Advances in computer-aided design and computer-aided manufacture technology.

Abstract

Although the development of computer-aided design (CAD) and computer-aided manufacture (CAM) technology and the benefits of increased productivity became obvious in the automobile and aerospace industries in the 1970s, investigations of this technology's application in the field of dentistry did not begin until the 1980s. Only now are we beginning to see the fruits of this work with the commercial availability of some systems; the potential for this technology seems boundless. This article reviews the recent literature with emphasis on the period from June 1992 to May 1993. This review should familiarize the reader with some of the latest developments in this technology, including a brief description of some systems currently available and the clinical and economical rationale for their acceptance into the dental mainstream. This article concentrates on a particular system, the Cerec (Siemens/Pelton and Crane, Charlotte, NC) system, for three reasons: first, this system has been available since 1985 and, as a result, has a track record of almost 7 years of data. Most of the data have just recently been released and consequently, much of this year's literature on CAD-CAM is monopolized by studies using this system. Second, this system was developed as a mobile, affordable, direct chairside CAD-CAM restorative method. As such, it is of special interest to the dentist who will offer this new technology directly to the patient, providing a one-visit restoration. Third, the author is currently engaged in research using this particular system and has a working knowledge of this system's capabilities.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

J R Calamia. 1994. Advances in computer-aided design and computer-aided manufacture technology.. https://pubmed.ncbi.nlm.nih.gov/8032444/

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

Bioactive glass as precursor of designed-architecture scaffolds for tissue engineering.

In this work, the conditions to obtain concentrated and fluid suspensions from a bioactive glass (55-SiO(2); 41-CaO; 4-P(2)O(5); mol %) were investigated. The influence of the heat treatment of the glass on the specific surface area, solubility, bioactivity, and finally on their dispersion characteristics was studied. Zeta potential and viscosity measurements were carried out, and based on the obtained results, the best dispersant was selected. The optimum concentration of dispersant, maximum content of solid and time of mixing were also investigated. Slurries containing 50 vol % could be obtained calcining the glass at 1100 degrees C and using Darvan 811 (sodium polyacrylate) as dispersant. Scaffolds with designed architecture were prepared from these suspensions combining the gelcasting method and the stereolithography technique. A polymeric negative (replica of the desired structure) was previously obtained by stereolithography. The slurry was cast into the molds and then polymerized (gelcasting method). The negative was eliminated by heat treatment. After sintering at 1300 degrees C, scaffolds with interconnected porosity and three-dimensional channels of 400-470 microm and macropores of 1.4 microm were obtained.

Ceramics↗

Effect of crystallization heat treatment on the microstructure and biaxial strength of fluorrichterite glass-ceramics.

The purpose of this study was to evaluate the effect of crystallization heat treatment on the flexural strength of potassium fluorrichterite glass-ceramics for biomedical applications. After melting and casting, discs were sectioned from the glass ingots, randomly divided into 10 groups, and heat treated at various temperatures ranging between 890 degrees C and 925 degrees C for various durations. One group was air-abraded after heat treatment. XRD revealed the presence of fluorrichterite and fluormica for all heat-treated groups. SEM confirmed the presence of both fluorrichterite and fluormica crystals. Crystal size increased with temperature and duration of the heat treatment. The mean flexural strength after air abrasion was not significantly different than that of the other groups except the group heat treated at 925 degrees C. The mean flexural strength was maximum after heat treatment at 900 degrees C for 1 h (497.6 +/- 25.5 MPa) and decreased linearly with the longer durations of heat treatment at 900 degrees C.

Ceramics↗

Influence of contamination on bonding to zirconia ceramic.

The purpose of this study was to investigate the influences of contaminations and cleaning methods on bonding to dental zirconia ceramic. After saliva immersion and using silicone disclosing agent, airborne-particle abraded ceramic specimens were cleaned with isopropanol (AL), acetone (AC), 37% phosphoric acid (PA), additional airborne-particle abrasion (AA), or only with water rinsing (SS). Airborne-particle abraded specimens without contaminations (CL) were used as control group. For chemical analysis specimens of all groups were examined with X-ray photoelectron spectroscopy (XPS). Plexiglas tubes filled with composite resin were bonded to ceramic specimens using a phosphate-monomer containing composite luting resin. After 3-day water storage, tensile bond strengths (TBS) were tested. XPS analysis of group SS showed the presence of saliva and silicone (Si) contamination on the surface. The ratios of carbon/zirconium and oxygen/zirconium for groups PA and AA were comparable to those ratios obtained for group CL, indicating the removal of the organic saliva contamination. Airborne-particle abrasion and acetone completely removed Si contamination from ceramic surfaces. Isopropanol had little cleaning effect on the two contaminants. TBS (median +/- standard deviation) in MPa of the groups SS (11.6 +/- 3.1), AL (10.0 +/- 2.9), and AC (13.0 +/- 2.8) were statistically lower than those of groups PA (33.6 +/- 5.5), AA (40.1 +/- 3.6), and CL (47.0 +/- 8.1) (p < 0.001), while no differences were found in TBS between groups AA and CL (p > 0.5). Contamination significantly reduced bond strengths to zirconia ceramic. Airborne-particle abrasion was the most effective cleaning method.

Ceramics↗