Polymerization of composites using pulsed laser.

Z Tarle·A Meniga·M Ristic·J Sutalo·G Pichler
View original source ↗Export metadata ↓

Abstract

The quality of visible-light-cured composites depends on the capability of the light source to properly polymerize the material within a specified exposure time. In this study, the degree of conversion of different composite materials (hybrid and microfilled) of light and dark shades was compared after illumination by a standard curing unit and pulsed laser (lambda=468) respectively. The degree of conversion was measured by Fourier transform infrared spectroscopy. Results obtained by the analysis of the pulsed laser-induced polymerization were significantly higher for all the materials and shades observed. All values of the degree of conversion were lower for dark shades of all types of composites, regardless of the photopolymerization technique used. Besides the surface, better polymerization was recorded also at depths of 1.0, 2.0 and 3.0 mm, respectively. These values varied from 59.7%+/-2.14 to 84.5%+/-0.33 for pulsed laser (including all depths) caused by the saturation effect induced by high power laser pulses and from 42.7%+/-1.48 to 74.7%+/-0.99 for standard polymerization.

Explore related subjects

Acrylic ResinsBisphenol A-Glycidyl MethacrylateChemical PhenomenaChemistry, PhysicalColorComposite ResinsDental MaterialsLasersLightPolymersPolyurethanesSpectroscopy, Fourier Transform InfraredSurface PropertiesComparative StudyJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Z Tarle, A Meniga, M Ristic, J Sutalo, G Pichler. 1995. Polymerization of composites using pulsed laser.. https://doi.org/10.1111/j.1600-0722.1995.tb01863.x

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Influence of the activator in an acrylic bone cement on an array of cement properties.

In all but one of the acrylic bone cement brands used in cemented arthroplasties, N,N-dimethyl-4-toluidine (DMPT) serves as the activator of the polymerization reaction. However, many concerns have been raised about this activator, all related to its toxicity. Thus, various workers have assessed a number of alternative activators, with two examples being N,N-dimethylamino-4-benzyl laurate (DMAL) and N,N-dimethylamino-4-benzyl oleate (DMAO). The results of limited characterization of cements that contain DMAL or DMAO have been reported in the literature. The present work is a comprehensive comparison of cements that contain one of these three activators, in which the values of a large array of their properties were determined. These properties range from the setting time and maximum exotherm temperature of the curing cement to the variation of the loss elastic modulus of the cured cement with frequency of the applied indenting force in dynamic nanoindentation tests. The present results, taken in conjunction with those presented in previous reports by the present authors and co-workers on other properties of these cements, indicate that both DMAL and DMPT are suitable alternatives to DMPT.

Acrylic Resins↗
PubMed2007

Dynamic scaling of polymer gels comprising nanoparticles.

We present dynamic light scattering (DLS) measurements of soft poly(methyl-methacrylate) (PMMA) and polyacrylamide (PA) polymer gels prepared with trapped bodies (latex spheres or magnetic nanoparticles). We show that the anomalous diffusivity of the trapped particles can be analyzed in terms of a fractal Gaussian network gel model for the entire time range probed by DLS technique. This model is a generalization of the Rouse model for linear chains extended for structures with power law network connectivity scaling, which includes both percolating and uniform bulk gel limits. For a dilute dispersion of strongly scattering particles trapped in a gel, the scattered electric field correlation function at small wavevector ideally probes self-diffusion of gel portions imprisoning the particles. Our results show that the time-dependent diffusion coefficients calculated from the correlation functions change from a free diffusion regime at short times to an anomalous subdiffusive regime at long times (increasingly arrested displacement). The characteristic time of transition between these regimes depends on scattering vector as approximately q(-2), while the time decay power exponent tends to the value expected for a bulk network at small q. The diffusion curves for all scattering vectors and all samples were scaled to a single master curve.

Acrylic Resins↗