Biodegradable polymer scaffolds for tissue engineering.

L E Freed·G Vunjak-Novakovic·R J Biron·D B Eagles·D C Lesnoy·S K Barlow·R Langer
View original source ↗Export metadata ↓

Abstract

Synthetic polymer scaffolds designed for cell transplantation were reproducibly made on a large scale and studied with respect to biocompatibility, structure and biodegradation rate. Polyglycolic acid (PGA) was extruded and oriented to form 13 microns diameter fibers with desired tenacity. Textile processing techniques were used to produce fibrous scaffolds with a porosity of 97% and sufficient structural integrity to maintain their dimensions when seeded with isolated cartilage cells (chondrocytes) and cultured in vitro at 37 degrees C for 8 weeks. Cartilaginous tissue consisting of glycosaminoglycan and collagen was regenerated in the shape of the original PGA scaffold. The resulting cell-polymer constructs were the largest grown in vitro to date (1 cm diameter x 0.35 cm thick). Construct mass was accurately predicted by accounting for accumulation of tissue components and scaffold degradation. The scaffold induced chondrocyte differentiation with respect to morphology and phenotype and represents a model cell culture substrate that may be useful for a variety of tissue engineering applications.

Explore related subjects

Biocompatible MaterialsBiodegradation, EnvironmentalCartilageCell TransplantationCells, CulturedCollagenGlycosaminoglycansPolyglycolic AcidPolymersProstheses and ImplantsRegenerationJournal ArticleResearch Support, Non-U.S. Gov'tResearch Support, U.S. Gov't, Non-P.H.S.

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

L E Freed, G Vunjak-Novakovic, R J Biron, D B Eagles, D C Lesnoy, S K Barlow, R Langer. 1994. Biodegradable polymer scaffolds for tissue engineering.. https://doi.org/10.1038/nbt0794-689

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed1997

Biocompatibility of nickel-titanium shape memory metal and its corrosion behavior in human cell cultures.

Nickel-titanium alloy (Nitinol) is a metallic biomaterial that has a unique thermal shape memory, superelasticity, and high damping properties. Nitinol is potentially very useful in orthopedic surgery, for example. At present, there are not enough confirmative biocompatibility data available on Nitinol. The aim of our study was to clarify the primary cytotoxicity and corrosion rate of Nitinol in human cell cultures. Comparisons were made with stainless steel (Stst), titanium (Ti), composite material (C), and control cultures with no test discs. Human osteoblasts (OB) and fibroblasts (FB) were incubated for 10 days with test discs of equal size, 6 x 7 mm. The cultures were photographed and the cells counted. Samples from culture media were collected on days 2, 4, 6, and 8, and the analysis of metals in the media was done using flameless atomic absorption spectrophotometry. The proliferation of FB was 108% (Nitinol), 134% (Ti) (p < 0.02), 107% (Stst), and 48% (C)(p < 0.0001) compared to the control cultures. The proliferation of OB was 101% (Nitinol), 100% (Ti), 105% (Stst), and 54% (C) (p < 0.025) compared to the controls. Initially, Nitinol released more nickel (129-87 micrograms/L) into the cell culture media than Stst (7 micrograms/L), but after 2 days the concentrations were about equal (23-5 micrograms/L versus 11-1 micrograms/L). The titanium concentrations from both Nitinol and Ti samples were all < 20 micrograms/L. We conclude that Nitinol has good in vitro biocompatibility with human osteoblasts and fibroblasts. Despite the higher initial nickel dissolution, Nitinol induced no toxic effects, decrease in cell proliferation, or inhibition on the growth of cells in contact with the metal surface.

Biocompatible Materials↗
PubMed1997

Effects of hydroxypropyl methylcellulose and other gelling agents on the handling properties of calcium phosphate cement.

The calcium phosphate cement (CPC) used in this study was formed by combining equimolar amounts of tetracalcium phosphate (TTCP) and dicalcium phosphate anhydrous (DCPA). This powder, when mixed with water, sets to a hard cement in about 30 min. However, the water-based CPC paste is not highly cohesive and is vulnerable to washout until hardening occurs. The objectives of this study were to investigate the effects on handling properties, washout resistance, cement hardening behavior, and mechanical properties of adding several gelling agents to CPC paste. Aqueous solutions that contained a mass fraction of 2-4% of hydroxypropyl methylcellulose (HPMC), carboxyl methylcellulose (CMC), chitosan acetate, and chitosan lactate were used as cement liquids. Hardening time was measured by the Gilmore needle test; resistance to washout was evaluated by the disintegration of the cement specimen in water with agitation; and mechanical strength was evaluated by the measurement of diametral tensile strength and compressive strength. Handling properties were greatly improved by the addition of HPMC, CMC, chitosan acetate, and chitosan lactate. Hardening time was retarded by the additions of HPMC and CMC, and mechanical strength was weakened by the addition of either the chitosan lactate or the chitosan acetate.

Biocompatible Materials↗
PubMed1997

Aqueous formation of hydroxyapatite.

The kinetics of stoichiometric (Ca/P = 1.67) and calcium-deficient (Ca/P = 1.5) hydroxyapatite formed in aqueous solution by acid-base reactions involving CaHPO4 and Ca4(PO4)2O were determined. Complete reaction occurs within 6 h at 37.4 degrees C regardless of composition with stoichiometric hydroxyapatite forming more rapidly. Stoichiometric hydroxyapatite formed more rapidly because the particle sizes of its precursors were smaller. Hydroxyapatite formation is characterized by an initial period of surface hydration of the precursors, an induction period, and a period during which the bulk of the conversion to hydroxyapatite occurs. During the first 3 h of reaction at 37.4 degrees C, the pH is about 8.25 and 7.6, respectively, as the stoichiometric and calcium-deficient hydroxyapatite are being formed. Subsequently the pH values move toward those of the related invariant points: Ca10(PO4)6(OH)2-Ca(OH)2 solution, and CaHPO4-Ca9HPO4(PO4)5OH solution. The concentrations of calcium and phosphate in solution never exceed those in serum. Seeding with 5 wt% hydroxyapatite eliminates induction regardless of composition. The kinetics are first-order and follow the Arrhenius relationship regardless of composition. The total heats of reaction (delta Hr) were determined at constant temperatures between 25 degrees C and 70 degrees C. delta Hr values of 261.3 and 320 kJ/mol were determined for the formation of calcium-deficient hydroxyapatite and stoichiometric hydroxyapatite, respectively. Activation energies of 84.5 and 87.4 kJ/mol were calculated for the formation of calcium-deficient and stoichiometric hydroxyapatite, respectively. Heats of formation for Ca4(PO4)2O and Ca9HPO4(PO4)5OH were calculated to be -4764.1 and -12707.7 kJ/mol, respectively.

Biocompatible Materials↗