The purpose of this study was to evaluate the long-term effect of aging in water on the physical properties of experimental composites having systematically controlled differences in degree of conversion (DC), filler volume fraction (Vf), and percentage of silane-treated fillers. Composites were made with a 50% Bis-GMA:50% TEGDMA light-cured resin and a 1-2 microm (average size) strontium glass filler (+ 5 wt% SiO2 microfiller). For composites A-E, the DC was varied from 56-66% by changing the curing time; for D and F-I, the Vf was varied from 28-62 vol%; and for D and J-M, the percent of fillers with a silane coupling agent (gamma-MPS) was varied from 20-100%. Fracture toughness (KIc), flexure strength (FS), elastic modulus (E), and hardness (KHN) were tested after soaking in water at 37 degrees C for 1 day, 6 months, 1 year, and 2 years. The KIc was reduced 20-30% for all composites after 6 months, with minimal changes thereafter. The FS was reduced for several composites at 6 months, but only those with poor cure (A and B) were lower at 2 years than they were initially. The E was not reduced for most composites. Hardness was reduced for most composites after 6 months, but many returned to their original levels at 2 years. Long-term aging in water caused a reduction in the KIc, independent of composition, but had little effect on other properties, suggesting limited degradation of composites in water.
In an effort to make composites from hydroxyapatite and a PEG/PBT copolymer (Polyactive 70/30), chemical linkages were introduced between the filler particles and polymer matrix using hexamethylene diisocyanate as a coupling agent. Infrared spectra (IR) and thermal gravimetric analysis (TGA) confirmed the presence of Polyactive 70/30 on the surface of HA filler particles. The amount of chemically bound polymer was 4.7 wt.%, as determined by TGA. The mechanical properties of the composites, that is, tensile strength and Young's modulus, were improved significantly by the introduction of a chemical linkage between the filler particles and polymer matrix compared to control composites. This method provides an effective way to introduce chemical linkage between HA filler particles and a polymer matrix. By optimizing the grafting process, a further improvement of the mechanical properties in the composites can be expected.
Explore the source record for details and available documents.