Ceramic implants in otologic surgery.

D Plester·K Jahnke
View original source ↗Export metadata ↓

Abstract

We have examined the suitability of ceramic materials for reconstruction in middle ear surgery. The excellent tolerance of bio-inert aluminum oxide ceramic implanted into the middle ear has been shown by our electron microscopic studies and clinical experience. Our implants developed for ossicular chain reconstruction were covered by a delicate middle ear mucous membrane within a few weeks. We have observed no foreign body reactions. The ceramic prostheses are distinguished by the almost unlimited number of forms or shapes into which they can be ground quickly and precisely during the operation. We value Al2O3 ceramic implants because there is no bony fixation with the surrounding bone, but rather a jointlike connection with the remaining parts of the ossicular chain. The composition of resorbable tricalcium phosphate, bio-active ceramic, corresponds to the inorganic component of bone. Because it exhibits the characteristic of being replaced by autogenous bone, we consider it for the obliteration of mastoid cavities. Based on our preliminary experience, dense tricalcium phosphate ceramic might play a valuable role in the reconstruction of the posterior auditory canal wall. In addition, we have used dense tricalcium phosphate ceramic to correct minor ossicular chain defects (for example, erosion of the long process of the incus). A survey is given concerning the indications and techniques for the use of these new materials in middle ear surgery, as well as our results covering a period of three years, which are very encouraging as far compatibility and function are concerned.

Explore related subjects

Aluminum OxideBiocompatible MaterialsCalcium PhosphatesCeramicsFollow-Up StudiesGlassHumansProstheses and ImplantsTympanoplastyJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

D Plester, K Jahnke. 1981. Ceramic implants in otologic surgery.. https://pubmed.ncbi.nlm.nih.gov/7304719/

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed1995

Ultramicrotomy of industrial alumina.

Industrial materials, such as alumina, often pose difficulties in their preparation for TEM examination. Composite and particulate materials are particularly difficult to prepare using conventional thinning techniques, i.e., ion beam and chemical jet thinning. Ultramicrotomy (UM) can be used to produce TEM specimens with a uniform thickness and an unaltered composition. Some crystalline materials, i.e., alumina hydrate, were difficult to section due to conflict between the cutting direction and cleavage planes. Sectioning was successful when these two directions were mutually parallel or perpendicular. At other orientations shattering occurred. Microcrystalline particulate materials, i.e., calcined alumina, were sectioned successfully in particles < 70 microns in diameter. The phases found in industrial alumina particles were gamma, delta, theta, and alpha alumina. Gamma alumina consisted of fine-grained, equiaxed crystallites. The selected area electron diffraction (SAED) patterns indicated poor crystallinity with a distinct hexagonal texture. Delta and theta alumina appeared as an undifferentiated intermediary microstructure of elongated grains. The SAED patterns indicated poor crystallinity, but without a distinct texture. Alpha alumina was found to be a coarse-grained crystalline phase with high diffraction contrast. SAED patterns consisted of fine, randomly oriented spots. Considerable variation was observed in the distribution of phases. In some specimens, discrete particles of gamma and alpha predominated. In others, particles were a mixture of phases representative of the bulk composition. To characterise these samples, TEM of numerous whole particles was required. Ultramicrotomy was the only preparation technique capable of producing such samples.

Aluminum Oxide↗
PubMed1995

Effects of hydroxyapatite and alumina sheaths on postoperative peritendinous adhesions in chickens.

Two experimental methods for restoring flexor tendon sheath integrity and preventing adhesions around traumatized flexor tendons utilizing artificial tendon sheaths made of either hydroxyapatite (HAp) or alumina were studied in a flexor tendon-trauma model and compared to a standard tendon sheath repair and a control. Eighty toes were divided equally into a control group, a sheath repair group, an HAp group, and an alumina group. Profundus tendons in zone II were divided and repaired after sublimis excision in all groups. In the sheath repair group, the flexor sheath was also repaired after suturing the tendon. In artificial sheath groups, sheaths made of HAp and alumina were placed over the repair sites to protect them from the surrounding tissues. In the control group, after repairing the tendon, the flexor sheath was excised and no artificial sheaths were used. Each toe was immobilized in a plaster cast for 3 weeks. After three weeks, the plaster cast was removed followed by the removal of the sheaths in the artificial sheath groups through a small incision in the skin in zone II. Active mobilization was encouraged in each group. Postoperative adhesions were examined at 3, 6, 9, and 12 week intervals by using light microscopic techniques. To further explore the effects of artificial sheaths on tendon healing, transmission electron microscopy was done for the HAp and alumina groups at 3, 6, and 12 week intervals. Results demonstrated decreased severity of postoperative adhesions in the HAp as well as in the alumina groups in comparison with the sheath repair and controls. A space resembling the fibro-osseous canal was formed around the tendon after removing the sheaths. This space remained patent until 12 weeks, 9 weeks after removing the sheaths, and a newly formed tendon sheath-like structure lined by synovial cells and with a peritenon-like structure over the tendon surface was observed. In the sheath repair and control groups, the severity of adhesions was decreased with the passage of time, to some extent due to unrestricted mobility. However, a newly formed tendon sheath or peritenon-like structure was not observed. Electron microscopic studies confirmed good healing at the suture in the HAp and alumina groups with no evidence of necrosis. These results are qualitative in nature as no statistical tests were performed. From these results we conclude that if the tendon is separated from the surrounding granulation tissue by a barrier with good biocompatibility, the tendon can heal with fewer adhesions.(ABSTRACT TRUNCATED AT 400 WORDS)

Aluminum Oxide↗
PubMed1995

Wettability and interfacial interactions in bioceramic-body-liquid systems.

Wetting experiments, by the sessile drop technique, were carried out at 37 degrees C in air to determine the surface and interfacial interactions that take place in various solid bioceramics based on Al2O3, ZrO2(YPZ), SiO2, and TiO2 in contact with water, Ringer solution, artificial synovial fluid, calf serum, human plasma, and whole blood (+ EDTA). The surface energy of the liquids was measured by the ring method. The calculated values of the energy of interaction (work of adhesion) reveal that intermolecular forces act across the solid-liquid interfaces. The contribution of the dispersion and polar interactions to the surface energy of the polar liquids and the pure or mixed oxides was determined assuming that in the system of Mn-steel-liquids only dispersion forces act at the interface. It was found that the contribution of the polar interactions to the energy of interaction at the solid-liquid interface increases with the glassy phase content of the oxide that causes reduction of the measured contact angle.

Aluminum Oxide↗