Metallic fragment deposits during phacoemulsification.

J J Martínez-Toldos·J C Elvira·J R Hueso·A Artola·E Mengual·A Barceló·J Garcia·M J Martínez-Reina
View original source ↗Export metadata ↓

Abstract

PURPOSE: To describe the nature and origin of foreign metallic intraocular bodies appearing after phacoemulsification. SETTING: Department of Ophthalmology, University Hospital of San Juan, Alicante, Spain. METHODS: Two metallic particles, 1 extracted during surgery and the other from a patient in whom surgery had been performed, were studied by scanning electronic microscopy and X-ray dispersive energy spectroscopy. Also evaluated were all metallic elements used in phacoemulsification including phaco tips, Sinskey hooks, and handpieces. A morphologic analysis at various magnifications was performed and the composition of the elements studied. RESULTS: Scanning electronic microscopy showed irregularities of the phaco tip and Sinskey hook after their use. Spectrographic analysis found that the phaco tip was mainly aluminum and titanium; the Sinskey hook, iron, chromium, cobalt, and nickel; the handpiece, iron, chromium, and nickel; and the 2 metallic particles, iron, chromium, and nickel, the same as the handpiece. CONCLUSION: The metallic particles extracted corresponded to those of the phaco handpiece. Vibration during prolonged use of the phacoemulsifier probably caused these particles to chip off the handpiece.

Explore related subjects

AlloysAnterior Eye SegmentElectron Probe MicroanalysisEye Foreign BodiesFollow-Up StudiesHumansMicroscopy, Electron, ScanningPhacoemulsificationJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

J J Martínez-Toldos, J C Elvira, J R Hueso, A Artola, E Mengual, A Barceló, J Garcia, M J Martínez-Reina. 1998. Metallic fragment deposits during phacoemulsification.. https://doi.org/10.1016/s0886-3350(98)80023-0

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Electrochemical characterization of albumin protein on Ti-6AL-4V alloy immersed in a simulated plasma solution.

The effect of oxygen and albumin on the electrochemical behavior of a Ti-6Al-4V alloy immersed in a simulated inorganic plasma (SIP) solution was studied with a rotating-cylindrical electrode configuration to focus on the surface/electrolyte reactions. Potentiokinetic scans and electrochemical impedance spectroscopy have been used to characterize the interface by determining the passive current density and capacitance. For the polarization scans, an albumin addition of 37.7 mg/cm(3) to the SIP solution (oxygenated and unoxygenated) decreased the passive current density, indicating a lowering of the corrosive rate. The surface capacitance for the Ti-6Al-4V alloy immersed in a SIP solution averaged 13 microF/cm(2), which transformed after albumin addition (37.7 mg/cm(3)) from a potential independent behavior to the capacitance ranging from 23 to 6 microF/cm(2) with increasing potentials from -800 to 1500 mV(SCE), respectively, indicative of albumin adsorption. Within the same potential range and albumin addition to oxygenated solutions, the capacitances expanded slightly with a similar decreasing trend from 31 to 6 microF/cm(2), although the capacitance depicts an interaction between the hydrated passive film and the adsorbed albumin from -550 to 500 mV(SCE) in which the capacitance plateaued at 15 microF/cm(2). The hydrated porous oxide film results from the porous rutile layer reacting with H(2)O(2) formed as an intermediary component of oxygen reduction at the Ti-6Al-4V surface. The passive film-albumin interaction would affect the processing of titanium alloys in their surface preparation for biocompatibility, as well as determining the reactivity of titanium alloys to proteins.

Alloys↗
PubMed2007

Fatigue-crack growth properties of thin-walled superelastic austenitic Nitinol tube for endovascular stents.

Over the past 10 years, the supereleastic nickel-titanium alloy Nitinol has found widespread application in the manufacture of small-scale biomedical devices, such as self-expanding endovascular stents. Although conventional stress/strain-life (S/N) analyses are invariably used as the primary method for design against fatigue loading and for predicting safe lifetimes, fracture mechanics-based methodologies provide a vital means of assessing the quantitative effect of defects on such lifetimes. Unfortunately, fracture mechanics studies on fatigue in Nitinol are scarce, and most results do not pertain to the (thin-walled tube) product forms that are typically used in the manufacture of endovascular stents. In the current work, we document the basic fatigue-crack growth properties of flattened thin-walled ( approximately 400 microm thick) Nitinol tubing in a 37 degrees C air environment. Crack-growth behavior is characterized over a wide range of growth rates ( approximately 6 orders of magnitude) and load ratios, that is, as a function of the alternating and maximum stress intensities, at 50 Hz. Limited experiments at both 5 and 50 Hz were also performed in 37 degrees C air and simulated body fluid to determine whether the cyclic frequency affects the fatigue behavior. Fatigue-crack growth-rate properties in such thin-walled Nitinol tube are found to be quite distinct from limited published data on other (mainly bulk) product forms of Nitinol, for example, bar and strip, both in terms of the relative fatigue thresholds and the variation in steady-state growth rates.

Alloys↗