Changes caused by processing complete mandibular dentures.

S K Lechner; G A Thomas

doi:10.1016/0022-3913(94)90293-3

Home/Archive/PubMed

PubMed · 7853258

Changes caused by processing complete mandibular dentures.

S K Lechner·G A Thomas

View original source ↗Export metadata ↓

Abstract

Qualitative and quantitative comparisons were made before and after complete mandibular dentures were processed. Linear measurements indicated shrinkage in all dimensions, and the greatest shrinkage occurred in an anteroposterior direction along the lingual flanges. Differences in shrinkage across the various points measured suggest that the denture material twists during curing, and the final qualitative changes appear as pressure areas in the distolingual and anterolabial regions.

Explore related subjects

Acrylic Resins Analysis of Variance Bicuspid Calcium Sulfate Dental Casting Technique Denture Design Denture, Complete, Lower Microscopy Molar Pilot Projects Rotation Surface Properties Tooth, Artificial Comparative Study Journal Article Research Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

S K Lechner, G A Thomas. 1994. Changes caused by processing complete mandibular dentures.. https://doi.org/10.1016/0022-3913(94)90293-3

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed1997

The staining of acidic proteins on polyacrylamide gels: enhanced sensitivity and stability of "Stains-all" staining in combination with silver nitrate.

A number of acidic proteins, such as those found in bone and dentin, are poorly resolved on acrylamide gels using Coomassie blue or silver nitrate staining. The cationic dye Stains-all allows visualization and identification of these proteins due to their differential staining: highly acidic proteins stain blue and intact proteoglycans stain purple, whereas less acidic proteins stain pink. However, the use of Stains-all is limited due to relatively poor staining sensitivity and lack of stability to light. A procedure which addresses these deficiencies has been developed utilizing established protocols for Stains-all staining followed by silver nitrate incubation and development. In this way, phosphoproteins such as osteopontin, bone sialoprotein, dentin phosphophoryn, and other acidic glycoproteins are visualized at higher sensitivity (greater than fivefold) and staining stability than normally achieved with just Stains-all. The protocol stains a greater variety of proteins than a combined alcian blue/silver staining procedure previously described. Utilizing the Stains-all/silver protocol, porcine bone osteopontin, a protein not visualized by standard silver staining, can be observed in amounts as little as 0.25 ng on polyacrylamide gels. Furthermore, densitometric scans demonstrate that the staining intensity is proportional to osteopontin amount and can be used for quantification over a range from 0.25 to 50 ng.

Acrylic Resins↗

PubMed1997

A laboratory evaluation of the construction of resin-bonded cast restorations.

OBJECTIVE: To compare the effect of two construction techniques and two pattern materials on the fit of resin-bonded cast restorations. DESIGN: In-vitro study carried out by one operator. SETTING: Postgraduate university hospital. SUBJECTS AND METHODS: 65 nickel-chrome castings were constructed using refractory die and lift-off techniques with wax and acrylic resin pattern material. They were cemented onto master silver dies, embedded in self-curing acrylic resin and sectioned along their long axes. Interfacial distance between the master silver die and casting was measured. RESULTS: A significant different between the range of figures in each group (Mann-Whitney Test, P < 0.01) was found. Construction techniques can be ranked in order of fit of castings: 1. Refractory die, wax patterns: 42.6 microns (SD 12.03). 2. Refractory die, acrylic resin patterns: 53.7 microns (SD.16.06).3. Conventional technique, acrylic resin patterns: 85.5 microns (SD 31.62). 4. Lift-off technique, wax patterns: 139 microns (SD 53.15).5. Lift-off technique, acrylic patterns: 172.8 microns (SD 74.04). CONCLUSIONS: Castings constructed using refractory die technique and subsequently cemented resulted in a more accurate and less variable fit than those produced with the lift-off technique. Wax patterns lead to more accurate castings than acrylic resin and locating indentations may interfere with the cementation of castings when lift-off techniques are used.

Acrylic Resins↗

PubMed1997

Rigid porous polyacrylamide-based monolithic columns containing butyl methacrylate as a separation medium for the rapid hydrophobic interaction chromatography of proteins.

Macroporous poly(acrylamide-co-butyl methacrylate-co-N,N'-methylenebisacrylamide) monoliths containing up to 15% butyl methacrylate units have been prepared by direct polymerization within the confines of HPLC columns. The hydrodynamic and chromatographic properties of these 50 mm x 8 mm I.D. columns-such as back pressure at different flow-rates, effect of percentage of hydrophobic component in the polymerization mixture, effect of salt concentration on the retention of proteins, dynamic loading capacity, and recovery-were determined under conditions typical of hydrophobic interaction chromatography. Using the monolithic column, five proteins were easily separated within only 3 min.

Acrylic Resins↗