H(2)O(2) formed as an intermediary component of oxygen reduction at the Ti-6Al-4V surface. The passive film-albumin interaction would affect the processing of titanium alloys in their surface preparation for biocompatibility, as well as determining the reactivity of titanium alloys to proteins.

Alloys↗
PubMed2007

Fatigue-crack growth properties of thin-walled superelastic austenitic Nitinol tube for endovascular stents.

Over the past 10 years, the supereleastic nickel-titanium alloy Nitinol has found widespread application in the manufacture of small-scale biomedical devices, such as self-expanding endovascular stents. Although conventional stress/strain-life (S/N) analyses are invariably used as the primary method for design against fatigue loading and for predicting safe lifetimes, fracture mechanics-based methodologies provide a vital means of assessing the quantitative effect of defects on such lifetimes. Unfortunately, fracture mechanics studies on fatigue in Nitinol are scarce, and most results do not pertain to the (thin-walled tube) product forms that are typically used in the manufacture of endovascular stents. In the current work, we document the basic fatigue-crack growth properties of flattened thin-walled ( approximately 400 microm thick) Nitinol tubing in a 37 degrees C air environment. Crack-growth behavior is characterized over a wide range of growth rates ( approximately 6 orders of magnitude) and load ratios, that is, as a function of the alternating and maximum stress intensities, at 50 Hz. Limited experiments at both 5 and 50 Hz were also performed in 37 degrees C air and simulated body fluid to determine whether the cyclic frequency affects the fatigue behavior. Fatigue-crack growth-rate properties in such thin-walled Nitinol tube are found to be quite distinct from limited published data on other (mainly bulk) product forms of Nitinol, for example, bar and strip, both in terms of the relative fatigue thresholds and the variation in steady-state growth rates.

Alloys↗